Lignin as the main component of black liquor is generally employed to modify aliphatic superplasticizer（AFS）. However, the modification effect is hard to evaluate correctly due to the uncertain molecular structure o...Lignin as the main component of black liquor is generally employed to modify aliphatic superplasticizer（AFS）. However, the modification effect is hard to evaluate correctly due to the uncertain molecular structure of lignin and the disturbance from the complexity of black liquor compositions. In this paper, the purified lignin via acid precipitation from straw black liquor is used to modify AFS. The modified AFS named as LAFS for short presents lower molecular mass than AFS. It is assumed that it is due to the single active site of guaiacol segments in lignin by which lignin graft modifies AFS in virtue of methylolation reaction. In order to verify this assumption, guaiacol and dihydro eugenol as the typical segments of lignin macromolecule were selected, respectively, as the simplified model compounds of lignin to modify AFS, and corresponding products are abbreviated in GAFS and DAFS. Both GAFS and DAFS show the lower molecular mass than unmodified AFS. FTIR and TG-DTG analyses prove that lignin is successfully grafted onto AFS. The graft modification of lignin results in a decrease in electrostatic epulsion, but an enhanced steric hindrance. Therefore, although the replacement rate of lignin in LAFS was about 23.3%, the dispersion performance was only slightly affected.展开更多
The microstructures of NiAl(Co)-TiB_2 composite prepared using exothermal dispersion (XD) method have been studied by optical microscopy, XRD, EDS, and TEM The results show that, TiB_2 paritcles are typically single c...The microstructures of NiAl(Co)-TiB_2 composite prepared using exothermal dispersion (XD) method have been studied by optical microscopy, XRD, EDS, and TEM The results show that, TiB_2 paritcles are typically single crystal, and fairly uniformly distributed. The matrix mainly consists of β-NiAl phase, Ll_2γ′Ni_3Al phase and δ-Ni_3Al phase. The δNi_3Al has a fcc crystal structure with lattice parameter a=1.068nm.The data of compressive testing at room temperature show that the room temperature ductility of NiAl(Co) matrix composite is much better than that of stoichiometric NiAl.展开更多
基金Funded by the National Natural Science Foundation of China(No.51778513)the China Ministry of Science and Technology(No.2015CB655101)
文摘Lignin as the main component of black liquor is generally employed to modify aliphatic superplasticizer（AFS）. However, the modification effect is hard to evaluate correctly due to the uncertain molecular structure of lignin and the disturbance from the complexity of black liquor compositions. In this paper, the purified lignin via acid precipitation from straw black liquor is used to modify AFS. The modified AFS named as LAFS for short presents lower molecular mass than AFS. It is assumed that it is due to the single active site of guaiacol segments in lignin by which lignin graft modifies AFS in virtue of methylolation reaction. In order to verify this assumption, guaiacol and dihydro eugenol as the typical segments of lignin macromolecule were selected, respectively, as the simplified model compounds of lignin to modify AFS, and corresponding products are abbreviated in GAFS and DAFS. Both GAFS and DAFS show the lower molecular mass than unmodified AFS. FTIR and TG-DTG analyses prove that lignin is successfully grafted onto AFS. The graft modification of lignin results in a decrease in electrostatic epulsion, but an enhanced steric hindrance. Therefore, although the replacement rate of lignin in LAFS was about 23.3%, the dispersion performance was only slightly affected.
文摘The microstructures of NiAl(Co)-TiB_2 composite prepared using exothermal dispersion (XD) method have been studied by optical microscopy, XRD, EDS, and TEM The results show that, TiB_2 paritcles are typically single crystal, and fairly uniformly distributed. The matrix mainly consists of β-NiAl phase, Ll_2γ′Ni_3Al phase and δ-Ni_3Al phase. The δNi_3Al has a fcc crystal structure with lattice parameter a=1.068nm.The data of compressive testing at room temperature show that the room temperature ductility of NiAl(Co) matrix composite is much better than that of stoichiometric NiAl.