The new electrorheologicai (ER) material, a particle material composed of Y4O(OH)9(NO3) and NH4NO3, was obtained. They display better ER performance. The shear stress of the suspension of Y4O (OH)9 (NO3) ( ...The new electrorheologicai (ER) material, a particle material composed of Y4O(OH)9(NO3) and NH4NO3, was obtained. They display better ER performance. The shear stress of the suspension of Y4O (OH)9 (NO3) ( NH4NO3 )2.8 material in dimethyl silicone oil reaches 1469 Pa at an electric field strength (E) of 4.2 kV·mm^-1 and the shear rate (7) of 150 s^-1 The relative shear stress, τ E/τ0( τE and τ0 are the shear stresses at E = 4.2 and 0 kV·mm^-1 respectively), is up to 29, which is 19 times that of pure Y2O3 material. The dielectric and conductive property of the materials play important roles in the modification of the ER effect of the particle materials. The researches on these new ER materials are very useful for obtaining a better understanding on the mechanism of the ER effect and finding an ideal ER material.展开更多
Transparent conducting F-doped texture SnO2 films with resistivity as low as 5× 10-4 Ω ·cm,with carrier concentrations between 3.5 × 1020 and 7× 1020 cm-3 and Hall mobilities from 15.7 to 20.1 cm2...Transparent conducting F-doped texture SnO2 films with resistivity as low as 5× 10-4 Ω ·cm,with carrier concentrations between 3.5 × 1020 and 7× 1020 cm-3 and Hall mobilities from 15.7 to 20.1 cm2/(V/s) have been prepared by atmosphere pressure chemical vapour deposition (APCVD). These polycrystalline films possess a variable preferred orientation, the polycrystallite sizes and orientations vary with substrate temperature. The substrate temperature and fluorine flow rate dependence of conductivity, Hall mobility and carrier conentration fOr the resultingfilms have been obtained. The temperature dependence of the mobiity and carrier concentrationhave been measured over a temperature range 16~400 K. A systematically theoretical analysis on scattering mechanisms for the highly conductive SnO2 films has been given. Both theoretical analysis and experimental results indicate that for these degenerate, polycrystalline SnO2 :F films in the low temperature range (below 100 K), ionized impurity scattering is main scattering mechanism. However, when the temperature is higher than 100 K, the lattice vibration scattering becomes dominant. The grain boundary scattering makes a small contribution to limit the mobility of the films.展开更多
A series of aluminium-containing α-type hydrated zirconium hydrogen phosphates,Zr_(1-x)Alx (H_(1+x/2)PO_4 )_2 with x=0-0.06,were hydrothermally synthesized and characterizedby means of X-ray diffraction,differential ...A series of aluminium-containing α-type hydrated zirconium hydrogen phosphates,Zr_(1-x)Alx (H_(1+x/2)PO_4 )_2 with x=0-0.06,were hydrothermally synthesized and characterizedby means of X-ray diffraction,differential thermal analysis and thermogravimetric analysis.The proton conductivity,1.2×10 ̄(-4) S·cm ̄(-1)at 180℃ was found in Zr_(0.98)Al_(0.02)(H_(1.01)PO_4)_2·H_2O.Humidity-sensing measurements were carried out at 120℃ and 140℃ respectively.Even a limited substitution of Al for Zr can enhance both proton conductivity and humidity sensitivity.展开更多
The conductivity of non-crystalline fast ionic conductor for B_2O_3-Li_2O-LiCl-Al_2O_3 system is studiedin this paper. The glass structure of this system is discussed by means of infrared spectrum and X-ray fluorescen...The conductivity of non-crystalline fast ionic conductor for B_2O_3-Li_2O-LiCl-Al_2O_3 system is studiedin this paper. The glass structure of this system is discussed by means of infrared spectrum and X-ray fluorescence analysis, and the effects of LiCl and A1_2O_3 on the conductivity of Li^+ in the system are studied as well. Adding Li_2O to the system gives rise to transfer from [BO_3] triangular units to [BO_4] tetrahedral. When Li_2O content exceeds 30mol%, the main group of the glass is the diborate group with more [BO_4] tetrahedra. The adding of LiCl has no obvious influence on the glass structure, and LiCl is under a state dissociated by network, but with the increase of LiCl, the increase of conductivity is obvious. By adding A1_2O_3, the glass can be formed when the room-temperature is cooling down,the conductivity decreases while the conductive activatory energy increases for the glass. The experiment shows that conductivity in the room-temperature is σ= 6.2×10^(-6)Ω^(-1)cm^(-1), when at 300℃, the σ=6.8×10^(-3)Ω^(-1)cm^(-1). The conductive activatory energy computed is 0.6~1.0eV.展开更多
Multiferroic material as a photovoltaic material has gained considerable attention in recent years.Nanoparticles(NPs)La_(0.1)Bi_(0.9-x)Sr_xFeO_y(LBSF,x = 0,0.2,0.4) with dopant Sr^(2+)ions were synthesized ...Multiferroic material as a photovoltaic material has gained considerable attention in recent years.Nanoparticles(NPs)La_(0.1)Bi_(0.9-x)Sr_xFeO_y(LBSF,x = 0,0.2,0.4) with dopant Sr^(2+)ions were synthesized by the sol–gel method.A systematic change in the crystal structure from rhombohedral to tetragonal upon increasing Sr doping was observed.There is an obvious change in the particle size from 180 nm to 50 nm with increasing Sr substitution into LBFO.It was found that Sr doping effectively narrows the band gap from~2.08 e V to~1.94 e V,while it leads to an apparent enhancement in the electrical conductivity of LBSF NPs,making a transition from insulator to semiconductor.This suggests an effective way to modulate the conductivity of BiFeO_(3-)based multiferroic materials with pure phase by co-doping with La and Sr at the A sites of BiFeO_3.展开更多
The lap joint of T2 copper plate and 1060 pure aluminum plate was made by using the plasma arc welding method with adding Fe_(2)O_(3)nanoparticles in different proportions.The research analysis found that the thicknes...The lap joint of T2 copper plate and 1060 pure aluminum plate was made by using the plasma arc welding method with adding Fe_(2)O_(3)nanoparticles in different proportions.The research analysis found that the thickness of the IMC(intermetallic compound)and eutect-ic region decreased after the addition of nanoparticles due to its inhibitory effect.When the proportion of Fe_(2)O_(3)nanoparticles is 3%,the in-terface intermetallic compound layer is the thinnest.However,after this ratio is continuously increased,the inhibition effect is weakened by the agglomeration of nanoparticles,and the thickness begins to increase significantly.The mechanical and electrical properties of the joint are mainly affected by the thickness of the IMC layer.Excessive nanoparticles are agglomerated into large particles with high resistivity.Therefore,the tensile strength and relative electrical conductivity of the joint are first increasing and then decreasing with the increase of nanoparticle ratio.When the proportion of nanoparticles is 3%,the tensile strength and electrical conductivity are maximum.展开更多
To extend the application of carbon nanotubes (CNTs) and explore novel aluminum matrix composites,CNTs were coated by molybdenum layers using metal organic chemical vapor deposition,and then Mo-coated CNT (Mo-CNT)...To extend the application of carbon nanotubes (CNTs) and explore novel aluminum matrix composites,CNTs were coated by molybdenum layers using metal organic chemical vapor deposition,and then Mo-coated CNT (Mo-CNT)/Al composites were prepared by the combination processes of powder mixing and spark plasma sintering.The influences of powder mixing and Mo-CNT content on the mechanical properties and electrical conductivity of the composites were investigated.The results show that magnetic stirring is better than mechanical milling for mixing the Mo-CNTs and Al powders.The electrical conductivity of the composites decreases with increasing Mo-CNT content.When the Mo-CNT content is 0.5wt%,the tensile strength and hardness of Mo-CNT/Al reach their maximum values.The tensile strength of 0.5wt% Mo-CNT/Al increases by 29.9%,while the electrical conductivity only decreases by 7.1%,relative to sintered pure Al.The phase analysis of Mo-CNT/Al composites reveals that there is no formation of Al carbide in the composites.展开更多
The electrical and optical effects of particles on the nano aluminum film deposited by thermal evaporation was investigated. From the characterization results of scanning electron microscope(SEM), the accumulation i...The electrical and optical effects of particles on the nano aluminum film deposited by thermal evaporation was investigated. From the characterization results of scanning electron microscope(SEM), the accumulation in tens of nanometers had been observed. The current-voltage(I-V) curve of the sample indicates its nonlinear electrical characters expecting the corresponding nonlinear optical properties. By the theoretical calculation, nonlinear conduction of the carrier transportation may result from the barrier-well-barrier structure, where negative resistance and Coulomb blockade effect appears. The simulation results are approximately matched with the experimental results. By testing the fluorescence emission spectrum of the sample, peaks were found to be located at 420 and 440 nm. In addition, the full width at half maximum(FWHM) had been obviously broadened by means of adding 2, 5-diphenyloxazole(DPO). Therefore, discrete energy levels could be estimated inside those particles.展开更多
Transparent conductive cadmium indium oxide films (CdIn2O4) were prepared by r.f. reactive sputtering from Cd-In alloy targets under an Ar-O2 atmosphere. Electrical conductivity of the order of 105Ω-1.m-1 and the opt...Transparent conductive cadmium indium oxide films (CdIn2O4) were prepared by r.f. reactive sputtering from Cd-In alloy targets under an Ar-O2 atmosphere. Electrical conductivity of the order of 105Ω-1.m-1 and the optical transmission as high as 94% are easily attained by postdeposition annealing treatment. The effects of oxygen concentration in the reactive gas mixture and post-deposition annealing treatment on the optical transmittance as well as optical parameters, such as refractive index (n), extinction coefficient (k), real part (ε') and imaginary part (ε') of the dielectric constant, were studied in the visible and near-infrared region. The highfrequency dielectric constant ε∞ the plasma frequency ωP, and the conduction band effective mass mc of different samples were also investigated展开更多
Continuous CNT fibers have been directly fabricated in a speed of 50 m/h-400 m/h,based on an improved chemical vapor deposition method.As-prepared fibers are further post-treated by acid.According to the SEM images an...Continuous CNT fibers have been directly fabricated in a speed of 50 m/h-400 m/h,based on an improved chemical vapor deposition method.As-prepared fibers are further post-treated by acid.According to the SEM images and Raman spectra,the acid treatment results in the compaction and surface modification of the CNTs in fibers,which are beneficial for the electron and load transfer.Compared to the HNO3 treatment,HClSO_3 or H_2SO_4 treatment is more effective for the improvement of the fibers' properties.After HCISO_3 treatment for 2 h,the fibers' strength and electrical conductivity reach up to-2 GPa and-4.3 MS/m,which are promoted by-200%and almost one order of magnitude than those without acid treatment,respectively.The load-bearing status of the CNT fibers are analyzed based on the downshifts of the G' band and the strain transfer factor of the fibers under tension.The results reveal that acid treatment could greatly enhance the load transfer and inter-bundle strength.With the HCISO3 treatment,the strain transfer factor is enhanced from-3.9%to-53.6%.展开更多
The mechanical, electrical, and thermal expansion properties of carbon nanotube(CNT)-based silver and silver–palladium(10:1, w/w) alloy nanocomposites are reported. To tailor the properties of silver, CNTs were ...The mechanical, electrical, and thermal expansion properties of carbon nanotube(CNT)-based silver and silver–palladium(10:1, w/w) alloy nanocomposites are reported. To tailor the properties of silver, CNTs were incorporated into a silver matrix by a modified molecular level-mixing process. CNTs interact weakly with silver because of their non-reactive nature and lack of mutual solubility. Therefore, palladium was utilized as an alloying element to improve interfacial adhesion. Comparative microstructural characterizations and property evaluations of the nanocomposites were performed. The structural characterizations revealed that decorated type-CNTs were dispersed, embedded, and anchored into the silver matrix. The experimental results indicated that the modification of the silver and silver–palladium nanocomposite with CNT resulted in increases in the hardness and Young's modulus along with concomitant decreases in the electrical conductivity and the coefficient of thermal expansion(CTE). The hardness and Young's modulus of the nanocomposites were increased by 30%?40% whereas the CTE was decreased to 50%-60% of the CTE of silver. The significantly improved CTE and the mechanical properties of the CNT-reinforced silver and silver–palladium nanocomposites are correlated with the intriguing properties of CNTs and with good interfacial adhesion between the CNTs and silver as a result of the fabrication process and the contact action of palladium as an alloying element.展开更多
Based on the transport theory and the polarization relaxation model,the effects of hydrogen and hydroxyl passivation on the conductivity and dielectric properties of silicon carbide nanowires(SiCNWs)with different siz...Based on the transport theory and the polarization relaxation model,the effects of hydrogen and hydroxyl passivation on the conductivity and dielectric properties of silicon carbide nanowires(SiCNWs)with different sizes are numerically simulated.The results show that the variation trend of conductivity and band gap of passivated SiCNWs are opposite to the scenario of the size effect of bare SiCNWs.Among the influencing factors of conductivity,the carrier concentration plays a leading role.In the dielectric properties,the bare SiCNWs have a strong dielectric response in the blue light region,while passivated SiCNWs show a more obvious dielectric response in the far ultraviolet-light region.In particular,hydroxyl passivation produces a strong dielectric relaxation in the microwave band,indicating that hydroxyl passivated SiCNWs have a wide range of applications in electromagnetic absorption and shielding.展开更多
Radiation-shielding concrete was made with ironstone aggregate. The compressive strength is affected by multi factors. The electrical conductive properties and smart performance was discovered and investigated. Experi...Radiation-shielding concrete was made with ironstone aggregate. The compressive strength is affected by multi factors. The electrical conductive properties and smart performance was discovered and investigated. Experimental results show that concrete conductivity rapidly declines with increasing loading, and the conductivity is much lower than the initial value of conductive aggregate of concrete, which may be related to special characters of ironstone. This kind of concrete has widely potential applications due to its special characters and low cost.展开更多
Adopting LB film method, an arachidic acid (AA)/PEDOT multilayer LB film and polymerized EDOT monomers in hydrophilic group of LB were chosen to prepare the arachidic acid (AA)/PEDOT multilayer LB film. UV-Vis, FT...Adopting LB film method, an arachidic acid (AA)/PEDOT multilayer LB film and polymerized EDOT monomers in hydrophilic group of LB were chosen to prepare the arachidic acid (AA)/PEDOT multilayer LB film. UV-Vis, FT-IR and XPS analyses implied that EDOT was effectively polymerized in film, and thus PEDOT conducting polymer was produced. Analyses of XRR and SIMS indicated that the film had a well-arranged lamella structure, and further research showed that polymerization of EDOT in AA film destroyed the orderliness of the original LB film. This phenomenon could be related to the destructive effect of polymerization on the layered structure. We used four-point probe and semiconductor instrument to study the conductivity property of the film, and observed that the conductivity of AA/PEDOT film had sudden changes with the changes of processing time in an effective conduction network, which was caused by "permeability" in conducting channel of multilayer film. The test results also indicated that the conductivity of AA/PEDOT film was obviously better than that of spin-coating PEDOT/PSS or ODA-SA/PEDOT-PSS film due to the higher π structure of PEDOT structure and ordered film structure.展开更多
For deep geological disposal of high-level radioactive waste(HLW)in granite,the temperature on the HLW canisters is commonly designed to be lower than100fiC.This criterion dictates the dimension of the repository.Base...For deep geological disposal of high-level radioactive waste(HLW)in granite,the temperature on the HLW canisters is commonly designed to be lower than100fiC.This criterion dictates the dimension of the repository.Based on the concept of HLW disposal in vertical boreholes,thermal process in the nearfield(host rock and buffer)surrounding HLW canisters has been simulated by using different methods.The results are drawn as follows:(a)the initial heat power of HLW canisters is the most important and sensitive parameter for evolution of temperaturefield;(b)the thermal properties and variations of the host rock,the engineered buffer,and possible gaps between canister and buffer and host rock are the additional key factors governing the heat transformation;(c)the gaps width and thefilling by water or air determine the temperature offsets between them.展开更多
This paper presents the substrate temperature dependence of opto-electrical properties for transparent conducting Al-doped ZnO films prepared on polyisocyanate (PI) substrates by r f sputtering. Polycrystalline ZnO:Al...This paper presents the substrate temperature dependence of opto-electrical properties for transparent conducting Al-doped ZnO films prepared on polyisocyanate (PI) substrates by r f sputtering. Polycrystalline ZnO:Al films with good adherence to the substrates having a (002) preferred orientation have been obtained with resistivities in the range from 4.1×10-3to 5.3×104 Ωcm, carrier densities more than 2.6×1020 cm-3 and Hall mobilities between 5.78 and 13.11 cm2/V/s for films. The average transmittance reaches 75% in the visible spectrum. The quality of obtained films depends on substrate temperature during film fabrication.展开更多
Ta-doped titanium dioxide films are deposited on fused quartz substrates using the rf magnetron sputtering technique at different substrate temperatures. After post-annealing at 550℃ in a vacuum, all the films are cr...Ta-doped titanium dioxide films are deposited on fused quartz substrates using the rf magnetron sputtering technique at different substrate temperatures. After post-annealing at 550℃ in a vacuum, all the films are crystallized into the polycrystalline anatase TiO2 structure. The effects of substrate temperature from room temperature up to 350℃ on the structure, morphology, and photoelectric properties of Ta-doped titanium dioxide films are analyzed. The average transmittance in the visible region(400-800 nm) of all films is more than 73%.The resistivity decreases firstly and then increases moderately with the increasing substrate temperature. The polycrystalline film deposited at 150℃ exhibits a lowest resistivity of 7.7 × 10^-4Ω·cm with the highest carrier density of 1.1×10^21 cm^-3 and the Hall mobility of 7.4 cm^2·V^-1s^-1.展开更多
Based on the study of a new type of conducting polymer poly (3,4-ethylenedioxythiophene) (PEDOT),we focussed on the preparation and characteristics of PEDOT nanoparticles made by reversed micelle method.Moreover,w...Based on the study of a new type of conducting polymer poly (3,4-ethylenedioxythiophene) (PEDOT),we focussed on the preparation and characteristics of PEDOT nanoparticles made by reversed micelle method.Moreover,we deeply investigated the optical,electrical and the thermal stability of PEDOT nanoparticles.The main results are as follows: the small-sized PEDOT nanoparticles were prepared and utilized by different methods,such as ultraviolet/visible (UV-Vis) spectroscopy,Fourier-transform infrared (FT- IR) spectrum,scanning electron microscopy(SEM) and so on.The results show that the amount of oxidizer,ultrasonic treatment,polymerizing temperature and doping degree can influent morphology,electrical ability and gas sensitivity of PEDOT nanoparticles.The Bragg peaks of nanoparticles at 6.7°,12.7°,25° were observed by XRD and the better orientation of molecular chain was attributed to the effective doping of toluene-p-sulfonic acid,which also resulted in an enhancement of thermal stability of nanoparticles than conventional PEDOT.展开更多
In this work,Yb2O3 and Mg O were used as sintering aids in preparing silicon nitride ceramics by gas pressure sintering( 0. 6 MPa N2atmosphere) to investigate how the amounts of Yb2O3- Mg O influence the mechanical ...In this work,Yb2O3 and Mg O were used as sintering aids in preparing silicon nitride ceramics by gas pressure sintering( 0. 6 MPa N2atmosphere) to investigate how the amounts of Yb2O3- Mg O influence the mechanical properties and thermal conductivity of silicon nitride ceramics. The total contents of Yb2O3- Mg O added were 1 mol%,2 mol%,4 mol%,6 mol%,8 mol%,10 mol%,12 mol%,14 mol%,keeping the Yb2O3-Mg O molar ratio of 1 ∶ 1 steadily. Curves of the relative density,thermal conductivity and bending strength plotted against the aids content present a ‘mountain'shape with a maximum at nearly 10 mol% aids. The fracture toughness increased with the amounts of additives up to10 mol% and decreased slightly thereafter. The mechanical properties and thermal conductivity were almost proportional to the amount of the additives before10 mol%. When the content of aids exceeded 10 mol%,it would weaken the mechanical properties and thermal conductivity of the ceramics. The optimum content of Yb2O3- Mg O was 10 mol% by gas pressure sintering( 0. 6MPa) at 1 850 ℃ for 4 h,which led to a relative density of 98. 9%,a flexural strength of( 966 ± 38)MPa as well as a fracture toughness of( 6. 29 ± 0. 29)MPa·m1 /2and thermal conductivity of 82 W /( m·K).展开更多
Studies of the rocks′ electrical properties under high temperature and pressure have found favors in the geophysicist′s eyes, because those studies are becoming to be the important methods to understand the earth′s...Studies of the rocks′ electrical properties under high temperature and pressure have found favors in the geophysicist′s eyes, because those studies are becoming to be the important methods to understand the earth′s interior materials, their migration and evolution. This article introduces the development and significant of those studies from the measurements, instruments and affections, etc .展开更多
文摘The new electrorheologicai (ER) material, a particle material composed of Y4O(OH)9(NO3) and NH4NO3, was obtained. They display better ER performance. The shear stress of the suspension of Y4O (OH)9 (NO3) ( NH4NO3 )2.8 material in dimethyl silicone oil reaches 1469 Pa at an electric field strength (E) of 4.2 kV·mm^-1 and the shear rate (7) of 150 s^-1 The relative shear stress, τ E/τ0( τE and τ0 are the shear stresses at E = 4.2 and 0 kV·mm^-1 respectively), is up to 29, which is 19 times that of pure Y2O3 material. The dielectric and conductive property of the materials play important roles in the modification of the ER effect of the particle materials. The researches on these new ER materials are very useful for obtaining a better understanding on the mechanism of the ER effect and finding an ideal ER material.
文摘Transparent conducting F-doped texture SnO2 films with resistivity as low as 5× 10-4 Ω ·cm,with carrier concentrations between 3.5 × 1020 and 7× 1020 cm-3 and Hall mobilities from 15.7 to 20.1 cm2/(V/s) have been prepared by atmosphere pressure chemical vapour deposition (APCVD). These polycrystalline films possess a variable preferred orientation, the polycrystallite sizes and orientations vary with substrate temperature. The substrate temperature and fluorine flow rate dependence of conductivity, Hall mobility and carrier conentration fOr the resultingfilms have been obtained. The temperature dependence of the mobiity and carrier concentrationhave been measured over a temperature range 16~400 K. A systematically theoretical analysis on scattering mechanisms for the highly conductive SnO2 films has been given. Both theoretical analysis and experimental results indicate that for these degenerate, polycrystalline SnO2 :F films in the low temperature range (below 100 K), ionized impurity scattering is main scattering mechanism. However, when the temperature is higher than 100 K, the lattice vibration scattering becomes dominant. The grain boundary scattering makes a small contribution to limit the mobility of the films.
文摘A series of aluminium-containing α-type hydrated zirconium hydrogen phosphates,Zr_(1-x)Alx (H_(1+x/2)PO_4 )_2 with x=0-0.06,were hydrothermally synthesized and characterizedby means of X-ray diffraction,differential thermal analysis and thermogravimetric analysis.The proton conductivity,1.2×10 ̄(-4) S·cm ̄(-1)at 180℃ was found in Zr_(0.98)Al_(0.02)(H_(1.01)PO_4)_2·H_2O.Humidity-sensing measurements were carried out at 120℃ and 140℃ respectively.Even a limited substitution of Al for Zr can enhance both proton conductivity and humidity sensitivity.
文摘The conductivity of non-crystalline fast ionic conductor for B_2O_3-Li_2O-LiCl-Al_2O_3 system is studiedin this paper. The glass structure of this system is discussed by means of infrared spectrum and X-ray fluorescence analysis, and the effects of LiCl and A1_2O_3 on the conductivity of Li^+ in the system are studied as well. Adding Li_2O to the system gives rise to transfer from [BO_3] triangular units to [BO_4] tetrahedral. When Li_2O content exceeds 30mol%, the main group of the glass is the diborate group with more [BO_4] tetrahedra. The adding of LiCl has no obvious influence on the glass structure, and LiCl is under a state dissociated by network, but with the increase of LiCl, the increase of conductivity is obvious. By adding A1_2O_3, the glass can be formed when the room-temperature is cooling down,the conductivity decreases while the conductive activatory energy increases for the glass. The experiment shows that conductivity in the room-temperature is σ= 6.2×10^(-6)Ω^(-1)cm^(-1), when at 300℃, the σ=6.8×10^(-3)Ω^(-1)cm^(-1). The conductive activatory energy computed is 0.6~1.0eV.
基金Project supported by the National Natural Science Foundation of China(Grant Nos.11104202 and 51572193)
文摘Multiferroic material as a photovoltaic material has gained considerable attention in recent years.Nanoparticles(NPs)La_(0.1)Bi_(0.9-x)Sr_xFeO_y(LBSF,x = 0,0.2,0.4) with dopant Sr^(2+)ions were synthesized by the sol–gel method.A systematic change in the crystal structure from rhombohedral to tetragonal upon increasing Sr doping was observed.There is an obvious change in the particle size from 180 nm to 50 nm with increasing Sr substitution into LBFO.It was found that Sr doping effectively narrows the band gap from~2.08 e V to~1.94 e V,while it leads to an apparent enhancement in the electrical conductivity of LBSF NPs,making a transition from insulator to semiconductor.This suggests an effective way to modulate the conductivity of BiFeO_(3-)based multiferroic materials with pure phase by co-doping with La and Sr at the A sites of BiFeO_3.
基金This work was supported by the National Natural Science Foundation of China(No.52165045).
文摘The lap joint of T2 copper plate and 1060 pure aluminum plate was made by using the plasma arc welding method with adding Fe_(2)O_(3)nanoparticles in different proportions.The research analysis found that the thickness of the IMC(intermetallic compound)and eutect-ic region decreased after the addition of nanoparticles due to its inhibitory effect.When the proportion of Fe_(2)O_(3)nanoparticles is 3%,the in-terface intermetallic compound layer is the thinnest.However,after this ratio is continuously increased,the inhibition effect is weakened by the agglomeration of nanoparticles,and the thickness begins to increase significantly.The mechanical and electrical properties of the joint are mainly affected by the thickness of the IMC layer.Excessive nanoparticles are agglomerated into large particles with high resistivity.Therefore,the tensile strength and relative electrical conductivity of the joint are first increasing and then decreasing with the increase of nanoparticle ratio.When the proportion of nanoparticles is 3%,the tensile strength and electrical conductivity are maximum.
基金supported by the National High-Tech Research and Development Program of China (No.2009AA03Z116)the National Natural Science Foundation of China (No.50971020)
文摘To extend the application of carbon nanotubes (CNTs) and explore novel aluminum matrix composites,CNTs were coated by molybdenum layers using metal organic chemical vapor deposition,and then Mo-coated CNT (Mo-CNT)/Al composites were prepared by the combination processes of powder mixing and spark plasma sintering.The influences of powder mixing and Mo-CNT content on the mechanical properties and electrical conductivity of the composites were investigated.The results show that magnetic stirring is better than mechanical milling for mixing the Mo-CNTs and Al powders.The electrical conductivity of the composites decreases with increasing Mo-CNT content.When the Mo-CNT content is 0.5wt%,the tensile strength and hardness of Mo-CNT/Al reach their maximum values.The tensile strength of 0.5wt% Mo-CNT/Al increases by 29.9%,while the electrical conductivity only decreases by 7.1%,relative to sintered pure Al.The phase analysis of Mo-CNT/Al composites reveals that there is no formation of Al carbide in the composites.
基金Supported by the 973 Program(No.2014CB932103)the 863 Program(No.2013AA032501)the National Natural Science Foundation of China(NSFC No.21676015)
文摘The electrical and optical effects of particles on the nano aluminum film deposited by thermal evaporation was investigated. From the characterization results of scanning electron microscope(SEM), the accumulation in tens of nanometers had been observed. The current-voltage(I-V) curve of the sample indicates its nonlinear electrical characters expecting the corresponding nonlinear optical properties. By the theoretical calculation, nonlinear conduction of the carrier transportation may result from the barrier-well-barrier structure, where negative resistance and Coulomb blockade effect appears. The simulation results are approximately matched with the experimental results. By testing the fluorescence emission spectrum of the sample, peaks were found to be located at 420 and 440 nm. In addition, the full width at half maximum(FWHM) had been obviously broadened by means of adding 2, 5-diphenyloxazole(DPO). Therefore, discrete energy levels could be estimated inside those particles.
文摘Transparent conductive cadmium indium oxide films (CdIn2O4) were prepared by r.f. reactive sputtering from Cd-In alloy targets under an Ar-O2 atmosphere. Electrical conductivity of the order of 105Ω-1.m-1 and the optical transmission as high as 94% are easily attained by postdeposition annealing treatment. The effects of oxygen concentration in the reactive gas mixture and post-deposition annealing treatment on the optical transmittance as well as optical parameters, such as refractive index (n), extinction coefficient (k), real part (ε') and imaginary part (ε') of the dielectric constant, were studied in the visible and near-infrared region. The highfrequency dielectric constant ε∞ the plasma frequency ωP, and the conduction band effective mass mc of different samples were also investigated
基金Project supported by the National Basic Research Program of China(Grant No.2012CB932302)the National Natural Science Foundation of China(Grant Nos.11634014,51172271,51372269,and 51472264)the“Strategic Priority Research Program”of the Chinese Academy of Sciences(Grant No.XDA09040202)
文摘Continuous CNT fibers have been directly fabricated in a speed of 50 m/h-400 m/h,based on an improved chemical vapor deposition method.As-prepared fibers are further post-treated by acid.According to the SEM images and Raman spectra,the acid treatment results in the compaction and surface modification of the CNTs in fibers,which are beneficial for the electron and load transfer.Compared to the HNO3 treatment,HClSO_3 or H_2SO_4 treatment is more effective for the improvement of the fibers' properties.After HCISO_3 treatment for 2 h,the fibers' strength and electrical conductivity reach up to-2 GPa and-4.3 MS/m,which are promoted by-200%and almost one order of magnitude than those without acid treatment,respectively.The load-bearing status of the CNT fibers are analyzed based on the downshifts of the G' band and the strain transfer factor of the fibers under tension.The results reveal that acid treatment could greatly enhance the load transfer and inter-bundle strength.With the HCISO3 treatment,the strain transfer factor is enhanced from-3.9%to-53.6%.
基金the financial assistance received from the Department of Science and Technology(Government of India)for conducting this investigation(Project-SR/FTP/PS-054/2011(G))
文摘The mechanical, electrical, and thermal expansion properties of carbon nanotube(CNT)-based silver and silver–palladium(10:1, w/w) alloy nanocomposites are reported. To tailor the properties of silver, CNTs were incorporated into a silver matrix by a modified molecular level-mixing process. CNTs interact weakly with silver because of their non-reactive nature and lack of mutual solubility. Therefore, palladium was utilized as an alloying element to improve interfacial adhesion. Comparative microstructural characterizations and property evaluations of the nanocomposites were performed. The structural characterizations revealed that decorated type-CNTs were dispersed, embedded, and anchored into the silver matrix. The experimental results indicated that the modification of the silver and silver–palladium nanocomposite with CNT resulted in increases in the hardness and Young's modulus along with concomitant decreases in the electrical conductivity and the coefficient of thermal expansion(CTE). The hardness and Young's modulus of the nanocomposites were increased by 30%?40% whereas the CTE was decreased to 50%-60% of the CTE of silver. The significantly improved CTE and the mechanical properties of the CNT-reinforced silver and silver–palladium nanocomposites are correlated with the intriguing properties of CNTs and with good interfacial adhesion between the CNTs and silver as a result of the fabrication process and the contact action of palladium as an alloying element.
基金supported by the National Natural Science Foundation of China(Grant No.11574261)the Natural Science Foundation of Hebei Province,China(Grant No.A2021203030).
文摘Based on the transport theory and the polarization relaxation model,the effects of hydrogen and hydroxyl passivation on the conductivity and dielectric properties of silicon carbide nanowires(SiCNWs)with different sizes are numerically simulated.The results show that the variation trend of conductivity and band gap of passivated SiCNWs are opposite to the scenario of the size effect of bare SiCNWs.Among the influencing factors of conductivity,the carrier concentration plays a leading role.In the dielectric properties,the bare SiCNWs have a strong dielectric response in the blue light region,while passivated SiCNWs show a more obvious dielectric response in the far ultraviolet-light region.In particular,hydroxyl passivation produces a strong dielectric relaxation in the microwave band,indicating that hydroxyl passivated SiCNWs have a wide range of applications in electromagnetic absorption and shielding.
基金Funded by the National Natural Science Foundation of China(No. 40674060)
文摘Radiation-shielding concrete was made with ironstone aggregate. The compressive strength is affected by multi factors. The electrical conductive properties and smart performance was discovered and investigated. Experimental results show that concrete conductivity rapidly declines with increasing loading, and the conductivity is much lower than the initial value of conductive aggregate of concrete, which may be related to special characters of ironstone. This kind of concrete has widely potential applications due to its special characters and low cost.
基金Funded by the National Natural Science Foundation of China (No. 60372002)
文摘Adopting LB film method, an arachidic acid (AA)/PEDOT multilayer LB film and polymerized EDOT monomers in hydrophilic group of LB were chosen to prepare the arachidic acid (AA)/PEDOT multilayer LB film. UV-Vis, FT-IR and XPS analyses implied that EDOT was effectively polymerized in film, and thus PEDOT conducting polymer was produced. Analyses of XRR and SIMS indicated that the film had a well-arranged lamella structure, and further research showed that polymerization of EDOT in AA film destroyed the orderliness of the original LB film. This phenomenon could be related to the destructive effect of polymerization on the layered structure. We used four-point probe and semiconductor instrument to study the conductivity property of the film, and observed that the conductivity of AA/PEDOT film had sudden changes with the changes of processing time in an effective conduction network, which was caused by "permeability" in conducting channel of multilayer film. The test results also indicated that the conductivity of AA/PEDOT film was obviously better than that of spin-coating PEDOT/PSS or ODA-SA/PEDOT-PSS film due to the higher π structure of PEDOT structure and ordered film structure.
文摘For deep geological disposal of high-level radioactive waste(HLW)in granite,the temperature on the HLW canisters is commonly designed to be lower than100fiC.This criterion dictates the dimension of the repository.Based on the concept of HLW disposal in vertical boreholes,thermal process in the nearfield(host rock and buffer)surrounding HLW canisters has been simulated by using different methods.The results are drawn as follows:(a)the initial heat power of HLW canisters is the most important and sensitive parameter for evolution of temperaturefield;(b)the thermal properties and variations of the host rock,the engineered buffer,and possible gaps between canister and buffer and host rock are the additional key factors governing the heat transformation;(c)the gaps width and thefilling by water or air determine the temperature offsets between them.
基金This work is supported by the National Natural Srience Foundation of China(No.69876025 and No.60076006)Science and Technology Committee of Shandong Province and the Natural Science Foundation of Shandong Province.
文摘This paper presents the substrate temperature dependence of opto-electrical properties for transparent conducting Al-doped ZnO films prepared on polyisocyanate (PI) substrates by r f sputtering. Polycrystalline ZnO:Al films with good adherence to the substrates having a (002) preferred orientation have been obtained with resistivities in the range from 4.1×10-3to 5.3×104 Ωcm, carrier densities more than 2.6×1020 cm-3 and Hall mobilities between 5.78 and 13.11 cm2/V/s for films. The average transmittance reaches 75% in the visible spectrum. The quality of obtained films depends on substrate temperature during film fabrication.
基金Supported by the National Natural Science Foundation of China under Grant No 11374114
文摘Ta-doped titanium dioxide films are deposited on fused quartz substrates using the rf magnetron sputtering technique at different substrate temperatures. After post-annealing at 550℃ in a vacuum, all the films are crystallized into the polycrystalline anatase TiO2 structure. The effects of substrate temperature from room temperature up to 350℃ on the structure, morphology, and photoelectric properties of Ta-doped titanium dioxide films are analyzed. The average transmittance in the visible region(400-800 nm) of all films is more than 73%.The resistivity decreases firstly and then increases moderately with the increasing substrate temperature. The polycrystalline film deposited at 150℃ exhibits a lowest resistivity of 7.7 × 10^-4Ω·cm with the highest carrier density of 1.1×10^21 cm^-3 and the Hall mobility of 7.4 cm^2·V^-1s^-1.
基金Funded by the National Natural Science Foundation of China (No. 60372002)
文摘Based on the study of a new type of conducting polymer poly (3,4-ethylenedioxythiophene) (PEDOT),we focussed on the preparation and characteristics of PEDOT nanoparticles made by reversed micelle method.Moreover,we deeply investigated the optical,electrical and the thermal stability of PEDOT nanoparticles.The main results are as follows: the small-sized PEDOT nanoparticles were prepared and utilized by different methods,such as ultraviolet/visible (UV-Vis) spectroscopy,Fourier-transform infrared (FT- IR) spectrum,scanning electron microscopy(SEM) and so on.The results show that the amount of oxidizer,ultrasonic treatment,polymerizing temperature and doping degree can influent morphology,electrical ability and gas sensitivity of PEDOT nanoparticles.The Bragg peaks of nanoparticles at 6.7°,12.7°,25° were observed by XRD and the better orientation of molecular chain was attributed to the effective doping of toluene-p-sulfonic acid,which also resulted in an enhancement of thermal stability of nanoparticles than conventional PEDOT.
文摘In this work,Yb2O3 and Mg O were used as sintering aids in preparing silicon nitride ceramics by gas pressure sintering( 0. 6 MPa N2atmosphere) to investigate how the amounts of Yb2O3- Mg O influence the mechanical properties and thermal conductivity of silicon nitride ceramics. The total contents of Yb2O3- Mg O added were 1 mol%,2 mol%,4 mol%,6 mol%,8 mol%,10 mol%,12 mol%,14 mol%,keeping the Yb2O3-Mg O molar ratio of 1 ∶ 1 steadily. Curves of the relative density,thermal conductivity and bending strength plotted against the aids content present a ‘mountain'shape with a maximum at nearly 10 mol% aids. The fracture toughness increased with the amounts of additives up to10 mol% and decreased slightly thereafter. The mechanical properties and thermal conductivity were almost proportional to the amount of the additives before10 mol%. When the content of aids exceeded 10 mol%,it would weaken the mechanical properties and thermal conductivity of the ceramics. The optimum content of Yb2O3- Mg O was 10 mol% by gas pressure sintering( 0. 6MPa) at 1 850 ℃ for 4 h,which led to a relative density of 98. 9%,a flexural strength of( 966 ± 38)MPa as well as a fracture toughness of( 6. 29 ± 0. 29)MPa·m1 /2and thermal conductivity of 82 W /( m·K).
文摘Studies of the rocks′ electrical properties under high temperature and pressure have found favors in the geophysicist′s eyes, because those studies are becoming to be the important methods to understand the earth′s interior materials, their migration and evolution. This article introduces the development and significant of those studies from the measurements, instruments and affections, etc .