The poly(epoxy-N-methylaniline)conductive organic carrier was used as the bonding phase of the low-temperature conductive silver paste.Then,this was mixed with different proportions of silver powder to prepare the low...The poly(epoxy-N-methylaniline)conductive organic carrier was used as the bonding phase of the low-temperature conductive silver paste.Then,this was mixed with different proportions of silver powder to prepare the low-temperature conductive silver paste.Afterwards,the effect of the conductive organic carrier on the properties of the low-temperature conductive silver paste was determined by IR,DMA and SEM.The results revealed that the prepared conductive paste has good conductivity,film-forming performance,printing performance,low-temperature curing performance,and anti-aging performance.When the mass percentage of the bonding phase/conductive phase was 40/60,the lowest volume resistivity of the conductive silver paste was 4.9×10^(−6)Ω⋅cm,and the conductivity was the best.展开更多
A series of water-based conductive carbon pastes were prepared by wet ball milling, followed by vacuum defoaming using isopropyl alcohol, propylene glycol or glycerin as co-solvents. Screen printing was then used to p...A series of water-based conductive carbon pastes were prepared by wet ball milling, followed by vacuum defoaming using isopropyl alcohol, propylene glycol or glycerin as co-solvents. Screen printing was then used to prepare conductive patterns. To determine the influence of co-solvent hydroxyl group number on the properties of water-based conductive carbon pastes, the rheological properties of the pastes and the surface morphologies and conductivities of the printed patterns were characterized. The results show that paste viscosity increased with the number of hydroxyl groups and the latter also affected thixotropy. In addition, the boiling points and surface tensions of the co-solvents increased consistently with hydroxyl group number, affecting the hydrodynamic flow. The conductive carbon paste created using propylene glycol as a co-solvent was the best for screen printing because of its weak coffee-ring effect and appro- priate rheological properties, resulting in a smooth coating surface and uniform deposition of the fillers. The resistivity of the pattern printed using paste PG, containing the closest packing of conductive carbon black particles, was 0.44 Ω cm.展开更多
Wearable gas sensors can improve early warning provision for workers in special worksites and can also be used as flexible electronic platforms.Here,the flexible multifunctional gas sensor was prepared by grafting gra...Wearable gas sensors can improve early warning provision for workers in special worksites and can also be used as flexible electronic platforms.Here,the flexible multifunctional gas sensor was prepared by grafting graphene oxide(GO)-Ag onto cotton fabric after swelling.The maximum bacterial inhibition rate of GO-150/cotton fabric was 95.6%for E.coli and 87.6%for S.aureus,while retaining the original high moisture permeability of cotton fabric.So GO/cotton fabric can resist the multiplication of bacteria.At the same time,GO can greatly improve the UV protection performance of cotton fabric used in garments.With increase of the GO concentration,the UV protection ability of composite fabric is enhanced.Finally,GO-Ag/cotton fabric sensors had stable NH3 gassensitive properties and good washing stability.In conclusion,these cotton fabric sensors with antibacterial properties,UV resistance and highly sensitive gas-sensitive properties have potential applications in wearable early warning devices and textile products.展开更多
基金fund for this work was provided by the“Research on Key Technologies of Photosensitive Conductive Silver Paste Based on Domestic Circuit Protection Micro Chip Components”(Project No.BE2020008 and Supporting Author:Chen P).
文摘The poly(epoxy-N-methylaniline)conductive organic carrier was used as the bonding phase of the low-temperature conductive silver paste.Then,this was mixed with different proportions of silver powder to prepare the low-temperature conductive silver paste.Afterwards,the effect of the conductive organic carrier on the properties of the low-temperature conductive silver paste was determined by IR,DMA and SEM.The results revealed that the prepared conductive paste has good conductivity,film-forming performance,printing performance,low-temperature curing performance,and anti-aging performance.When the mass percentage of the bonding phase/conductive phase was 40/60,the lowest volume resistivity of the conductive silver paste was 4.9×10^(−6)Ω⋅cm,and the conductivity was the best.
文摘A series of water-based conductive carbon pastes were prepared by wet ball milling, followed by vacuum defoaming using isopropyl alcohol, propylene glycol or glycerin as co-solvents. Screen printing was then used to prepare conductive patterns. To determine the influence of co-solvent hydroxyl group number on the properties of water-based conductive carbon pastes, the rheological properties of the pastes and the surface morphologies and conductivities of the printed patterns were characterized. The results show that paste viscosity increased with the number of hydroxyl groups and the latter also affected thixotropy. In addition, the boiling points and surface tensions of the co-solvents increased consistently with hydroxyl group number, affecting the hydrodynamic flow. The conductive carbon paste created using propylene glycol as a co-solvent was the best for screen printing because of its weak coffee-ring effect and appro- priate rheological properties, resulting in a smooth coating surface and uniform deposition of the fillers. The resistivity of the pattern printed using paste PG, containing the closest packing of conductive carbon black particles, was 0.44 Ω cm.
基金We thank the Scientific Research Foundation of Zhejiang Sci-Tech University(ZSTU)under Grant Nos.19082472-Y and 19012099-Y.
文摘Wearable gas sensors can improve early warning provision for workers in special worksites and can also be used as flexible electronic platforms.Here,the flexible multifunctional gas sensor was prepared by grafting graphene oxide(GO)-Ag onto cotton fabric after swelling.The maximum bacterial inhibition rate of GO-150/cotton fabric was 95.6%for E.coli and 87.6%for S.aureus,while retaining the original high moisture permeability of cotton fabric.So GO/cotton fabric can resist the multiplication of bacteria.At the same time,GO can greatly improve the UV protection performance of cotton fabric used in garments.With increase of the GO concentration,the UV protection ability of composite fabric is enhanced.Finally,GO-Ag/cotton fabric sensors had stable NH3 gassensitive properties and good washing stability.In conclusion,these cotton fabric sensors with antibacterial properties,UV resistance and highly sensitive gas-sensitive properties have potential applications in wearable early warning devices and textile products.