Study on deformation and microstructure characterizations of mild steel joints by continuous drive friction welding

Macro-deformation characteristics of continuous drive friction welded mild steel joints were examined by using one deformable workpiece （objective） and the other undeformable one （rigid）. The microstructure evolution and hardness change across the joint were studied. The results show that the axial shortening and radial increment of joints increase with increasing the frictiou time at l 200 rpm. The cementite particles of pearlites in the weld center are uniformly distributed on the ferrite matrix, while the cementites of the pearlite in the thermal-mechanically affected zone are broken and discontinuously dispersed in the pearlite. The hardness decreases rapidly from the weld center to the parent metal under the coupled effects of heat and deformation during the rapid heating and cooling processes.

Evolution of microstructural and mechanical properties of AISI 316 during continuous drive friction welding process

The aim of present study is introducing a method by subdividing friction welding phases into three steps according to the temperature change during continuous drive friction welding operation. Thermal curve allowable subdividing of the friction welding phase's time into three distinct periods, while the microstructure evolution during friction welding goes through three different situations. The effects of three distinct periods were achieved by macro-microscopy, microhardness HV_(0.1), tensile tests and scanning electronic microscopy(SEM).The results clearly show that the microstructure during the friction phase goes through three completely different situations which mechanically influenced on microstructure, tensile strength and ductility of the welded joint.

Effect of temperature field on flashes formation of continuous drive friction welding

On basis of the finite element software DEFORM, the 2D coupled thermo-mechanical model of continuous drive friction welding of ring parts is established. The temperature and the flashes during the welding process are investigated. The results of numerical simulation show that the temperature of friction surface is higher than that of other region and the peak temperature increases with the increase of welding time. During the process of friction stage, no flash appears because of the low temperature and the small axial friction pressure. At the forging stage, the flashes appear, whose dimensions and bending degree increase with the increase of welding temperature. Moreover, with the increase of rotational velocity and axial forging pressure, the dimensions and the bending degree of flashes of continuous drive friction welding increase.

Microstructure and mechanical properties of continuous drive friction welded Ti_(2)AlNb alloy under different rotational rates

Ti_(2)AlNb-based alloy was joined in a continuous drive friction welding machine under different rotational rates(500,1000 and 1500 r/min).The microstructure and mechanical properties of the joints were investigated.It is shown that the weld zone(WZ) is fully composed of recrystallized B2 phase,and the grain size decreases with increasing rotational rate.The thermo-mechanically affected zone(TMAZ) suffers severe deformation during welding,due to which most of original precipitation phase is dissolved and streamlines are present.In the heat affected zone(HAZ),only the fine O phase is dissolved.The as-welded joint produced using 1000 r/min has the best mechanical properties,whose strength and elongation are both close to those of the base metal,while the as-welded joint obtained using 500 r/min exhibits the worst mechanical properties.Post-weld annealing treatment annihilates the deformation microstructure and fine O phase precipitates in the joints,consequently improving the mechanical properties significantly.Decomposed α_(2) phase is a weakness for the mechanical performance of the joint since microcracks are apt to form in it in the tensile test.

Parametric optimization and microstructural characterization of friction welded aeronautic aluminum alloy 2024

Continuous drive friction welding was employed to join the aeronautic aluminum alloy 2024.Parametric optimization and microstructural characterization were investigated.Results show that friction pressure is the most significant factor influencing the tensile strength of joints.To obtain a high joint efficiency,the combination of moderate friction pressure,less friction time and higher upset pressure is recommended.The optimized joint efficiency from Taguchi analysis reaches 92% of base metal.Under the optimized experimental condition,the interfacial peak temperature is calculated analytically in the range of 779-794 K,which is validated by experimental data.Fine recrystallized grains caused by the high temperature and plastic deformation are observed in the friction interface zone.The grain refinement is limited in the thermo-mechanically affected zone,where most of matrix grains are deformed severely.The extensive dissolution and limited re-precipitation of strengthening phases result in a lower microhardness in the friction interface zone than that in the thermo-mechanically affected zone.