Prevention and Control of Chlorella for C30 Concrete Surface with Coral Aggregate

C30 coral aggregate concrete with chlorella control effect was prepared by adding nano-TiO_(2) and hydrophobic material,and the effects of nano-TiO_(2) and hydrophobic material on the basic properties of C30 coral aggregate concrete and chlorella control effect under different experimental conditions were compared.The experimental results show that nano-TiO_(2) and hydrophobic materials have a certain degree of influence on the basic properties of concrete,but the influence is not significant.Under long-term immersion,nano-TiO_(2) and hydrophobic materials can inhibit the growth of Chlorella vulgaris.The maximum fluorescence value of concrete is decreased by 53.6% after adding TiO_(2),and the maximum fluorescence value of concrete is prolonged by 20%(1 day).The maximum fluorescence value of concrete is decreased by 67.7% after adding hydrophobic materials,and the maximum fluorescence value of concrete is also prolonged by 20%(1 day);Under the condition of simulated tidal water,the inhibition effect of Nano-TiO_(2) on the growth degree and growth rate of Chlorella vulgaris is weakened,at this time the maximum fluorescence value of concrete mixed with nano-TiO_(2) is decreased by 50.5%,and the maximum fluorescence value is only prolonged by 14.3%;while the inhibition of hydrophobic materials on the growth degree and growth rate of Chlorella vulgaris is enhanced significantly,and the maximum fluorescence value of concrete with hydrophobic materials is decreased by 80.3%;the maximum fluorescence time is prolonged by 114.3%.

煤矸石混凝土性能研究现状

煤矸石是在原煤开采过程中产生的一种工业固体废弃物,其堆存量大,利用率相对较低。若将煤矸石用作混凝土骨料,不仅能有效解决煤矸石堆存造成的环境污染,还能缓解天然砂石资源短缺的问题,为煤矸石的大规模利用开辟一条有效途径。该文针对煤矸石作为混凝土骨料的应用特性,系统分析了煤矸石化学成分、矿物组成以及物理特性,概述了国内外关于煤矸石作为骨料对混凝土的工作性能、力学性能、体积稳定性以及耐久性的影响规律,并展望了煤矸石在混凝土骨料应用中的发展趋势,以期为煤矸石在混凝土中的大规模推广利用提供参考。

固废粗集料平均弹性模量与混凝土弹性模量的相关性

试验研究了12种不同固废粗集料压碎值试验中σ-ε曲线与配制混凝土的静态弹性模量之间关系,进行了压碎值试验固废粗集料变形的离散元数值模拟,分析了国内外主要标准中公式计算固废粗集料混凝土弹性模量误差偏大的原因。研究结果表明:基于中国、美国和欧洲标准的普通密度固废粗集料混凝土弹性模量计算值分别高出实测值45.5%、15.8%和52.5%;固废粗集料在压碎值试验σ-ε曲线的线性区间主要发生弹性变形;建立的固废粗集料σ-ε曲线指数模型拟合度高,R^(2)均大于0.99;通过在传统的压碎值试验中引入粗集料平均弹性模量、含水系数等参数,回归建立了固废粗集料混凝土弹性模量半经验公式,R^(2)为0.867。利用已有文献数据对半经验公式的普适性进行了检验,高判定系数(R^(2)=0.895)实测值与预测值的比较表明模型具有有效性,为快速、可靠预测固废粗集料混凝土弹性模量提供了依据。

自燃煤矸石粗骨料混凝土双变量强度公式研究

通过对16组自燃煤矸石粗骨料混凝土试件的试验,研究了自燃煤矸石粗骨料压碎值、水胶比对混凝土抗压强度的影响。利用多元回归建立了自燃煤矸石压碎值、水胶比和混凝土28 d抗压强度之间的回归方程,并由25组试件检验,普适性良好。自燃煤矸石粗骨料混凝土双变量强度公式的建立,对自燃煤矸石粗骨料混凝土配合比设计及强度推算具有重要的实际意义。

关于水泥混凝土用粗集料压碎值技术标准的探讨

随着我国公路基础建设投资的加大以及环保政策的推进,混凝土用碎石供应一度紧张,碎石质量控制难度加大。加之新的试验规程对碎石压碎值试验方法作了调整,而新的规范提高了压碎值的要求,使得满足现行规范要求的碎石料源更少。通过对既往各版本试验规程的分析研究,发现各规范之间对于碎石压碎值的要求并不统一,且新的试验规程对水泥混凝土用碎石压碎值规定过于严格。通过大量现场采集样本,运用MINITAB软件中提供的过程能力分析工具,采用统计方法分析出多地区碎石压碎值数据分布情况,发现我国很多地区的碎石压碎值难以满足现行规范的要求,得出了在江苏及周边地区石灰岩碎石压碎值满足现行桥梁结构混凝土规范标准的几率较小、对推进工程建设进度将产生较大影响的结论。据此,提出对现行行业标准进行调整的建议。

水泥粉煤灰稳定砖、混凝土再生碎石试验

为研究水泥粉煤灰稳定砖、混凝土再生碎石作为公路材料的适用性能,通过砖、混凝土再生碎石压碎值试验,设计了15组不同配比水泥粉煤灰稳定砖、混凝土再生碎石混合料,测试其击实特性和力学性能,分析砖、混凝土骨料掺比对级配碎石压碎值和击实指标的影响规律,以及水泥剂量和龄期对混合料力学性能的影响规律。结果表明:混合料压碎值满足最低等级公路要求时砖再生碎石掺量约为38%;随着砖再生碎石掺量增加,混合料的最佳含水率和最大干密度分别呈近似线性增大和减小趋势,相同水泥掺量混合料的无侧限抗压强度和间接抗拉强度基本呈线性减小的趋势,并建立了无侧限抗压强度和间接抗拉强度的关系模型。给出了不同等级公路水泥粉煤灰稳定砖、混凝土再生碎石的建议配比方案,为工业废渣利用提供了借鉴。

再生骨料掺量对沥青混凝土路用性能的影响

对废旧水泥混凝土块采用冲击破碎法制备再生骨料,先后通过试验研究了再生骨料的性能和再生骨料沥青混凝土的性能。研究发现,相较于天然骨料,再生骨料外表面裹附着的多空隙水泥砂浆一方面会导致其表观相对密度、毛体积相对密度、吸水率均大幅增加;另一方面会导致其高温压碎值和洛杉矶磨耗值分别增长约97.73%和112.03%。而再生骨料中水泥砂浆的多空隙结构也是造成沥青混合料性能降低的主要因素。在沥青混合料中,当再生骨料的占比未超过30%时,其内部支撑骨料材料未发生改变,故其高温稳定性能未发生改变,即仅降低1.45%;但随着再生骨料占比的持续增长,其高温稳定性能将加速降低;另外,沥青混凝土的低温弯曲应变、浸水残留稳定度和冻融劈裂强度比均则随着再生骨料占比的增长而降低,而当再生骨料的占比未超过30%时,其降低幅度分别为9.33%,4.19%,3.84%,均可满足路用要求。

废弃混凝土再生集料的生产流程及破碎工艺研究

高速公路改扩建过程中会产生大量废弃结构物混凝土,由于再生集料资源化利用价值意识不足、技术条件受限、废旧混凝土破碎加工设备不匹配等因素,导致现有加工方式较为粗放,生产效率低,再生料品质难以保证。本文从硬件设施优化、生产工艺改进、再生集料质量控制等方面出发,提出相应的技术路线及改进措施,实现结构物混凝土再生集料资源化利用。

Test Study on the Recycled Aggregate and Concrete Regenerated from Worn Cement Concrete Pavement

Regenerate utilization of worn cement concrete is the key technical problem to be solved in traffic field while the cement concrete pavement built long ago durative disrepair. The study aimed at the worn cement concrete which can not be reused in site,get recycled aggregate according to the practically technics of regenerate,and then carry out test study on the aggregate and recycle aggregate cement concrete. Test results show recycled fine aggregate is about 26% of recycled aggregate,and substantive sand pulps are adhere on the surface of recycled while the distinct crackle appears on this sand pulp surface. relative to the natural aggregate,one of the remarkable characters of the recycled aggregate is that the inartificial water ratio is relatively low and the water-absorbing ratio can reach 4%～12%,and the water-absorbing ratio increased while the grain getting fine. the second remarkable characters of recycled coarse aggregate is that the weared stone value and crushed stone value of recycled coarse aggregate are both bigger,the Los-angeles weared stone value is 32.7,the crushed stone value is 26.5. So,the recycled aggregate can not meet the criterion,but after mixed into 40% natural aggregate,it can meet. The mixture ratio test results proved that based on the dosage of cement we can through reduce water cement ratio and augment water quantity to improve the working performance of recycled concrete. The destroy form of recycled concrete goes all the way with natural concrete,the recycled aggregate can absolutely used in cement concrete under C50.

基于CBR法的旧水泥混凝土路面再生集料级配碎石级配控制范围

为确定旧水泥混凝土路面再生集料级配碎石关键筛孔控制范围,在分析各国级配碎石关键筛孔控制范围的基础上,以CBR试验方法为测试手段,分析了集料4.75mm通过率、最大粒径和0.075mm通过率等因素对CBR值的影响。结果表明:最大粒径为31.5mm时CBR值较好,随着4.75mm和0.075mm通过率的增加,CBR值均呈现出先增加后减小的趋势。提出了旧水泥混凝土路面再生集料级配碎石级配控制范围的建议。

宁夏桥涵水泥混凝土用集料压碎值取值研究

针对宁夏桥涵水混凝土用集料,采用不同规范压碎值试验方法及不同评价标准,通过试验、分析、研究,最终提出了“桥规”新的压碎值控制标准。

梁体混凝土静力受压弹性模量影响因素分析

简支预制梁在铁路建设中被广泛运用,而梁体混凝土弹性模量是保证梁体质量的关键因素之一。经过多次配合比和实际操作试验,得出:通过控制梁体混凝土的骨料压碎值、砂率、粉煤灰掺量和使用成熟的施工工艺,可有效保证并提高混凝土弹性模量。对提高简支预制梁梁体的工作性能和力学性能具有参考价值。

压碎值指标对再生混凝土抗压强度的影响

采用来源于不同场地的废弃混凝土制备了3种不同的再生骨料，进行了8组饱和面干状态和气干状态下的压碎值指标试验。通过试验研究并对比国内外学者研究成果，结果表明：再生骨料的压碎值指标高于天然骨料的2．0倍～2．5倍，饱和面干状态比气干状态的压碎值指标高7．22％～18．20％。在此基础上，通过26组抗压强度试验研究不同来源骨料在不同取代率下抗压强度的变化规律。试验结果表明，由于骨料基材较大的变异性使得试验结果差异较大甚至截然相反。为探索骨料强度与抗压强度之间的关系，对比分析了12组气干状态和饱和面干状态下压碎值指标对抗压强度的影响。经过最小二乘法拟合并对拟合结果分析表明：随骨料压碎值指标的增加，骨料强度的降低，再生混凝土的抗压强度并不一定降低。