The pH-sensitive copolymer hydrogels were prepared with the monomers of acrylic acid and N-vinyl-2-pyrrolidone based on gamma radiation technique. The morphology of the hydrogels was monitored by using scanning electr...The pH-sensitive copolymer hydrogels were prepared with the monomers of acrylic acid and N-vinyl-2-pyrrolidone based on gamma radiation technique. The morphology of the hydrogels was monitored by using scanning electron microscope. The influence of absorbed dose, monomer composition and concentration on the swelling ratio (SR) of the hydrogels were investigated in detail. The effect of pH and temperature of the swelling medium on the swelling behavior of the hydrogels were also examined. The results show that the SR of the copolymer hydrogels decreases with the monomer concentration and absorbed dose increasing. The copolymer hydrogels show a better pH-sensitive behavior. In alkaline solution, the SR of the hydrogels is much higher than in acid solution.展开更多
In this study, the main objective is to develop a good chelation and ion exchange hydrogel. This hydrogel is obtained by polymerization of dimethyl amino ethyl methacrylate (DMAEMA) and acrylic acid (AAc) by gamma irr...In this study, the main objective is to develop a good chelation and ion exchange hydrogel. This hydrogel is obtained by polymerization of dimethyl amino ethyl methacrylate (DMAEMA) and acrylic acid (AAc) by gamma irradiation, for the purpose of separation of some heavy and toxic metals from water. UV spectroscopy is applied to determine the metal ion concentration before and after treatment. The FTIR spectral analysis has identified the bond structure of PAAc, DMAEMA and P (DMAEMA/AAc) hydrogels. Microstructure and nanostructure are investigated by means of SEM and positron annihilation lifetime spectroscopy (PALS) respectively. A maximum swelling percent is found for 80/20 DMAEMA/AAc at free-volume hole size and fraction of 97?3 and 3.4% respectively. The P (DMAEMA/AAc) and PAAc hydrogels have been applied for Cu+2, Co+2 and Ni+2 removals from aqueous solutions, and the factors affecting the adsorption capacity are determined. The adsorption capacity of P (DMAEMA/AAc) is found to be higher than the corresponding ones PAAc. Its experimental results showed that, the maximum adsorption of P (DMAEMA/AAc) after 24 h occurs at pH 7 with concentration of 250 ppm for Ni+2 ions and at pH 5 with concentration of 40 ppm for Cu+2 and Co+2 ions. The adsorption affinity of P (DMAEMA/AAc) hydrogel at different treatment contact times is in the following order Ni > Cu > Co. However, the order becomes Co > Ni > Cu by the variation of the pH of the metal ion solution;the variation of its concentration leads to a different order of Cu > Co > Ni.展开更多
基金Natural Science Foundation of Henan Province (0611023900)
文摘The pH-sensitive copolymer hydrogels were prepared with the monomers of acrylic acid and N-vinyl-2-pyrrolidone based on gamma radiation technique. The morphology of the hydrogels was monitored by using scanning electron microscope. The influence of absorbed dose, monomer composition and concentration on the swelling ratio (SR) of the hydrogels were investigated in detail. The effect of pH and temperature of the swelling medium on the swelling behavior of the hydrogels were also examined. The results show that the SR of the copolymer hydrogels decreases with the monomer concentration and absorbed dose increasing. The copolymer hydrogels show a better pH-sensitive behavior. In alkaline solution, the SR of the hydrogels is much higher than in acid solution.
文摘In this study, the main objective is to develop a good chelation and ion exchange hydrogel. This hydrogel is obtained by polymerization of dimethyl amino ethyl methacrylate (DMAEMA) and acrylic acid (AAc) by gamma irradiation, for the purpose of separation of some heavy and toxic metals from water. UV spectroscopy is applied to determine the metal ion concentration before and after treatment. The FTIR spectral analysis has identified the bond structure of PAAc, DMAEMA and P (DMAEMA/AAc) hydrogels. Microstructure and nanostructure are investigated by means of SEM and positron annihilation lifetime spectroscopy (PALS) respectively. A maximum swelling percent is found for 80/20 DMAEMA/AAc at free-volume hole size and fraction of 97?3 and 3.4% respectively. The P (DMAEMA/AAc) and PAAc hydrogels have been applied for Cu+2, Co+2 and Ni+2 removals from aqueous solutions, and the factors affecting the adsorption capacity are determined. The adsorption capacity of P (DMAEMA/AAc) is found to be higher than the corresponding ones PAAc. Its experimental results showed that, the maximum adsorption of P (DMAEMA/AAc) after 24 h occurs at pH 7 with concentration of 250 ppm for Ni+2 ions and at pH 5 with concentration of 40 ppm for Cu+2 and Co+2 ions. The adsorption affinity of P (DMAEMA/AAc) hydrogel at different treatment contact times is in the following order Ni > Cu > Co. However, the order becomes Co > Ni > Cu by the variation of the pH of the metal ion solution;the variation of its concentration leads to a different order of Cu > Co > Ni.