The title compound, thiodiglycol dimethacrylate (TDGDMA), was synthesized from thiodiglycol and methacryloyl chloride by phase transfer catalysis reaction, and its structure was confirmed by FTIR and 1H-NMR analyses. ...The title compound, thiodiglycol dimethacrylate (TDGDMA), was synthesized from thiodiglycol and methacryloyl chloride by phase transfer catalysis reaction, and its structure was confirmed by FTIR and 1H-NMR analyses. TDGDMA possesses good polymerizability to produce a homopolymer resin with excellent transparency (T%, 90), moderate refractivity (nd20, 1.55), lower dispersivity (Abbe's number, 50.6) and higher glass transition temperature (Tg, 119°C). Through copolymerization with styrene (St) or styrene-4,4'-bismethacryloyloxydiphenylsulfone (BPSDMA), many properties of the copolymer such as refractive index, Abbe's number, strength, onset wavelength in the UV region and density were significantly modified. A copolymer resin with balanced properties between refractive index and dispersion was produced at the weight ratio of TDGDMA:St:BPSDMA (25:50:25), where nd20 and Abbe's number are 1.5815 and 36.5, respectively.展开更多
A stable epoxy emulsion was prepared with epoxy resin （EP） as raw material, 2-acrylamido-2- methyl-l-propanesulfonic acid （AMPS） as modifier and benzoyl peroxide as initiator. By criterion of yield of the copolyme...A stable epoxy emulsion was prepared with epoxy resin （EP） as raw material, 2-acrylamido-2- methyl-l-propanesulfonic acid （AMPS） as modifier and benzoyl peroxide as initiator. By criterion of yield of the copolymer AMPS-EP, water-solubility, change of the acid value and intrinsic viscosity [η] along with reaction time, the copolymerization course was deduced. It is found that during the process, AMPS takes part in both the grafting copolymerization with epoxy principal chain and the ring-opening polyaddition with epoxy group. It is also discovered that the yield of AMPS-EP and water dispersing varies with reaction time. When it reaches 1.5 h, AMPS-EP can obtain good water-solubility; but the water-solubility will go bad gradually if it exceeds 3.5 h.. R spectrum analysis indicates that partial epoxy group partially remains and the others create sulfonic ester.展开更多
Synthesis of super absorbent resin was studied by using graft copolymerization of cornstarch and acrlyic acid.The effects of various factors including that the initiator and its concentration,monomer concentration,rea...Synthesis of super absorbent resin was studied by using graft copolymerization of cornstarch and acrlyic acid.The effects of various factors including that the initiator and its concentration,monomer concentration,reaction temperature,pH valuse,reaction time and cornstarch gelatimzed on resin absorbing water ratio was investigated,respectively.The optimal technological condition waas obtained via the comparative analysis.Under the optimal technological condition,the resin absorbing water ratio may reached 880g*g-1.展开更多
基金This project was supported by the Natural Science Foundation of Zhejiang Province (599103).
文摘The title compound, thiodiglycol dimethacrylate (TDGDMA), was synthesized from thiodiglycol and methacryloyl chloride by phase transfer catalysis reaction, and its structure was confirmed by FTIR and 1H-NMR analyses. TDGDMA possesses good polymerizability to produce a homopolymer resin with excellent transparency (T%, 90), moderate refractivity (nd20, 1.55), lower dispersivity (Abbe's number, 50.6) and higher glass transition temperature (Tg, 119°C). Through copolymerization with styrene (St) or styrene-4,4'-bismethacryloyloxydiphenylsulfone (BPSDMA), many properties of the copolymer such as refractive index, Abbe's number, strength, onset wavelength in the UV region and density were significantly modified. A copolymer resin with balanced properties between refractive index and dispersion was produced at the weight ratio of TDGDMA:St:BPSDMA (25:50:25), where nd20 and Abbe's number are 1.5815 and 36.5, respectively.
文摘A stable epoxy emulsion was prepared with epoxy resin （EP） as raw material, 2-acrylamido-2- methyl-l-propanesulfonic acid （AMPS） as modifier and benzoyl peroxide as initiator. By criterion of yield of the copolymer AMPS-EP, water-solubility, change of the acid value and intrinsic viscosity [η] along with reaction time, the copolymerization course was deduced. It is found that during the process, AMPS takes part in both the grafting copolymerization with epoxy principal chain and the ring-opening polyaddition with epoxy group. It is also discovered that the yield of AMPS-EP and water dispersing varies with reaction time. When it reaches 1.5 h, AMPS-EP can obtain good water-solubility; but the water-solubility will go bad gradually if it exceeds 3.5 h.. R spectrum analysis indicates that partial epoxy group partially remains and the others create sulfonic ester.
文摘Synthesis of super absorbent resin was studied by using graft copolymerization of cornstarch and acrlyic acid.The effects of various factors including that the initiator and its concentration,monomer concentration,reaction temperature,pH valuse,reaction time and cornstarch gelatimzed on resin absorbing water ratio was investigated,respectively.The optimal technological condition waas obtained via the comparative analysis.Under the optimal technological condition,the resin absorbing water ratio may reached 880g*g-1.