The corrosion behavior and electrochemical impedance spectroscopy (EIS) features of 8090 Al-Li alloys in EXCO solution were investigated, and the EIS was simulated using an equivalent circuit. At the beginning of imme...The corrosion behavior and electrochemical impedance spectroscopy (EIS) features of 8090 Al-Li alloys in EXCO solution were investigated, and the EIS was simulated using an equivalent circuit. At the beginning of immersion in EXCO solution, the EIS is comprised by a depressed capacitive arc at high-mediate frequency and an inductive arc at low frequency, and the inductive component decreases and disappears with im- mersion time. Once exfoliation or severe pitting corrosion is produced, two capacitive arcs appear in the EIS. These two capacitive arcs are originated from the two parts of the corroded alloy surface, the original flat alloy surface and the new inter-face exposed to the aggressive EXCO solution due to the exfoliation or pitting corrosion. Some corrosion development features of 8090 Al-Li alloys in EXCO solution can be obtained through simulated EIS information.展开更多
In order to evaluate the degree and severity of Al-Mg-Mn-Sc-Zr alloy in exfoliation corrosion(EXCO) solution quickly and nondestructively, electrochemical impedance spectroscopy(EIS) technique was employed. The Al-Mg-...In order to evaluate the degree and severity of Al-Mg-Mn-Sc-Zr alloy in exfoliation corrosion(EXCO) solution quickly and nondestructively, electrochemical impedance spectroscopy(EIS) technique was employed. The Al-Mg-Mn-Sc-Zr alloy suffers pitting corrosion in the EXCO solution. During pit incubation, the Nyquist diagram is composed of a depressed capacitive arc at high-mediate frequency and an inductive arc at low frequency. The inductive arc fades with immersion time, and the beginning of pitting corrosion and the appearance of two capacitive arcs have simultaneity. During pit propagation, the Nyquist diagram is composed of two overlapped capacitive arcs. As time goes on, two time constants are more clearly distinguished. The high frequency and low frequency capacitive arc are aroused by passive surface and new interface, respectively. An equivalent circuit is designed to fit EIS, and the experimental results and the fitted results have good correspondence. The degree and severity of pitting corrosion can be obtained by the features of EIS and comparing the fitted values of parameters at different times.展开更多
文摘The corrosion behavior and electrochemical impedance spectroscopy (EIS) features of 8090 Al-Li alloys in EXCO solution were investigated, and the EIS was simulated using an equivalent circuit. At the beginning of immersion in EXCO solution, the EIS is comprised by a depressed capacitive arc at high-mediate frequency and an inductive arc at low frequency, and the inductive component decreases and disappears with im- mersion time. Once exfoliation or severe pitting corrosion is produced, two capacitive arcs appear in the EIS. These two capacitive arcs are originated from the two parts of the corroded alloy surface, the original flat alloy surface and the new inter-face exposed to the aggressive EXCO solution due to the exfoliation or pitting corrosion. Some corrosion development features of 8090 Al-Li alloys in EXCO solution can be obtained through simulated EIS information.
文摘In order to evaluate the degree and severity of Al-Mg-Mn-Sc-Zr alloy in exfoliation corrosion(EXCO) solution quickly and nondestructively, electrochemical impedance spectroscopy(EIS) technique was employed. The Al-Mg-Mn-Sc-Zr alloy suffers pitting corrosion in the EXCO solution. During pit incubation, the Nyquist diagram is composed of a depressed capacitive arc at high-mediate frequency and an inductive arc at low frequency. The inductive arc fades with immersion time, and the beginning of pitting corrosion and the appearance of two capacitive arcs have simultaneity. During pit propagation, the Nyquist diagram is composed of two overlapped capacitive arcs. As time goes on, two time constants are more clearly distinguished. The high frequency and low frequency capacitive arc are aroused by passive surface and new interface, respectively. An equivalent circuit is designed to fit EIS, and the experimental results and the fitted results have good correspondence. The degree and severity of pitting corrosion can be obtained by the features of EIS and comparing the fitted values of parameters at different times.