Six kinds of Cr2O3 - Al2 O3 fused grains （the mass percent of Cr203 was 15%, 40%, 50%, 60%, 85% and 99%, respectively ） were prepared using chrome green and Al203 powder as starting materials by electro-fnsion, n...Six kinds of Cr2O3 - Al2 O3 fused grains （the mass percent of Cr203 was 15%, 40%, 50%, 60%, 85% and 99%, respectively ） were prepared using chrome green and Al203 powder as starting materials by electro-fnsion, named as CR15, CR40, CR50, CR60, CR85, and CR99, respectively. The corrosion resistance of the six kinds of Cr2O3- Al2O3.fused grains （4-1 ram） was studied using rotary slag corrosion method. The results show that： （ 1 ） the corrosion resistance of the fused grains increases with the Cr203 content and the grain size increasing; （2）the grains of CR99 and CR85 with higher Cr2O3 content are corroded at the slag surJace layer, because FeO and Al2O3. in the slag corrode the grains ; FeO reacts with Cr2O3 in the aggregates.forming （Fe, Cr ）3O4 ,spinel firstly, and the spinel reacts with other phases forming composite spinel; when FeO is fidly consumed, Al2 O3 penetrated into the grains reacts with Cr2O3 Jorming Al2O3 - Cr2O3 solid solution on the grains surface; （3） for CR60, the corrosion exists both in the slag surface layer and in the penetration layer; in the penetration layer, CaO and SiO2 react with Al2O3 in Al2O3 - Cr2O3 solid solution forming anorthite , gehlenite ,and glass phase; the grains of CR50, CR40 and CRI5 have the same corrosion mechanism with CR60 in the penetration layer.展开更多
文摘Six kinds of Cr2O3 - Al2 O3 fused grains （the mass percent of Cr203 was 15%, 40%, 50%, 60%, 85% and 99%, respectively ） were prepared using chrome green and Al203 powder as starting materials by electro-fnsion, named as CR15, CR40, CR50, CR60, CR85, and CR99, respectively. The corrosion resistance of the six kinds of Cr2O3- Al2O3.fused grains （4-1 ram） was studied using rotary slag corrosion method. The results show that： （ 1 ） the corrosion resistance of the fused grains increases with the Cr203 content and the grain size increasing; （2）the grains of CR99 and CR85 with higher Cr2O3 content are corroded at the slag surJace layer, because FeO and Al2O3. in the slag corrode the grains ; FeO reacts with Cr2O3 in the aggregates.forming （Fe, Cr ）3O4 ,spinel firstly, and the spinel reacts with other phases forming composite spinel; when FeO is fidly consumed, Al2 O3 penetrated into the grains reacts with Cr2O3 Jorming Al2O3 - Cr2O3 solid solution on the grains surface; （3） for CR60, the corrosion exists both in the slag surface layer and in the penetration layer; in the penetration layer, CaO and SiO2 react with Al2O3 in Al2O3 - Cr2O3 solid solution forming anorthite , gehlenite ,and glass phase; the grains of CR50, CR40 and CRI5 have the same corrosion mechanism with CR60 in the penetration layer.