The Crack Self-healing Properties of Cement-based Material with EVA Heat-melt Adhesive

An experimental program was carried out to investigate whether EVA （ethylene vinyl acetate copolymer） heat-melt adhesive can potentially act as a self-healing agent in cement-based material. The effects of incorporation of EVA and heating on the properties of mortar were studied. Self-healing capacity of EVA specimens was also verified. The experimental results show that the addition of EVA would not greatly affect original characteristics of the matrix when EVA content was less than 5%; the interface between EVA and cement matrix was well improved after heating, which allows a significant improvement in flexural strength and toughness of specimen; pre-damaged specimens in various degrees （30%, 50% and 70%） were effectively repaired by EVA and the repair efficiency all exceeded 100%.

Effect of drying cracks on swelling and self-healing of bentonite-sand blocks used as engineered barriers for radioactive waste disposal

Experiments were conducted to evaluate the healing of drying cracks in air-dried bentonite-sand blocks after hydration and swelling in groundwater,providing justifications to simplify the protection of blocks prior to installation in a high-level radioactive waste repository.Synthetic groundwater was prepared to represent the geochemistry of Beishan groundwater,and was used to hydrate the blocks during the swelling pressure and swelling strain measurements,as Beishan is the most promising site for China's repository.Healing of the surface cracks was recorded by photography,and healing of the internal cracks was visualized by CT images and hydraulic conductivity of air-dried blocks.The results indicate that the maximum swelling pressure and swelling strain are primarily affected by the geochemistry of Beishan groundwater,but not affected by the drying cracks.The maximum swelling pressure and swelling strain of air-dried blocks are comparable to or even higher than the pressure and strain of fresh blocks.The maximum swelling pressure measured in strong(i.e.high ion strength)Beishan groundwater was 44%of the pressure measured in deionized(DI)water,and the maximum swelling strain was reduced to 23%of the strain measured in DI water.Nevertheless,the remained swelling of the blocks hydrated in strong Beishan groundwater was sufficient to heal the surface and internal drying cracks,as demonstrated by the pictures of surface cracks and CT images.The hydraulic conductivity of the air-dried block permeated with strong groundwater was comparable(3.7×higher)to the hydraulic conductivity of the fresh block,indicating the self-healing of drying cracks after hydration and swelling in groundwater.A simplified method of protecting the block with plastic wraps before installation is recommended,since the remained swelling of the block hydrated in Beishan groundwater is sufficient to heal the drying cracks.

Mechanical reliable,NIR light-induced rapid self-healing hydrogel electrolyte towards flexible zinc-ion hybrid supercapacitors with low-temperature adaptability and long service life

Hydrogel electrolytes hold great potential in flexible zinc ion supercapacitors(ZICs)due to their high conductivity,good safety,and flexibility.However,freezing of electrolytes at low temperature(subzero)leads to drastic reduction in ionic conductivity and mechanical properties that deteriorates the performance of flexible ZICs.Besides,the mechanical fracture during arbitrary deformations significantly prunes out the lifespan of the flexible device.Herein,a Zn^(2+)and Li^(+)co-doped,polypyrrole-dopamine decorated Sb_(2)S_(3)incorporated,and polyvinyl alcohol/poly(N-(2-hydroxyethyl)acrylamide)double-network hydrogel electrolyte is constructed with favorable mechanical reliability,anti-freezing,and self-healing ability.In addition,it delivers ultra-high ionic conductivity of 8.6 and 3.7 S m^(-1)at 20 and−30°C,respectively,and displays excellent mechanical properties to withstand tensile stress of 1.85 MPa with tensile elongation of 760%,together with fracture energy of 5.14 MJ m^(-3).Notably,the fractured hydrogel electrolyte can recover itself after only 90 s of infrared illumination,while regaining 83%of its tensile strain and almost 100%of its ionic conductivity during−30–60°C.Moreover,ZICs coupled with this hydrogel electrolyte not only show a wide voltage window(up to 2 V),but also provide high energy density of 230 Wh kg^(-1)at power density of 500 W kg^(-1)with a capacity retention of 86.7%after 20,000 cycles under 20°C.Furthermore,the ZICs are able to retain excellent capacity even under various mechanical deformation at−30°C.This contribution will open up new insights into design of advanced wearable flexible electronics with environmental adaptability and long-life span.

A Self-Healing Optoacoustic Patch with High Damage Threshold and Conversion Efficiency for Biomedical Applications

Compared with traditional piezoelectric ultrasonic devices,optoacoustic devices have unique advantages such as a simple preparation process,anti-electromagnetic interference,and wireless long-distance power supply.However,current optoacoustic devices remain limited due to a low damage threshold and energy conversion efficiency,which seriously hinder their widespread applications.In this study,using a self-healing polydimethylsiloxane(PDMS,Fe-Hpdca-PDMS)and carbon nanotube composite,a flexible optoacoustic patch is developed,which possesses the self-healing capability at room temperature,and can even recover from damage induced by cutting or laser irradiation.Moreover,this patch can generate high-intensity ultrasound(>25 MPa)without the focusing structure.The laser damage threshold is greater than 183.44 mJ cm^(-2),and the optoacoustic energy conversion efficiency reaches a major achievement at 10.66×10^(-3),compared with other carbon-based nanomaterials and PDMS composites.This patch is also been successfully examined in the application of acoustic flow,thrombolysis,and wireless energy harvesting.All findings in this study provides new insight into designing and fabricating of novel ultrasound devices for biomedical applications.

Multifunctional phase change film with high recyclability, adjustable thermal responsiveness, and intrinsic self-healing ability for thermal energy storage

Phase change materials(PCMs) present promising potential for guaranteeing safety in thermal management systems.However,most reported PCMs have a single application in energy storage for thermal management systems,which does not meet the growing demand for multi-functional materials.In this paper,the flexible material and hydrogen-bonding function are innovatively combined to design and prepare a novel multi-functional flexible phase change film(PPL).The 0.2PPL-2 film exhibits solid-solid phase change behavior with energy storage density of 131.8 J/g at the transition temperature of42.1℃,thermal cycling stability(500 cycles),wide-temperature range flexibility(0-60℃) and selfhealing property.Notably,the PPL film can be recycled up to 98.5% by intrinsic remodeling.Moreover,the PPL film can be tailored to the desired colors and configurations and can be cleverly assembled on several thermal management systems at ambient temperature through its flexibility combined with shape-memory properties.More interestingly,the transmittance of PPL will be altered when the ambient temperature changes(60℃),conveying a clear thermal signal.Finally,the thermal energy storage performance of the PPL film is successfully tested by human thermotherapy and electronic device temperature control experiments.The proposed functional integration strategy provides innovative ideas to design PCMs for multifunctionality,and makes significant contributions in green chemistry,highefficiency thermal management,and energy sustainability.

Flexible,thermal processable,self-healing,and fully bio-based starch plastics by constructing dynamic imine network

The serious environmental threat caused by petroleum-based plastics has spurred more researches in developing substitutes from renewable sources.Starch is desirable for fabricating bioplastic due to its abundance and renewable nature.However,limitations such as brittleness,hydrophilicity,and thermal properties restrict its widespread application.To overcome these issues,covalent adaptable network was constructed to fabricate a fully bio-based starch plastic with multiple advantages via Schiff base reactions.This strategy endowed starch plastic with excellent thermal processability,as evidenced by a low glass transition temperature(T_(g)=20.15℃).Through introducing Priamine with long carbon chains,the starch plastic demonstrated superior flexibility(elongation at break=45.2%)and waterproof capability(water contact angle=109.2°).Besides,it possessed a good thermal stability and self-adaptability,as well as solvent resistance and chemical degradability.This work provides a promising method to fabricate fully bio-based plastics as alternative to petroleum-based plastics.

Shear resistance of assembled bentonite interface after confined water saturation and interfacial self-healing capacity

The requisite functions of a bentonite buffer in a deep geological repository depend on the sealing/healing of bentonite interfaces,with particular emphasis on the self-healing(automatic healing upon wetting)of assembled bentonite-bentonite interfaces.This study determined the shear resistance(including the peak shear strength and secant modulus)of densely compacted Gaomiaozi(GMZ)bentonite and its assembled interface after confined water saturation.The effect of bentonite dry density and saturation time on the shear resistance of saturated healed interfaces was elucidated,and the interfacial self-healing capacity was assessed.The results indicate that the shear resistance of the saturated healed interfaces increased with the bentonite dry density but had a non-monotonic correlation with the saturation time.For a given dry density of the bentonite,the saturated healed interface exhibits a lower peak shear strength than the saturated intact bentonite but a higher peak shear strength than the saturated separated interface.The saturated healed and separated interfaces have comparable shear moduli(secant moduli),which are lower than that of the saturated intact bentonite.The saturated healed interfaces display smooth shear failure planes,while the saturated assembled interfaces and intact bentonite exhibit comparable frictional angles.This indicates that interfacial self-healing plays a pivotal role in enhancing interfacial peak shear strength by facilitating microstructural bonding at the assembled interface.Finally,it can be stated that densely compacted GMZ bentonite has a robust interfacial self-healing capacity in terms of shear resistance.These findings contribute to the design of the bentonite buffer and facilitate the evaluation of its safe operation at specified disposal ages.

High performance photodegradation resistant PVA@TiO_(2)/carboxyl-PES self-healing reactive ultrafiltration membrane

The occurrence of ultrafiltration(UF)membrane fouling frequently hampers the sustainable advancement of UF technology.Reactive self-cleaning UF membranes can effectively alleviate the problem of membrane fouling.Nevertheless,the self-cleaning process may accelerate membrane aging.Addressing these concerns,we present an innovative design concept for composite self-healing materials based on self-cleaning UF membranes.To begin,TiO_(2)nanoparticles were incorporated into the polymer molecular structure via molecular design,resulting in the synthesis of TiO_(2)/carboxyl-polyether sulfone(PES)hybrid materials.Subsequently,the nonsolvent-induced phase inversion technique was employed to prepare a novel of UF membrane.Lastly,a polyvinyl alcohol(PVA)hydrogel coating was applied to the hybrid UF membrane surface to create PVA@TiO_(2)/carboxyl-PES self-healing reactive UF membranes.By establishing a covalent bond,the TiO_(2)nanoparticles were effectively and uniformly dispersed within the UF membrane,leading to exceptional self-cleaning properties.Furthermore,the water-absorbing and swelling properties of PVA hydrogel,along with its capacity to form hydrogen bonds with water molecules,resulted in UF membranes with improved hydrophilicity and active self-healing abilities.The results demonstrated that the water contact angle of PVA@5%TiO_(2)/carboxyl-PES UF membrane was 43.1°.Following a 1-h exposure to simulated solar exposure,the water flux recovery ratio increased from 48.16%to 81.03%.Moreover,even after undergoing five cycles of 12-h simulated sunlight exposure,the UF membranes exhibited a consistent retention rate of over 97%,thus fully demonstrating their exceptional self-cleaning,antifouling,and selfhealing capabilities.We anticipate that the self-healing reactive UF membrane system will serve as a pioneering and comprehensive solution for the self-cleaning antifouling challenges encountered in UF membranes while also effectively mitigating the aging effects of reactive UF membranes.

An intrinsically self-healing and anti-freezing molecular chains induced polyacrylamide-based hydrogel electrolytes for zinc manganese dioxide batteries

The anti-freezing strategy of hydrogels and their self-healing structure are often contradictory,it is vital to break through the molecular structure to design and construct hydrogels with intrinsic anti-freezing/self-healing for meeting the rapid development of flexible and wearable devices in diverse service conditions.Herein,we design a new hydrogel electrolyte(AF/SH-Hydrogel)with intrinsic anti-freezing/self-healing capabilities by introducing ethylene glycol molecules,dynamic chemical bonding(disulfide bond),and supramolecular interaction(multi-hydrogen bond)into the polyacrylamide molecular chain.Thanks to the exceptional freeze resistance(84%capacity retention at-20℃)and intrinsic self-healing capabilities(95%capacity retention after 5 cutting/self-healing cycles),the obtained AF/SH-Hydrogel makes the zinc||manganese dioxide cell an economically feasible battery for the state-of-the-art applications.The Zn||AF/SH-Hydrogel||MnO_(2)device offers a near-theoretical specific capacity of 285 m A h g^(-1)at 0.1 A g^(-1)(Coulombic efficiency≈100%),as well as good self-healing capability and mechanical flexibility in an ice bath.This work provides insight that can be utilized to develop multifunctional hydrogel electrolytes for application in next generation of self-healable and freeze-resistance smart aqueous energy storage devices.

Behavior Characteristics of Asphalt Components during the Process of Nano-cracks Temperature Self-healing

In order to investigate the behavior characteristics of asphalt components during the process of nano-cracks temperature self-healing(NTS),molecular simulation technology was used to simulate the temperature self-healing of asphalt.Based on the determination of asphalts(virgin asphalt and aged asphalt),the proportional changes of asphalt components were confirmed.The distribution characteristics of asphalt components were obtained by marking different components in the process of NTS.At the same time,the rationality of the micro simulation findings was confirmed by asphalt performance tests and infrared spectroscopy results.The results show that different asphalt components have different behavior characteristics in the process of NTS.The content of asphaltene and resin plays a key role in the process of NTS,while saturation and aromatics play an active role in the temperature self-healing before and after aging.The NTS is the result of the comprehensive action of different components,and the self-healing efficiency is proportional to the relative molecular mass.The effect of aging on the NTS is also realized by changing the proportion of asphalt components.

Self-Healing Liquid Metal Magnetic Hydrogels for Smart Feedback Sensors and High-Performance Electromagnetic Shielding

Hydrogels exhibit potential applications in smart wearable devices because of their exceptional sensitivity to various external stimuli.However,their applications are limited by challenges in terms of issues in biocompatibility,custom shape,and self-healing.Herein,a conductive,stretchable,adaptable,self-healing,and biocompatible liquid metal GaInSn/Ni-based composite hydrogel is developed by incorporating a magnetic liquid metal into the hydrogel framework through crosslinking polyvinyl alcohol(PVA)with sodium tetraborate.The excellent stretchability and fast self-healing capability of the PVA/liquid metal hydrogel are derived from its abundant hydrogen binding sites and liquid metal fusion.Significantly,owing to the magnetic constituent,the PVA/liquid metal hydrogel can be guided remotely using an external magnetic field to a specific position to repair the broken wires with no need for manual operation.The composite hydrogel also exhibits sensitive deformation responses and can be used as a strain sensor to monitor various body motions.Additionally,the multifunctional hydrogel displays absorption-dominated electromagnetic interference(EMI)shielding properties.The total shielding performance of the composite hydrogel increases to~62.5 dB from~31.8 dB of the pure PVA hydrogel at the thickness of 3.0 mm.The proposed bioinspired multifunctional magnetic hydrogel demonstrates substantial application potential in the field of intelligent wearable devices.

Intrinsic Self-Healing Chemistry for Next-Generation Flexible Energy Storage Devices

The booming wearable/portable electronic devices industry has stimulated the progress of supporting flexible energy storage devices.Excellent performance of flexible devices not only requires the component units of each device to maintain the original performance under external forces,but also demands the overall device to be flexible in response to external fields.However,flexible energy storage devices inevitably occur mechanical damages(extrusion,impact,vibration)/electrical damages(overcharge,over-discharge,external short circuit)during longterm complex deformation conditions,causing serious performance degradation and safety risks.Inspired by the healing phenomenon of nature,endowing energy storage devices with self-healing capability has become a promising strategy to effectively improve the durability and functionality of devices.Herein,this review systematically summarizes the latest progress in intrinsic self-healing chemistry for energy storage devices.Firstly,the main intrinsic self-healing mechanism is introduced.Then,the research situation of electrodes,electrolytes,artificial interface layers and integrated devices based on intrinsic self-healing and advanced characterization technology is reviewed.Finally,the current challenges and perspective are provided.We believe this critical review will contribute to the development of intrinsic self-healing chemistry in the flexible energy storage field.

Self-Healing MXene-and Graphene-Based Composites:Properties and Applications

Today,self-healing graphene-and MXene-based composites have attracted researchers due to the increase in durability as well as the cost reduction in long-time applications.Different studies have focused on designing novel self-healing graphene-and MXenebased composites with enhanced sensitivity,stretchability,and flexibility as well as improved electrical conductivity,healing efficacy,mechanical properties,and energy conversion efficacy.These composites with self-healing properties can be employed in the field of wearable sensors,supercapacitors,anticorrosive coatings,electromagnetic interference shielding,electronic-skin,soft robotics,etc.However,it appears that more explorations are still needed to achieve composites with excellent arbitrary shape adaptability,suitable adhesiveness,ideal durability,high stretchability,immediate self-healing responsibility,and outstanding electromagnetic features.Besides,optimizing reaction/synthesis conditions and finding suitable strategies for functionalization/modification are crucial aspects that should be comprehensively investigated.MXenes and graphene exhibited superior electrochemical properties with abundant surface terminations and great surface area,which are important to evolve biomedical and sensing applications.However,flexibility and stretchability are important criteria that need to be improved for their future applications.Herein,the most recent advancements pertaining to the applications and properties of self-healing graphene-and MXene-based composites are deliberated,focusing on crucial challenges and future perspectives.

“Smart”micro/nano container-based self-healing coatings on magnesium alloys:A review

Coating technologies are a commonly used way to protect metals against corrosion.However,with more and more severe service environments of materials,many protective coating systems often are not environmentally friendly or toxic as in the case of chromates.Based on the world’s abundant ideal magnesium(Mg)and its alloy,the smart self-healing anticorrosive coating can autonomously restore the damaged part of the coating according to the environmental changes,strengthen the corrosion protection ability,and prolong its service life.This paper reviews the research progress of smart self-healing coatings on Mg alloys.These coatings mostly contain suitable corrosion inhibitors encapsulated into micro/nano containers.Moreover,the different self-healing mechanisms and functionalities of micro/nano containers are discussed.The micro/nano containers range from inorganic nanocontainers such as mesoporous nanoparticles(silica(SiO_(2)),titanium dioxide(TiO_(2)),etc.),over inorganic clays(halloysite,hydrotalcite-like,zeolite),to organic nanocontainers such as polymer microcapsules,nanofibers,chitosan(CS)and cyclodextrin(CD),as well as,carbon materials such as graphene and carbon nanotubes and hybrids such as metal organic frameworks.The functioning of micro/nano containers can be divided in two principal groups:autonomous(based on defect filling and corrosion inhibition)and non-autonomous(based on dynamic bonds and shape memory polymers).Moreover,multi functionalities and composite applications of various micro/nano containers are summarized.At present,significant progress has been made in the preparation methods and technologies of micro/nano containers.Achieving long-term self-healing properties of coatings sensing of coating failure and early warning after self-healing function failure can be expected as the main development direction of self-healing corrosion protection coatings in the future.

Self-healing wearable self-powered deep ultraviolet photodetectors based on Ga_(2)O_(3)

Gallium oxide(Ga_(2)O_(3))based flexible heterojunction type deep ultraviolet(UV)photodetectors show excellent solar-blind photoelectric performance,even when not powered,which makes them ideal for use in intelligent wearable devices.How-ever,traditional flexible photodetectors are prone to damage during use due to poor toughness,which reduces the service life of these devices.Self-healing hydrogels have been demonstrated to have the ability to repair damage and their combination with Ga_(2)O_(3) could potentially improve the lifetime of the flexible photodetectors while maintaining their performance.Herein,a novel self-healing and self-powered flexible photodetector has been constructed onto the hydrogel substrate,which exhibits an excellent responsivity of 0.24 mA/W under 254 nm UV light at zero bias due to the built-in electric field originating from the PEDOT:PSS/Ga_(2)O_(3) heterojunction.The self-healing of the Ga_(2)O_(3) based photodetector was enabled by the reversible property of the synthesis of agarose and polyvinyl alcohol double network,which allows the photodetector to recover its original configu-ration and function after damage.After self-healing,the photocurrent of the photodetector decreases from 1.23 to 1.21μA,while the dark current rises from 0.95 to 0.97μA,with a barely unchanged of photoresponse speed.Such a remarkable recov-ery capability and the photodetector’s superior photoelectric performance not only significantly enhance a device lifespan but also present new possibilities to develop wearable and intelligent electronics in the future.

Self-healing of Cracks in Concrete with Various Crystalline Mineral Additives in Underground Environment

Cracks can deteriorate mechanical properties and/or durability of concrete. A few studies have shown that, cracks can autogenously heal under a certain conditions besides the traditional passive repair with a deliberate external intervention. For underground concrete structures, the presence of water, as a necessity for chemical reactions of the healing additives, is beneficial to healing concrete. In this paper, a natural healing method by mineral additives was developed according to the chemical and physical characteristics of underground environment. The healing capacity of three different crystalline mineral materials classified namely, carbonate, calcium sulphoaluminate expansive agent and natural metakaolin due to permeation- crystallization, expansion and pozzolanic reaction, has been assessed from the mechanical properties, referring to the relative elastic modulus, the strength restoration, and the water permeability of the healed specimens. In addition, the morphology of the healing products in the vicinity of the crack was observed. The results indicate that the specimens incorporated with the three mineral additives show different healing capacity according to the improved mechanical properties and permeability. The permeability of the host matrix decreased a lot after crack healing by natural metakaolin followed by carbonate whereas no noticeable improvement of water permeability has been observed for the specimens mixed with expansive agent. The specimens incorporated with carbonate show the best mechanical restoration in terms of relative elastic modulus and compressive strength. Although the dominate element is CaCO3 by reaction of CO32-, either from the dissolved CO2 or from the additives, and Ca2＋ in the cementitious system to fill the cracks, the healing capacity depends greatly on the morphology and the properties of the newly formed products.

Recent research progress in the mechanism and suppression of fusion welding-induced liquation cracking of nickel based superalloys

Nickel-based superalloys are extensively used in the crucial hot-section components of industrial gas turbines,aeronautics,and astronautics because of their excellent mechanical properties and corrosion resistance at high temperatures.Fusion welding serves as an effective means for joining and repairing these alloys;however,fusion welding-induced liquation cracking has been a challenging issue.This paper comprehensively reviewed recent liquation cracking,discussing the formation mechanisms,cracking criteria,and remedies.In recent investigations,regulating material composition,changing the preweld heat treatment of the base metal,optimizing the welding process parameters,and applying auxiliary control methods are effective strategies for mitigating cracks.To promote the application of nickel-based superalloys,further research on the combination impact of multiple elements on cracking prevention and specific quantitative criteria for liquation cracking is necessary.

Self-healing Action of Permeable Crystalline Coating on Pores and Cracks in Cement-based Materials

The self-healing action of a permeable crystalline coating on the po rous mortar was investigated by two times impermeability test. Moreover, the sel f-healing mechanism of cement-based materials with the permeable crystalline c oating was studied by SEM. The results indicate that the permeable crystalline c oating not only seals the pores and cracks in mortar during its curing process, but also heals the permeable pathway caused by first impermeability test or crac ks produced by freeze-thaw cycles. Therefore, cement-based materials can be im proved by the permeable crystalline coating for the self-healing function. SEM images prove that the self-healing function is realized by generating a great q uantity of non-soluble dendritic crystalline within the pores and cracks, which prevents the penetration of water and other liquids.

Exploring an eco-friendly approach to improve soil tensile behavior and cracking resistance

Soil tensile strength is a critical parameter governing the initiation and propagation of tensile cracking.This study proposes an eco-friendly approach to improve the tensile behavior and crack resistance of clayey soils.To validate the feasibility and efficacy of the proposed approach,direct tensile tests were employed to determine the tensile strength of the compacted soil with different W-OH treatment concentrations and water contents.Desiccation tests were also performed to evaluate the effectiveness of W-OH treatment in enhancing soil tensile cracking resistance.During this period,the effects of W-OH treatment concentration and water content on tensile properties,soil suction and microstructure were investigated.The tensile tests reveal that W-OH treatment has a significant impact on the tensile strength and failure mode of the soil,which not only effectively enhances the tensile strength and failure displacement,but also changes the brittle failure behavior into a more ductile quasi-brittle failure behavior.The suction measurements and mercury intrusion porosimetry(MIP)tests show that W-OH treatment can slightly reduce soil suction by affecting skeleton structure and increasing macropores.Combined with the microstructural analysis,it becomes evident that the significant improvement in soil tensile behavior through W-OH treatment is mainly attributed to the W-OH gel's ability to provide additional binding force for bridging and encapsulating the soil particles.Moreover,desiccation tests demonstrate that W-OH treatment can significantly reduce or even inhibit the formation of soil tensile cracking.With the increase of W-OH treatment concentration,the surface crack ratio and total crack length are significantly reduced.This study enhances a fundamental understanding of eco-polymer impacts on soil mechanical properties and provides valuable insight into their potential application for improving soil crack resistance.

Wide temperature range-and damage-tolerant microsupercapacitors from salt-tolerant, anti-freezing and self-healing organohydrogel via dynamic bonds modulation

The advance of microelectronics requires the micropower of microsupercapacitors(MSCs) to possess wide temperature-and damage-tolerance beyond high areal energy density.The properties of electrolyte are crucial for MSCs to meet the above requirements.Here,an organohydrogel electrolyte,featured with high salt tolerance,ultralow freezing point,and strong self-healing ability,is experimentally realized via modulating its inner dynamic bonds.Spectroscopic and theoretical analysis reveal that dimethyl sulfoxide has the ability to reconstruct Li^(+)solvation structure,and interact with free water and polyvinyl alcohol chains via forming hydrogen bonds.The organohydrogel electrolyte is employed to build MSCs,which show a boosted energy density,promising wide temperature range-and damage-tolerant ability.These attractive features make the designed organohydrogel electrolyte have great potential to advance MSCs.