Critical crack tip opening displacement of different strength concrete

Critical crack tip opening displacement (CTODc) of concrete using experimental and analytical evaluation with seven different compressive strengths ranging from 30 up to 150 MPa was studied based on two types of fracture tests:three-point bending (TPB) and wedge splitting (WS).In the tests,the values of CTODc were experimentally recorded using a novel technique,in which fiber Bragg grating (FBG) sensors were used,and two traditional techniques,in which strain gauges and clip gauges were deployed.The values of CTODc of tested concrete were also predicted using two existing analytical formulae proposed by JENQ & SHAH and XU,respectively.It is found that the values of CTODc obtained by both experimental measurements and analytical formulae exhibit a negligible variation as the compressive strength of concrete increases,and the test geometry adopted has little impact on the value of CTODc.Regarding the experimental measurement of CTODc,the clip gauge method generally leads to a larger value of CTODc and shows a more significant scatter as compared with the other two methods,while the strain gauge method leads to a slightly lower CTODc as compared with the FBG sensor method.The analytical formula proposed by JENQ and SHAH is found to generally lead to an overestimation,while the analytical formula proposed by XU shows a good accuracy.

THE ANALYSES OF THE THREE-DIMENSIONAL STRESS STRUCTURE NEAR THE CRACK TIP OF MODE I CT SPECIMENS IN ELASTICPLASTIC STATE(Ⅰ)--THE ANALYSES OF CONSTRAINT PARAMETERS AND FRACTURE PARAMETERS

In the present paper,three dimensional analyses of some general constraint parameters and fracture parameters near the crack tip of Mode I CT specimens in two different thicknesses are carried out by employing ADINA program.The results reveal that the constraints along the thickness direction are obviously separated into two parts:the keeping similar high constraint field(Z_(1))and rapid reducing constraints one(Z_(2)).The two fields are experimentally confiremed to correspond to the smooth region and the shear lip on the fracture face respectively.So the three dimensional stress structure of Mode I specimens can be derived through discussing the two fields respectively.The distribution of the Crack Tip Opening Displacement(CTOD)along the thickness direction and the three dimensional distribution of the void growth ratio(V_(g))near the crack tip are also obtained.The two fracture parameters are in similar trends along the thickness direction,and both of them can reflect the effect of thickness and that of the loading level to a certain degree.

Engineering critical assessment on welding flaws of the X65 UOE girth weld based on CRACKWISE

Focused on the girth weld of a φ762 x 28.6 mm （X65） offshore UOE pipe, the fracture toughness properties at different weld joint positions were tested. Meanwhile,the largest size of different cracks under service condition was calculated by using CRACKWISE. The service life of the UOE pipe with postulated crack-like flaws was calculated by considering various fatigue factors, such as vibrations caused by ocean current and fluctuations of inner pressure. The assessment process and results can be used to direct the repair of weld flaws laid in pipes or to assess the reliability of in-serving pipes.

APPLICATION OF SINTAP TO THE SAFETY ASSESSMENT OF X65 PIPELINE STEEL

The recently developed European flaw assessment procedure, structural integrity assessment procedure（SiNTAP） is applied to assessment for welded joints of the API 5L X65 pipeline steel with an assumed embedded flaw and surface flaw at the weld toe. As one of the basic input data, fracture toughness crack tip opening displacement （CTOD） tests are conducted at 0℃ and performed according to the requirements of the standard of BS7448. For the heat affected zone （HAZ） specimens, the microstructure observation is performed to insure that the tip of the crack is located in the coarse grain zone. The result explains the dispersity of the test values. In structural integrity assessment procedure-fracture assessment diagram（SINTAP FAD） method, the failure curves of welded joints at level 1 and 3 are derived from the tensile test results. The results of the assessment show that all assessment points are located within the failure lines of analysis level 1 and 3. So the welded joint of the pipeline is safe. This study laid the foundation of application of SINTAP to pipeline structure assessment.