Hot tearing is one of the most serious defects during the casting solidification process.In this study,a new type of multichannel"cross"hot tearing device was designed.The hot cracks initiation and propagati...Hot tearing is one of the most serious defects during the casting solidification process.In this study,a new type of multichannel"cross"hot tearing device was designed.The hot cracks initiation and propagation were predicted by the relationship between temperature,shrinkage force and solidification time during the casting solidification process.The reliability and practicability of the multichannel"cross"hot tearing device were verified by casting experiments and numerical simulations.The theoretical calculation based on Clyne-Davies model and numerical simulation results show that the hot tearing tendency decreases in the order:2024 Al alloy>Al-Cu alloy>Al-Si alloy at a pouring temperature of 670°C and a mold temperature of 25°C.Feeding of liquid films at the end of solidification plays an important role in the propagation process of hot tearing.The decrease of hot tearing tendency is attributed to the feeding of liquid film and intergranular bridging.展开更多
基金This work was financially supported by the National Natural Science Foundation of China(Grant No.51875365).
文摘Hot tearing is one of the most serious defects during the casting solidification process.In this study,a new type of multichannel"cross"hot tearing device was designed.The hot cracks initiation and propagation were predicted by the relationship between temperature,shrinkage force and solidification time during the casting solidification process.The reliability and practicability of the multichannel"cross"hot tearing device were verified by casting experiments and numerical simulations.The theoretical calculation based on Clyne-Davies model and numerical simulation results show that the hot tearing tendency decreases in the order:2024 Al alloy>Al-Cu alloy>Al-Si alloy at a pouring temperature of 670°C and a mold temperature of 25°C.Feeding of liquid films at the end of solidification plays an important role in the propagation process of hot tearing.The decrease of hot tearing tendency is attributed to the feeding of liquid film and intergranular bridging.