A highly crosslinked, monodispersed polystyrene（PS） particle was prepared by a seeded batch dispersion polymerization with a monomer absorption method. Prior to polymerization, 1,9 lam monodispersed PS seed particle...A highly crosslinked, monodispersed polystyrene（PS） particle was prepared by a seeded batch dispersion polymerization with a monomer absorption method. Prior to polymerization, 1,9 lam monodispersed PS seed particles were treated under an optimum condition of monomer absorption. The effects of divinylbenzebe（DVB） concentration and polymerization temperature were examined for styrene（in PS seed）/styrene（in the second stage） mass ratio of 1：1 in the medium range of EtOH/water mass ratio of 100/0-80/20 and 2.3 μm uniform crosslinked PS particles containing 15%-20% （mass fraction） DVB were prepared at 60-70 ℃. The results show that monomer absorption before the second stage of polymerization is more effective to prepare highly crosslinked monodispersed PS particles.展开更多
Monodisperse crosslinked polystyrene （CPS） particles were prepared through the normal emulsion polymerization method by adding crosslinker--divinylbenzene （DVB） into the reaction system after polystyrene （PS） pa...Monodisperse crosslinked polystyrene （CPS） particles were prepared through the normal emulsion polymerization method by adding crosslinker--divinylbenzene （DVB） into the reaction system after polystyrene （PS） particles grew to -80% of the final size. When the amount of crosslinker DVB added was less than 6.17 wt% based on styrene, the prepared CPS particles were spherical and uniform and the size of the CPS particles could be predicted through the normal emulsion method. The glass transition temperature （Tg） of the prepared CPS particles was higher than that of un-crosslinked PS particles and, the more crosslinker that was added, the higher the Tg of CPS Particles. The prepared CPS particles had strong resistance to organic solvents.展开更多
基金the second stage of BK21 program for supporting a fellowship
文摘A highly crosslinked, monodispersed polystyrene（PS） particle was prepared by a seeded batch dispersion polymerization with a monomer absorption method. Prior to polymerization, 1,9 lam monodispersed PS seed particles were treated under an optimum condition of monomer absorption. The effects of divinylbenzebe（DVB） concentration and polymerization temperature were examined for styrene（in PS seed）/styrene（in the second stage） mass ratio of 1：1 in the medium range of EtOH/water mass ratio of 100/0-80/20 and 2.3 μm uniform crosslinked PS particles containing 15%-20% （mass fraction） DVB were prepared at 60-70 ℃. The results show that monomer absorption before the second stage of polymerization is more effective to prepare highly crosslinked monodispersed PS particles.
基金National Basic Research Program of China(Grant No:2006CB932601)the Scientific Research Foundation for Returned Overseas Chinese Scholar,Ministry of Education
文摘Monodisperse crosslinked polystyrene （CPS） particles were prepared through the normal emulsion polymerization method by adding crosslinker--divinylbenzene （DVB） into the reaction system after polystyrene （PS） particles grew to -80% of the final size. When the amount of crosslinker DVB added was less than 6.17 wt% based on styrene, the prepared CPS particles were spherical and uniform and the size of the CPS particles could be predicted through the normal emulsion method. The glass transition temperature （Tg） of the prepared CPS particles was higher than that of un-crosslinked PS particles and, the more crosslinker that was added, the higher the Tg of CPS Particles. The prepared CPS particles had strong resistance to organic solvents.