Cruciform joints in ships are prone to fatigue damage and the determination of type of weld plays a significant role in thefatigue design of the joint. In this paper, the effect of weld geometry on fatigue failure of ...Cruciform joints in ships are prone to fatigue damage and the determination of type of weld plays a significant role in thefatigue design of the joint. In this paper, the effect of weld geometry on fatigue failure of load carrying cruciform joints inships is investigated using Effective Notch Stress (ENS) approach. A fictitious notch of 1 mm radius is introduced at theweld root and toe and fatigue stress is evaluated. The effect of weld leg length (l) and weld penetration depth (p) on ENS atweld root and toe are determined. The critical weld leg length (lcr) at which fatigue failure transitions from weld root toweld toe is investigated. An approximation formula for determination of the critical weld leg length considering weldpenetration depth (p) is proposed.展开更多
Surface impact treatment was carried out on the cruciform joint weldment of 16MnR steel by using the HJ-II-type ultrasonic impact machine.The ultrasonic impact current is 1.2 A,the impact amplitude is 30?m and ultraso...Surface impact treatment was carried out on the cruciform joint weldment of 16MnR steel by using the HJ-II-type ultrasonic impact machine.The ultrasonic impact current is 1.2 A,the impact amplitude is 30?m and ultrasonic impacting time is 30 and 60 min,respectively.Fatigue experiments were carried out for both treated specimen and un-treated specimen by using EHF-EM200K2-070-1A fatigue testing machine.The fatigue fractures were observed with the scanning electron microscope of 6360LA type and the microstructure of ultrasonic impact treating surface layer was analyzed by using high resolution transmission electron microscope of JEM-2100 type.The experimental results show that the microstructure of ultrasonic impact surface layer has been successfully nanocrystallized.The fatigue life of welded cruciform joints of 16MnR steel can be significantly improved through the ultrasonic impact treatment.The main reasons are that the ultrasonic impact treating can reduces the stress concentration in the weld toe,decrease the tensile stress,and even change to compressive stress in the weldment,the grain size in the welded joint can be refined.The longer the impact time,the greater increasing range of fatigue life will be.Compared to the sample without treatment,its fatigue life was increased 210.37%,362.48%,respectively,when the impact time was 30,60 min,respectively.展开更多
Empirical relationship was developed to predict the fatigue life of gas metal arc welded （GMAW） cruciform joints failing from root region. High strength, age hardenable aluminium alloy of AA7075-T6 grade was used as...Empirical relationship was developed to predict the fatigue life of gas metal arc welded （GMAW） cruciform joints failing from root region. High strength, age hardenable aluminium alloy of AA7075-T6 grade was used as the base material. The design of experiments concept was used to optimize the required number of fatigue testing experiments. Fatigue experiment was conducted in a servo hydraulic controlled fatigue testing machine under constant amplitude loading. The empirical relationship was developed. By using the developed empirical relationship, the fatigue life of GMAW cruciform joints failing from root region was predicted at 95% confidence level. The effect of cruciform joint dimensions on fatigue life was discussed in detail.展开更多
文摘Cruciform joints in ships are prone to fatigue damage and the determination of type of weld plays a significant role in thefatigue design of the joint. In this paper, the effect of weld geometry on fatigue failure of load carrying cruciform joints inships is investigated using Effective Notch Stress (ENS) approach. A fictitious notch of 1 mm radius is introduced at theweld root and toe and fatigue stress is evaluated. The effect of weld leg length (l) and weld penetration depth (p) on ENS atweld root and toe are determined. The critical weld leg length (lcr) at which fatigue failure transitions from weld root toweld toe is investigated. An approximation formula for determination of the critical weld leg length considering weldpenetration depth (p) is proposed.
基金National Natural Science Foundations of China(51065010)Science Foundations of Jiangxi(2009GZC0016)
文摘Surface impact treatment was carried out on the cruciform joint weldment of 16MnR steel by using the HJ-II-type ultrasonic impact machine.The ultrasonic impact current is 1.2 A,the impact amplitude is 30?m and ultrasonic impacting time is 30 and 60 min,respectively.Fatigue experiments were carried out for both treated specimen and un-treated specimen by using EHF-EM200K2-070-1A fatigue testing machine.The fatigue fractures were observed with the scanning electron microscope of 6360LA type and the microstructure of ultrasonic impact treating surface layer was analyzed by using high resolution transmission electron microscope of JEM-2100 type.The experimental results show that the microstructure of ultrasonic impact surface layer has been successfully nanocrystallized.The fatigue life of welded cruciform joints of 16MnR steel can be significantly improved through the ultrasonic impact treatment.The main reasons are that the ultrasonic impact treating can reduces the stress concentration in the weld toe,decrease the tensile stress,and even change to compressive stress in the weldment,the grain size in the welded joint can be refined.The longer the impact time,the greater increasing range of fatigue life will be.Compared to the sample without treatment,its fatigue life was increased 210.37%,362.48%,respectively,when the impact time was 30,60 min,respectively.
文摘Empirical relationship was developed to predict the fatigue life of gas metal arc welded （GMAW） cruciform joints failing from root region. High strength, age hardenable aluminium alloy of AA7075-T6 grade was used as the base material. The design of experiments concept was used to optimize the required number of fatigue testing experiments. Fatigue experiment was conducted in a servo hydraulic controlled fatigue testing machine under constant amplitude loading. The empirical relationship was developed. By using the developed empirical relationship, the fatigue life of GMAW cruciform joints failing from root region was predicted at 95% confidence level. The effect of cruciform joint dimensions on fatigue life was discussed in detail.
基金Supported by National Natural Science Foundation of China(Grant No.51479153)the Fundamental Research Funds for the Central Universities(No.2013-JL-007)