Microscopic and Dynamic Rheological Characteristics of Crumb Rubber Modified Asphalt

A test for crumb rubber modified asphalt containing 20% crumb rubber particles（30 mesh） was performed using a scanning electron microscope（SEM）.The experimental results indicate that the crumb rubber particles are evenly distributed in the asphalt.Shear rate sweep and shear-temperature sweep tests on the crumb rubber modified asphalt at-20-80 ℃ using a dynamic shear rheology（DSR） instrument,were carried out.The tests show that the complex modulus decreases with increasing temperature;at equivalent temperature,higher load frequencies lead to a larger complex modulus,and this value increasingly decreases as the temperature increases;the phase angle increases with temperature and decreases as the load frequency increases.It can be concluded that the rutting resistance limiting temperature of crumb rubber modified asphalt is 78 ℃,and the anti-fatigue limiting temperature is 16 ℃,which shows that the asphalt has preferable rutting resistance characteristics at high temperature,as well as anti-fatigue characteristics.In addition,the complex modulus master curve at different temperatures was plotted according to the time temperature equivalence principle,which allows the study of the dynamic state behavior of crumb rubber modified asphalt at a wide range of load frequency.

Creep Characteristics of Crumb Rubber Modified Asphalt Binder

Crumb rubber modified asphalt containing 20 percent crumb rubber particles of 30 mesh has been examined by Scanning Electron Microscope （SEM） to observe the microcosmic appearance and the characteristic distribution of crumb rubber particles in asphalt. The SEM pictures reveal that the crumb rubber particles distribute evenly in the asphalt and they are compatible well with asphalt. The shear creep test of crumb rubber modified asphalt was carried out at -10 ℃ and 40 ℃ by Dynamic Shear Rheology （DSR）. The shearing deformation at different temperature and creep stiffness modulus curve at loading stage of crumb rubber modified asphalt have been measured. The stiffness modulus of crumb rubber modified asphalt is much temperature sensitive and it decays much quick at the early stage of loading than normal asphalt. The rate of decay of stiffness modulus is slow at the subsequent stage and stiffness modulus approaches to a stable value at the final stage at a higher temperature. In addition, Burgers model is suitable to describe and simulate experimental results of viscoelastic properties of the crumb rubber modified asphalt.

Laboratory investigation on effects of organic montmorillonite on performance of crumb rubber modified asphalt

In this paper,organic montmorillonite(OMMT)was added into crumb rubber modified asphalt(CRMA)to improve its high temperature performance,anti-aging performance and storage stability.The effects of different OMMT content on properties of CRMA were studied.The rutting factor obtained by dynamic shear rheological(DSR)test was adopted to evaluate the high-temperature performance.The creep stiffness and m value determined by the bending beam rheometer(BBR)test were employed to evaluate the low-temperature performance.The softening point,ductility,rutting factor before and after rolling thin film ovens test(RTFOT)and pressure aging vessel test(PAV)were compared to characterize the aging properties.Moreover,the segregation test after being reserved for 48 h and 7 d was conducted,and the softening point and rutting factor of upper and lower layers of segregation pipe were adopted to evaluate the storage stability.The results indicated that the high-temperature performance and anti-aging performance were developed with the increasing content of OMMT,while the low-temperature performance deteriorated.The storage stability was improved with the increasing content of OMMT before the content exceeded 4%,after which the storage stability declined.Taking account of all factors,it is suggested that the optimum content of OMMT is 3%−4%.

The Viscosity-reducing Mechanism of Organic Wax Additive on CRMA

CRMA was prepared by mixing PG 64-22 asphalt with crumb rubber powder of 40 mesh size and 18% by weight of the asphalt. Sasobit, a typical organic wax additive, was selected and added into CRMA. A series of tests, namely, brookfield viscosity, environmental scanning electron microscope（ESEM）, component test, differential scanning calorimeter（DSC）, fourier transform infrared spectroscopy （FTIR） and nuclear magnetic resonance （NMR） were conducted on CRMA with and without organic wax additive, and microcosmic appearance, component content and molecular structure of various asphalt binders were obtained. The test results indicate that the addition of Sasobit~ into CRMA can effectively change the contents of components： the content of asphaltenes increases relatively, while saturates decreases. In addition, the interaction between various components of CRMA is weakened, and the state of equilibrium between the dispersant and dispersed phase is changed at the same time. That is why the viscosity decreases after the organic wax additive is added into CRMA.