The phase transition of two kinds of solvent-induced crystalline syndiotactic polystyrene (sPS). gamma-sPS and delta(c)-sPS, has been studied via WAXD and DSC. gamma-sPS transform to a-sPS at 195-225 degrees C before ...The phase transition of two kinds of solvent-induced crystalline syndiotactic polystyrene (sPS). gamma-sPS and delta(c)-sPS, has been studied via WAXD and DSC. gamma-sPS transform to a-sPS at 195-225 degrees C before melt during heating, whereas delta(e)-sPS transform to first gamma-sPS and then a-sPS at 100-200 degrees C and 200-215 degrees C, respectively. The transition of delta(e)-gamma and gamma-a occurs for below melting point of sPS indicates they are all solid-solid transition.展开更多
Syndiotactic polypropylene （sPP） as-spun fiber （sPP1） and drawn fiber （sPP2） were prepared by melt-spinning and melt-spinning/hot-drawing, respectively. The structure transition of the two fibers induced by anne...Syndiotactic polypropylene （sPP） as-spun fiber （sPP1） and drawn fiber （sPP2） were prepared by melt-spinning and melt-spinning/hot-drawing, respectively. The structure transition of the two fibers induced by annealing at different temperatures and the corresponding mechanical properties were subsequently investigated by the combination of Fourier transform infrared spectroscopy （FTIR）, wide-angle X-ray diffraction （WAXD） and tensile testing. The results indicate that the chain conformation and crystal forms of the two sPP fibers are not obviously changed at low annealing temperature （40℃）. With increasing the annealing temperature, the trans-planar conformation and mesophase in sPP1 and sPP2 fibers can be completely transformed to helical conformation and crystal form I under tension. Upon removing the tension, a small amount of mesophase and trans-planar conformation will be regained. The mechanical properties of the annealed fibers are manifestly dependent on their initial structure and the annealing temperature.展开更多
基金the open laboratory funds of Chinese Academy of Sciences.
文摘The phase transition of two kinds of solvent-induced crystalline syndiotactic polystyrene (sPS). gamma-sPS and delta(c)-sPS, has been studied via WAXD and DSC. gamma-sPS transform to a-sPS at 195-225 degrees C before melt during heating, whereas delta(e)-sPS transform to first gamma-sPS and then a-sPS at 100-200 degrees C and 200-215 degrees C, respectively. The transition of delta(e)-gamma and gamma-a occurs for below melting point of sPS indicates they are all solid-solid transition.
基金supported by the National Natural Science Foundation of China(No.50603029)the Innovation Foundation of Center for Molecular Science,Chinese Academy of Sciences(CMS-Y200724)
文摘Syndiotactic polypropylene （sPP） as-spun fiber （sPP1） and drawn fiber （sPP2） were prepared by melt-spinning and melt-spinning/hot-drawing, respectively. The structure transition of the two fibers induced by annealing at different temperatures and the corresponding mechanical properties were subsequently investigated by the combination of Fourier transform infrared spectroscopy （FTIR）, wide-angle X-ray diffraction （WAXD） and tensile testing. The results indicate that the chain conformation and crystal forms of the two sPP fibers are not obviously changed at low annealing temperature （40℃）. With increasing the annealing temperature, the trans-planar conformation and mesophase in sPP1 and sPP2 fibers can be completely transformed to helical conformation and crystal form I under tension. Upon removing the tension, a small amount of mesophase and trans-planar conformation will be regained. The mechanical properties of the annealed fibers are manifestly dependent on their initial structure and the annealing temperature.