In this work,an alternative alkali-activated cement(AAC)made of ladle slag precursor mixed with sodium hydroxide and sodium silicate has been developed to enhance the bearing capacity of estuarine soils in coastal con...In this work,an alternative alkali-activated cement(AAC)made of ladle slag precursor mixed with sodium hydroxide and sodium silicate has been developed to enhance the bearing capacity of estuarine soils in coastal conditions via deep soil mixing(DSM).The AAC was optimized to use a low reactivity precursor(ladle slag)and to deal with a contaminated high-water content natural sediment cured under water.The material performance was analysed by comparison to a mixture made with Portland cement and cured in the same conditions.Flexural and unconfined compressive strength tests as well as seismic waves measurements after 3-,7-,14-and 28-d curing were performed to obtain a relationship between elastic stiffness and strength with curing time for both mixtures.Remarkably,the AAC mix demonstrated superior strength results,exhibiting almost double flexural and compressive strengths after 28 d compared to the Portland cement mix.The AAC mix also showed a higher rate of stiffness increase than the Portland cement mix,which has a higher initial stiffness at young ages but lower stiffness evolution.Leachate analysis confirmed that the proposed AAC could effectively immobilise any contaminants from soil or precursors.The effect of curing under stress was analysed in triaxial compression tests and found to be insignificant,indicating that laboratory data obtained without stress curing can represent the material's behaviour in a DSM column,which will cure under the weight of the column.展开更多
The reactive diluent prepared by siloxane modified Trimethylene oxide can improve the performance of the UV curing system.Therefore,1,7-bis[(3-ethyl-3-methoxyoxacylobutane)propyl]octadecylosiloxane(BEMOPOMTS)was synth...The reactive diluent prepared by siloxane modified Trimethylene oxide can improve the performance of the UV curing system.Therefore,1,7-bis[(3-ethyl-3-methoxyoxacylobutane)propyl]octadecylosiloxane(BEMOPOMTS)was synthesized from diethyl carbonate,trimethylopropanes,allyl bromide,and 1,1,3,3,5,5,7,7-octadecylosiloxane as the main raw materials.BEMOPOMTS can be used as reactive diluents in the field of cationic UV curing.It has good thermal stability,and the addition of BEMOPOMTS significantly improves the tensile strength and elongation at break of epoxy resin.Compared with the pure epoxy resin,adding 20%BEMOPOMTS increased the elastic modulus by 25%to 677 MPa.展开更多
The strength development law of γ-type dicalcium silicate (γ-C_(2)S) under different carbonation processes was investigated,and the carbonation mechanism of γ-C_(2)S under the action of NH_(4)HCO_(3) was clarified ...The strength development law of γ-type dicalcium silicate (γ-C_(2)S) under different carbonation processes was investigated,and the carbonation mechanism of γ-C_(2)S under the action of NH_(4)HCO_(3) was clarified by using a wide range of test methods,including XRD and SEM.A method of saturated NH_(4)HCO_(3) solution as a curing agent was identified to improve the carbonation efficiency and enhance the carbonation degree of γ-C_(2)S,and then a high-strength carbonated specimen was obtained.Microhardness analysis and SEM morphology analysis were conducted on the carbonised specimens obtained under atmospheric pressure carbonisation conditions using the curing agent.It was found that γ-C_(2)S could perform carbonisation well under atmospheric pressure,which promoted the carbonisation efficiency and decreased the carbonisation cost simultaneously.Therefore,a new carbonisation process solution was proposed for the rapid carbonisation of γ-C_(2)S.展开更多
Sustained casing pressure(SCP)is a crucial issue in the oil and gas production lifecycle.Epoxy resins,exhibiting exceptional compressive strength,ductility,and shear bonding strength,have the potential to form reliabl...Sustained casing pressure(SCP)is a crucial issue in the oil and gas production lifecycle.Epoxy resins,exhibiting exceptional compressive strength,ductility,and shear bonding strength,have the potential to form reliable barriers.The injectivity and sealing capacity of the epoxy resin is crucial parameters for the success of shallow remediation operations.This study aimed to develop and assess a novel solid-free resin sealant as an alternative to Portland cement for mitigating fluid leakage.The investigation evaluated the viscosity,compressive strength,and brittleness index of the epoxy resin sealant,as well as its tangential and normal shear strengths in conjunction with casing steel.The flow characteristics and sealing abilities of conventional cement and epoxy resin were comparatively analyzed in cracks.The results showed that the application of a viscosity reducer facilitated control over the curing time of the epoxy resin,ranging from 1.5 to 6 h,and reduced the initial viscosity from 865.53 to 118.71 m Pa,s.The mechanical properties of the epoxy resin initially increased with a rise in curing agent content before experiencing a minor decrease.The epoxy resin containing 30%curing agent exhibited optimal mechanical properties.After a 14-day curing period,the epoxy resin's compressive strength reached81.37 MPa,2.12 times higher than that of cement,whereas the elastic modulus of cement was 2.99 times greater than that of the epoxy resin.The brittleness index of epoxy resin is only 3.42,demonstrating high flexibility and toughness.The tangential and normal shear strengths of the epoxy resin exceeded those of cement by 3.17 and 2.82 times,respectively.In a 0.5 mm-wide crack,the injection pressure of the epoxy resin remained below 0.075 MPa,indicating superior injection and flow capabilities.Conversely,the injection pressure of cement surged dramatically to 2.61 MPa within 5 min.The breakthrough pressure of0.5 PV epoxy resin reached 7.53 MPa,decreasing the crack's permeability to 0.02 D,a mere 9.49%of the permeability observed following cement plugging.Upon sealing a 2 mm-wide crack using epoxy resin,the maximum breakthrough pressure attained 5.47 MPa,3.48 times of cement.These results suggest that epoxy resin sealant can be employed safely and effectively to seal cracks in the cement.展开更多
Internal curing agents (ICA) based on super absorbent polymer have poor alkali tolerance and reduce the early strength of concrete.An alkali tolerate internal curing agent (CAA-ICA) was designed and prepared by using ...Internal curing agents (ICA) based on super absorbent polymer have poor alkali tolerance and reduce the early strength of concrete.An alkali tolerate internal curing agent (CAA-ICA) was designed and prepared by using sodium carboxymethyl starch (CMS) with high hydrophilicity,acrylic acid (AA) containing anionic carboxylic group and acrylamide (AM) containing non-ionic amide group as the main raw materials.The results show that the ratio of CAA-ICA alkali absorption solution is higher than that existing ICA,which solves the low water absorption ratio of the ICA in alkali environment.The water absorption ratio of CAA-ICA in saturated Ca(OH)_(2) solution is 95.8 g·g^(-1),and the alkali tolerance coefficient is 3.4.The application of CAA-ICA in cement-based materials can increase the internal relative humidity and miniaturize the pore structure.The compressive strength of mortar increases up to 12.95%at 28 d,which provids a solution to overcome the reduction of the early strength.展开更多
To promote the production and application of artificial aggregates,save natural sand resources and protect the ecological environment,we evaluated the feasibility of using spherical porous functional aggregates(SPFAs)...To promote the production and application of artificial aggregates,save natural sand resources and protect the ecological environment,we evaluated the feasibility of using spherical porous functional aggregates(SPFAs) formed by basalt saw mud under autoclave curing in ordinary structural concrete.In our work,two types of prewetted functional aggregates were taken as replacements for natural aggregates with different volume substitution rates(0%,5%,10%,15%,20%,25%,and 30%) in the preparation of ordinary structural concrete with water-to-binder ratios(W/B) of 0.48 and 0.33.The effects of the functional aggregate properties and content,W/B,and curing age on the fluidity,density,mechanical properties and autogenous shrinkage of ordinary concrete were analyzed.The experimental results showed that the density of concrete declined at a rate of not more than 5%,and the 28 d compressive strength could reach 31.0-68.2 MPa.Low W/B,long curing age and high-quality functional aggregates were conducive to enhancing the mechanical properties of SPFAs concrete.Through the rolling effects,SPFAs can optimize the particle gradation of aggregate systems and improve the fluidity of concrete,and the water stored inside SPFAs provides an internal curing effect,which prolongs the cement hydration process and considerably reduces the autogenous shrinkage of concrete.SPFAs exhibits high strength and high density,as well as being more cost-effective and ecological,and is expected to be widely employed in ordinary structural concrete.展开更多
Plain concrete is strong in compression but brittle in tension,having a low tensile strain capacity that can significantly degrade the long-term performance of concrete structures,even when steel reinforcing is presen...Plain concrete is strong in compression but brittle in tension,having a low tensile strain capacity that can significantly degrade the long-term performance of concrete structures,even when steel reinforcing is present.In order to address these challenges,short polymer fibers are randomly dispersed in a cement-based matrix to forma highly ductile engineered cementitious composite(ECC).Thismaterial exhibits high ductility under tensile forces,with its tensile strain being several hundred times greater than conventional concrete.Since concrete is inherently weak in tension,the tensile strain capacity(TSC)has become one of the most extensively researched properties.As a result,developing a model to predict the TSC of the ECC and to optimize the mixture proportions becomes challenging.Meanwhile,the effort required for laboratory trial batches to determine the TSC is reduced.To achieve the research objectives,five distinct models,artificial neural network(ANN),nonlinear model(NLR),linear relationship model(LR),multi-logistic model(MLR),and M5P-tree model(M5P),are investigated and employed to predict the TSCof ECCmixtures containing fly ash.Data from115 mixtures are gathered and analyzed to develop a new model.The input variables include mixture proportions,fiber length and diameter,and the time required for curing the various mixtures.The model’s effectiveness is evaluated and verified based on statistical parameters such as R2,mean absolute error(MAE),scatter index(SI),root mean squared error(RMSE),and objective function(OBJ)value.Consequently,the ANN model outperforms the others in predicting the TSC of the ECC,with RMSE,MAE,OBJ,SI,and R2 values of 0.42%,0.3%,0.33%,0.135%,and 0.98,respectively.展开更多
[Objectives]This study was conducted to compare the effects of different curing processes on the characteristics of marinated beef.[Methods]Marinated beef was obtained by two curing processes:static curing and injecti...[Objectives]This study was conducted to compare the effects of different curing processes on the characteristics of marinated beef.[Methods]Marinated beef was obtained by two curing processes:static curing and injection and vacuum tumbling curing.The effects of the two curing processes on the production rate,curing absorption rate,water content,soluble protein content,amino acid nitrogen content,texture characteristics and microstructure of the product were compared.[Results]Compared with static curing,the production rate of marinated beef increased by 10%,the curing absorption rate increased by 28%,the texture and microstructure were improved,and the water content increased,while the soluble protein content decreased.As a result,the sensory score was higher.There was no significant difference in the content of amino acid nitrogen,but it decreased compared with raw meat.To sum up,injection and vacuum tumbling curing is more conducive to the processing of marinated beef.[Conclusions]This study provides a theoretical basis for the industrial production of marinated beef,and lays a foundation for in-depth exploration of injection and vacuum tumbling curing technique of marinated beef.展开更多
By using HDI and TMP as the main raw materials,polyethylene glycol 400(PEG400)is used as a non-ionic hydrophilic modifier,and sodium hydroxyethyl sulfonate is used as an ionic hydrophilic modifier to synthesize a dual...By using HDI and TMP as the main raw materials,polyethylene glycol 400(PEG400)is used as a non-ionic hydrophilic modifier,and sodium hydroxyethyl sulfonate is used as an ionic hydrophilic modifier to synthesize a dual hydrophilic modified polyurethane curing agent.Research revealed that introducing PEG400 for hydrophilic chain segments and sodium hydroxyethyl sulfonate for hydrophilic ionic groups in the polyurethane curing agent component leads to a uniform distribution of hydrophilic components,significantly enhancing compatibility with the aqueous polyol component,and results in excellent film performance.The synthesis process and film were characterized using Fourier transform infrared spectroscopy and high-resolution scanning electron microscopy in the study.展开更多
National food security is the backbone of any economy,and achieving food security is essential for the prosperity of a nation.During my study in China at the Institute of South-South Cooperation and Development,Peking...National food security is the backbone of any economy,and achieving food security is essential for the prosperity of a nation.During my study in China at the Institute of South-South Cooperation and Development,Peking University,from September 2022 to July 2023,I leant how China has managed to achieve food security despite its large population of around 1.4 billion and numerous other challenges by means of strategic planning,e"ective policy execution,technological advancement and global collaboration.展开更多
Some people,mainly in the West,were taken by surprise when six Chinese warships were seen near the Red Sea in October 2023 amid the conflict in Gaza.Some Western media and politicians tried to frame China’s mission a...Some people,mainly in the West,were taken by surprise when six Chinese warships were seen near the Red Sea in October 2023 amid the conflict in Gaza.Some Western media and politicians tried to frame China’s mission as an escalatory move in the Middle East.展开更多
This paper examines the application of polyurethane curing technology in the construction of railway track beds,with a specific focus on its implementation in China’s rapidly developing railway infrastructure.The stu...This paper examines the application of polyurethane curing technology in the construction of railway track beds,with a specific focus on its implementation in China’s rapidly developing railway infrastructure.The study begins by identifying the limitations of traditional ballasted track beds,especially under the demands of high-speed and heavyload railways.It then methodically analyzes the advantages of polyurethane-cured track beds,highlighting their improved mechanical properties,including enhanced stability and durability.The paper further explores the benefits of transitioning to prefabricated polyurethane track beds,emphasizing significant cost reductions,better construction quality,and enhanced maintainability.Through a detailed review of experimental data and practical applications,the paper demonstrates the efficacy of polyurethane track beds in various railway settings.A critical part of the research involves optimizing the structural parameters of polyurethane track beds to achieve the best balance of mechanical and damping properties.The conclusion of the paper underscores the potential of polyurethane curing technology as a transformative approach to railway track bed construction,offering a solution to the challenges posed by traditional methods and aligning with the evolving needs of modern railways.展开更多
The mesoscale fiber-matrix interfacial transition zone(FM-ITZ) under induced curing pressure plays a key role in the effectiveness of fiber reinforcement and the engineering application of fiber-reinforced cementitiou...The mesoscale fiber-matrix interfacial transition zone(FM-ITZ) under induced curing pressure plays a key role in the effectiveness of fiber reinforcement and the engineering application of fiber-reinforced cementitious composites(FRCCs). This critical review establishes the link among induced curing pressure(i.e., external loading condition), multiphysics processes(i.e., internal governing mechanism), and interface behavior(i.e., material behavior) for FRCC materials through analysis of the state-of-the-art research findings on the FM-ITZ of FRCC materials. The following results are obtained. For the mechanical process, the induced curing pressure changes the stress state and enhances multicracking behavior, which can strengthen the FM-ITZ. For the hydraulic process, the strengthened seepage of the FM-ITZ under induced curing pressure weakens the effective stress and exaggerates the deficiency in water retention capacity between the bulk matrix and the FMITZ. For the thermal process, the induced curing pressure causes a steep temperature gradient in the FM-ITZ and thus influences the temperature evolution and thermally-induced microcracks in the FM-ITZ. For the chemical process, the induced curing pressure enhances hydration kinetics and results in the formation of additional hydration products in the FM-ITZ. Moreover, recommendations are proposed on the basis of findings from this review to facilitate the implementation of fiber reinforcement in cemented paste backfill technology.展开更多
With the emphasis on environmental issues,the recycling of waste concrete,even recycled concrete,has become a hot spot in the field of architecture.But the repeated recycling of waste concrete used in harsh environmen...With the emphasis on environmental issues,the recycling of waste concrete,even recycled concrete,has become a hot spot in the field of architecture.But the repeated recycling of waste concrete used in harsh environments is still a complex problem.This paper discusses the durability and recyclability of recycled aggregate concrete(RAC)as a prefabricated material in the harsh environment,the effect of high-temperature curing(60℃,80℃,and 100℃)on the frost resistance of RAC and physical properties of the second generation recycled coarse aggregate(RCA_(2))of RAC after 300 freeze-thaw cycles were studied.The frost resistance of RAC was characterized by compressive strength,relative dynamic elastic modulus,and mass loss.As the physical properties of RCA_(2),the apparent density,water absorption,and crushing value were measured.And the SEM images of RAC after 300 freeze-thaw cycles were shown.The results indicated that the frost resistance of RAC cured at 80℃ for 7 days was comparable to that cured in the standard condition(cured for 28 days at 20℃±2℃ and 95%humidity),and the RAC cured at 100℃ was slightly worse.However,the frost resistance of RAC cured at 60℃ deteriorated seriously.The RAC cured at 80℃ for 7 days is the best.Whether after the freeze-thaw cycle or not,the RCA that curd at 60℃,80℃,and 100℃ for 7 days can also meet the requirements of Grade III RCA and be used as the aggregate of non-bearing part of prefabricated concrete components.RCA_(2) which is cured at 80℃ for 7 days had the best physical properties.展开更多
A type of heat-curing phosphate binder was proposed,and orthogonal experiments based on the tensile strength of sand samples determined that the optimal composition of the binder was phosphoric acid:water:aluminum hyd...A type of heat-curing phosphate binder was proposed,and orthogonal experiments based on the tensile strength of sand samples determined that the optimal composition of the binder was phosphoric acid:water:aluminum hydroxide:magnesium oxide:boric acid=300:70:60:9:8.Adding 10%polyvinyl alcohol(PVA)solution during the sand mixture process can significantly improve the 24 h tensile strength of sand samples.When adding 30 g phosphate binder and 8 g 10%PVA solution,the initial tensile strength of the sample is 0.76 MPa,the room temperature tensile strength is 2.29 MPa,and the 24 h tensile strength is 1.73 MPa.The heat-curing modified phosphate sand mold has high tensile strength and low gas generation,which can meet general casting production requirements.展开更多
Energy demands are increasing continuously,and the development of sustainable technologies in energy systems is a critical and vital concern.Providing the required energy for social and economic needs in line with dim...Energy demands are increasing continuously,and the development of sustainable technologies in energy systems is a critical and vital concern.Providing the required energy for social and economic needs in line with diminishing the environmental effects and pollution emissions is necessary to meet sustainable development.Designing new energy systems with improved efficiency,securing the energy need,using clean and renewable energy sources,reducing energy losses and pollution,and expanding the availability and access to energy are the key elements of sustainable energy development.展开更多
Understanding the variation of lags with respect to the X-ray flux is important to explore the geometry of the inner region of the accretion disk in AGNs.We performed frequency-lag,energy–lag and spectral studies for...Understanding the variation of lags with respect to the X-ray flux is important to explore the geometry of the inner region of the accretion disk in AGNs.We performed frequency-lag,energy–lag and spectral studies for two sets of observations,in order to investigate the variations in lags with respect to X-ray flux in the AGN source Mrk 704 using the XMM-Newton observatory.We divided one of the light curves into two sections which were noticed to exhibit a flux variation.The frequency-lag spectra in different energy domains revealed that reverberation(soft)lags varied along with the flux.For the first time,we show that the blurred reflection model can consistently explain the soft excess observed in the X-ray spectra for this source.The fluxes of soft(i.e.,reflection)and hard components were noted to vary by~18%and~9%respectively,across the sections.The soft lag amplitude was found to be larger at the high flux state than the amplitude at the low flux state.Most importantly,we found that both frequency-lag and energy–lag spectra do not display significant variation between two observational data sets despite a flux variation of 43%.This phenomenon cannot be explained by the reflection model because the soft lag amplitudes must be larger in the high flux state.The probable scenario is that,in the low flux state,the obscuring cloud delays the reflected soft photons which increases the soft lag amplitude.展开更多
In order to explore the internal curing mechanism of sepiolite in cement-based materials,the effects of sepiolite on the water consumption of standard consistency,setting time,viscosity,strength,pore structure charact...In order to explore the internal curing mechanism of sepiolite in cement-based materials,the effects of sepiolite on the water consumption of standard consistency,setting time,viscosity,strength,pore structure characteristics,micro-hardness characteristics and two-dimensional surface characteristics of cement paste were studied,respectively.The experimental results show that the water consumption of standard consistency increases linearly with the increase of sepiolite content.The setting time and viscosity are also lengthened and increased with the addition of sepiolite,respectively.When the content of sepiolite exceeds 5%,the strength of the specimen increases significantly.The BET results show that the pore structure of the interfacial transition zone(ITZ)in hardened cement paste(HCP)with sepiolite is optimized after curing for28 d and its pore volume content with below 10 nm is decreased,especially for the specimen with a lower watercement ratio.The characteristics of microhardness and strength of specimens have the same law.Backscattered electron image(BSE-IA)shows that the ITZ of the specimen with sepiolite is denser and the unhydrated cement particles are less than the reference specimen.展开更多
This study aims to clarify the effects of curing regimes and lightweight aggregate(LWA)on the morphology, width and mechanical properties of the interfacial transition zone(ITZ) of ultra-high performance concrete(UHPC...This study aims to clarify the effects of curing regimes and lightweight aggregate(LWA)on the morphology, width and mechanical properties of the interfacial transition zone(ITZ) of ultra-high performance concrete(UHPC), and provide reference for the selection of lightweight ultra-high performance concrete(L-UHPC) curing regimes and the pre-wetting degree LWA. The results show that, under the three curing regimes(standard curing, steam curing and autoclaved curing), LWA is tightly bound to the matrix without obvious boundaries. ITZ width increases with the water absorption of LWA and decreases with increasing curing temperature. The ITZ microhardness is the highest when water absorption is 3%, and the microhardness value is more stable with the distance from LWA. Steam and autoclaved curing increase ITZ microhardness compared to standard curing. As LWA pre-wetting and curing temperatures increase, the degree of hydration at the ITZ increases, generating high-density CSH(HD CSH) and ultra-high-density CSH(UHD CSH), and reducing unhydrated particles in ITZ. ITZ micro-mechanical properties are optimized due to hydration products being denser.展开更多
To explore the distribution of and the mechanical properties(compressive strength)of the hardened body of alkali slag-fly ash cementitious materials,this study was conducted by using the XRD,FTIR,SEM/EDS,and other tes...To explore the distribution of and the mechanical properties(compressive strength)of the hardened body of alkali slag-fly ash cementitious materials,this study was conducted by using the XRD,FTIR,SEM/EDS,and other test methods in three conditions:airtight drying(AD),airtight immersion(AI),and airtight soaking(AS).The 1D distribution law of free of hardened body under standard curing conditions was explored.The experimental results show that under standard curing conditions,the 1D distribution of within 0d-3 d shows a∨-shaped distribution,within 3-7 d show a∧-shaped distribution,and within 7-28 d tends to be balanced.The test results of leaching rate show that the free was the most stable under AD conditions and the hardened body bound the most by XRD,FTIR and SEM/EDS.And the compressive strength of the hardened body was the highest.The compressive strength of 28th reached 95.9 MPa.The definite distribution of provides an important reference for the strength development and durability evaluation of the hardened body of alkaliexcited cementitious materials.展开更多
基金funding from CNPq(Brazilian council for scientific and technological development)through 201465/2015-9 scholarship of the“Science without borders”programsupport of MCTES/FCT(Portuguese Science and Technology Foundation of Portuguese Ministry of Science and Technology)through CEECIND/04583/2017 grant+1 种基金financially supported by:Base Funding-UIDB/04708/2020 of the CONSTRUCT-Instituto de I&D em Estruturas e Construções-funded by national funds through FCT/MCTES(PIDDAC)A special acknowledgment is also due to the Portuguese National Steel Industry of Maia,part of MEGASA group,for the steel slag supply and to Professor Joaquim Faria for his support in understanding the basic notions of chemistry.
文摘In this work,an alternative alkali-activated cement(AAC)made of ladle slag precursor mixed with sodium hydroxide and sodium silicate has been developed to enhance the bearing capacity of estuarine soils in coastal conditions via deep soil mixing(DSM).The AAC was optimized to use a low reactivity precursor(ladle slag)and to deal with a contaminated high-water content natural sediment cured under water.The material performance was analysed by comparison to a mixture made with Portland cement and cured in the same conditions.Flexural and unconfined compressive strength tests as well as seismic waves measurements after 3-,7-,14-and 28-d curing were performed to obtain a relationship between elastic stiffness and strength with curing time for both mixtures.Remarkably,the AAC mix demonstrated superior strength results,exhibiting almost double flexural and compressive strengths after 28 d compared to the Portland cement mix.The AAC mix also showed a higher rate of stiffness increase than the Portland cement mix,which has a higher initial stiffness at young ages but lower stiffness evolution.Leachate analysis confirmed that the proposed AAC could effectively immobilise any contaminants from soil or precursors.The effect of curing under stress was analysed in triaxial compression tests and found to be insignificant,indicating that laboratory data obtained without stress curing can represent the material's behaviour in a DSM column,which will cure under the weight of the column.
基金Funded by the National Natural Science Foundation of China(No.21865017)。
文摘The reactive diluent prepared by siloxane modified Trimethylene oxide can improve the performance of the UV curing system.Therefore,1,7-bis[(3-ethyl-3-methoxyoxacylobutane)propyl]octadecylosiloxane(BEMOPOMTS)was synthesized from diethyl carbonate,trimethylopropanes,allyl bromide,and 1,1,3,3,5,5,7,7-octadecylosiloxane as the main raw materials.BEMOPOMTS can be used as reactive diluents in the field of cationic UV curing.It has good thermal stability,and the addition of BEMOPOMTS significantly improves the tensile strength and elongation at break of epoxy resin.Compared with the pure epoxy resin,adding 20%BEMOPOMTS increased the elastic modulus by 25%to 677 MPa.
基金Funded by Hubei Technology Innovation Key Program (No.2018AAA004)。
文摘The strength development law of γ-type dicalcium silicate (γ-C_(2)S) under different carbonation processes was investigated,and the carbonation mechanism of γ-C_(2)S under the action of NH_(4)HCO_(3) was clarified by using a wide range of test methods,including XRD and SEM.A method of saturated NH_(4)HCO_(3) solution as a curing agent was identified to improve the carbonation efficiency and enhance the carbonation degree of γ-C_(2)S,and then a high-strength carbonated specimen was obtained.Microhardness analysis and SEM morphology analysis were conducted on the carbonised specimens obtained under atmospheric pressure carbonisation conditions using the curing agent.It was found that γ-C_(2)S could perform carbonisation well under atmospheric pressure,which promoted the carbonisation efficiency and decreased the carbonisation cost simultaneously.Therefore,a new carbonisation process solution was proposed for the rapid carbonisation of γ-C_(2)S.
基金funded by the National Natural Science(Grant No.52274015)。
文摘Sustained casing pressure(SCP)is a crucial issue in the oil and gas production lifecycle.Epoxy resins,exhibiting exceptional compressive strength,ductility,and shear bonding strength,have the potential to form reliable barriers.The injectivity and sealing capacity of the epoxy resin is crucial parameters for the success of shallow remediation operations.This study aimed to develop and assess a novel solid-free resin sealant as an alternative to Portland cement for mitigating fluid leakage.The investigation evaluated the viscosity,compressive strength,and brittleness index of the epoxy resin sealant,as well as its tangential and normal shear strengths in conjunction with casing steel.The flow characteristics and sealing abilities of conventional cement and epoxy resin were comparatively analyzed in cracks.The results showed that the application of a viscosity reducer facilitated control over the curing time of the epoxy resin,ranging from 1.5 to 6 h,and reduced the initial viscosity from 865.53 to 118.71 m Pa,s.The mechanical properties of the epoxy resin initially increased with a rise in curing agent content before experiencing a minor decrease.The epoxy resin containing 30%curing agent exhibited optimal mechanical properties.After a 14-day curing period,the epoxy resin's compressive strength reached81.37 MPa,2.12 times higher than that of cement,whereas the elastic modulus of cement was 2.99 times greater than that of the epoxy resin.The brittleness index of epoxy resin is only 3.42,demonstrating high flexibility and toughness.The tangential and normal shear strengths of the epoxy resin exceeded those of cement by 3.17 and 2.82 times,respectively.In a 0.5 mm-wide crack,the injection pressure of the epoxy resin remained below 0.075 MPa,indicating superior injection and flow capabilities.Conversely,the injection pressure of cement surged dramatically to 2.61 MPa within 5 min.The breakthrough pressure of0.5 PV epoxy resin reached 7.53 MPa,decreasing the crack's permeability to 0.02 D,a mere 9.49%of the permeability observed following cement plugging.Upon sealing a 2 mm-wide crack using epoxy resin,the maximum breakthrough pressure attained 5.47 MPa,3.48 times of cement.These results suggest that epoxy resin sealant can be employed safely and effectively to seal cracks in the cement.
基金Funded by the National Key Research and Development Program of China (No.2019YFC1906202)the Guangxi Key Research and Development Plan (Nos.Guike AA18242007-3, Guike AB19259008, and Guike AB20297014)。
文摘Internal curing agents (ICA) based on super absorbent polymer have poor alkali tolerance and reduce the early strength of concrete.An alkali tolerate internal curing agent (CAA-ICA) was designed and prepared by using sodium carboxymethyl starch (CMS) with high hydrophilicity,acrylic acid (AA) containing anionic carboxylic group and acrylamide (AM) containing non-ionic amide group as the main raw materials.The results show that the ratio of CAA-ICA alkali absorption solution is higher than that existing ICA,which solves the low water absorption ratio of the ICA in alkali environment.The water absorption ratio of CAA-ICA in saturated Ca(OH)_(2) solution is 95.8 g·g^(-1),and the alkali tolerance coefficient is 3.4.The application of CAA-ICA in cement-based materials can increase the internal relative humidity and miniaturize the pore structure.The compressive strength of mortar increases up to 12.95%at 28 d,which provids a solution to overcome the reduction of the early strength.
基金Funded by the National Natural Science Foundation of China(No.52378213)the Technology Development Project(No.20201902977180010) of CABR Technology Co.,Ltd。
文摘To promote the production and application of artificial aggregates,save natural sand resources and protect the ecological environment,we evaluated the feasibility of using spherical porous functional aggregates(SPFAs) formed by basalt saw mud under autoclave curing in ordinary structural concrete.In our work,two types of prewetted functional aggregates were taken as replacements for natural aggregates with different volume substitution rates(0%,5%,10%,15%,20%,25%,and 30%) in the preparation of ordinary structural concrete with water-to-binder ratios(W/B) of 0.48 and 0.33.The effects of the functional aggregate properties and content,W/B,and curing age on the fluidity,density,mechanical properties and autogenous shrinkage of ordinary concrete were analyzed.The experimental results showed that the density of concrete declined at a rate of not more than 5%,and the 28 d compressive strength could reach 31.0-68.2 MPa.Low W/B,long curing age and high-quality functional aggregates were conducive to enhancing the mechanical properties of SPFAs concrete.Through the rolling effects,SPFAs can optimize the particle gradation of aggregate systems and improve the fluidity of concrete,and the water stored inside SPFAs provides an internal curing effect,which prolongs the cement hydration process and considerably reduces the autogenous shrinkage of concrete.SPFAs exhibits high strength and high density,as well as being more cost-effective and ecological,and is expected to be widely employed in ordinary structural concrete.
文摘Plain concrete is strong in compression but brittle in tension,having a low tensile strain capacity that can significantly degrade the long-term performance of concrete structures,even when steel reinforcing is present.In order to address these challenges,short polymer fibers are randomly dispersed in a cement-based matrix to forma highly ductile engineered cementitious composite(ECC).Thismaterial exhibits high ductility under tensile forces,with its tensile strain being several hundred times greater than conventional concrete.Since concrete is inherently weak in tension,the tensile strain capacity(TSC)has become one of the most extensively researched properties.As a result,developing a model to predict the TSC of the ECC and to optimize the mixture proportions becomes challenging.Meanwhile,the effort required for laboratory trial batches to determine the TSC is reduced.To achieve the research objectives,five distinct models,artificial neural network(ANN),nonlinear model(NLR),linear relationship model(LR),multi-logistic model(MLR),and M5P-tree model(M5P),are investigated and employed to predict the TSCof ECCmixtures containing fly ash.Data from115 mixtures are gathered and analyzed to develop a new model.The input variables include mixture proportions,fiber length and diameter,and the time required for curing the various mixtures.The model’s effectiveness is evaluated and verified based on statistical parameters such as R2,mean absolute error(MAE),scatter index(SI),root mean squared error(RMSE),and objective function(OBJ)value.Consequently,the ANN model outperforms the others in predicting the TSC of the ECC,with RMSE,MAE,OBJ,SI,and R2 values of 0.42%,0.3%,0.33%,0.135%,and 0.98,respectively.
文摘[Objectives]This study was conducted to compare the effects of different curing processes on the characteristics of marinated beef.[Methods]Marinated beef was obtained by two curing processes:static curing and injection and vacuum tumbling curing.The effects of the two curing processes on the production rate,curing absorption rate,water content,soluble protein content,amino acid nitrogen content,texture characteristics and microstructure of the product were compared.[Results]Compared with static curing,the production rate of marinated beef increased by 10%,the curing absorption rate increased by 28%,the texture and microstructure were improved,and the water content increased,while the soluble protein content decreased.As a result,the sensory score was higher.There was no significant difference in the content of amino acid nitrogen,but it decreased compared with raw meat.To sum up,injection and vacuum tumbling curing is more conducive to the processing of marinated beef.[Conclusions]This study provides a theoretical basis for the industrial production of marinated beef,and lays a foundation for in-depth exploration of injection and vacuum tumbling curing technique of marinated beef.
文摘By using HDI and TMP as the main raw materials,polyethylene glycol 400(PEG400)is used as a non-ionic hydrophilic modifier,and sodium hydroxyethyl sulfonate is used as an ionic hydrophilic modifier to synthesize a dual hydrophilic modified polyurethane curing agent.Research revealed that introducing PEG400 for hydrophilic chain segments and sodium hydroxyethyl sulfonate for hydrophilic ionic groups in the polyurethane curing agent component leads to a uniform distribution of hydrophilic components,significantly enhancing compatibility with the aqueous polyol component,and results in excellent film performance.The synthesis process and film were characterized using Fourier transform infrared spectroscopy and high-resolution scanning electron microscopy in the study.
文摘National food security is the backbone of any economy,and achieving food security is essential for the prosperity of a nation.During my study in China at the Institute of South-South Cooperation and Development,Peking University,from September 2022 to July 2023,I leant how China has managed to achieve food security despite its large population of around 1.4 billion and numerous other challenges by means of strategic planning,e"ective policy execution,technological advancement and global collaboration.
文摘Some people,mainly in the West,were taken by surprise when six Chinese warships were seen near the Red Sea in October 2023 amid the conflict in Gaza.Some Western media and politicians tried to frame China’s mission as an escalatory move in the Middle East.
文摘This paper examines the application of polyurethane curing technology in the construction of railway track beds,with a specific focus on its implementation in China’s rapidly developing railway infrastructure.The study begins by identifying the limitations of traditional ballasted track beds,especially under the demands of high-speed and heavyload railways.It then methodically analyzes the advantages of polyurethane-cured track beds,highlighting their improved mechanical properties,including enhanced stability and durability.The paper further explores the benefits of transitioning to prefabricated polyurethane track beds,emphasizing significant cost reductions,better construction quality,and enhanced maintainability.Through a detailed review of experimental data and practical applications,the paper demonstrates the efficacy of polyurethane track beds in various railway settings.A critical part of the research involves optimizing the structural parameters of polyurethane track beds to achieve the best balance of mechanical and damping properties.The conclusion of the paper underscores the potential of polyurethane curing technology as a transformative approach to railway track bed construction,offering a solution to the challenges posed by traditional methods and aligning with the evolving needs of modern railways.
基金the Natural Sciences and Engineering Research Council of Canada (NSERC)Lakehead University for their financial support。
文摘The mesoscale fiber-matrix interfacial transition zone(FM-ITZ) under induced curing pressure plays a key role in the effectiveness of fiber reinforcement and the engineering application of fiber-reinforced cementitious composites(FRCCs). This critical review establishes the link among induced curing pressure(i.e., external loading condition), multiphysics processes(i.e., internal governing mechanism), and interface behavior(i.e., material behavior) for FRCC materials through analysis of the state-of-the-art research findings on the FM-ITZ of FRCC materials. The following results are obtained. For the mechanical process, the induced curing pressure changes the stress state and enhances multicracking behavior, which can strengthen the FM-ITZ. For the hydraulic process, the strengthened seepage of the FM-ITZ under induced curing pressure weakens the effective stress and exaggerates the deficiency in water retention capacity between the bulk matrix and the FMITZ. For the thermal process, the induced curing pressure causes a steep temperature gradient in the FM-ITZ and thus influences the temperature evolution and thermally-induced microcracks in the FM-ITZ. For the chemical process, the induced curing pressure enhances hydration kinetics and results in the formation of additional hydration products in the FM-ITZ. Moreover, recommendations are proposed on the basis of findings from this review to facilitate the implementation of fiber reinforcement in cemented paste backfill technology.
基金This research was funded by the National Natural Science Foundation of China(52078068)Practice Innovation Program of Jiangsu Province(KYCX22_3082).
文摘With the emphasis on environmental issues,the recycling of waste concrete,even recycled concrete,has become a hot spot in the field of architecture.But the repeated recycling of waste concrete used in harsh environments is still a complex problem.This paper discusses the durability and recyclability of recycled aggregate concrete(RAC)as a prefabricated material in the harsh environment,the effect of high-temperature curing(60℃,80℃,and 100℃)on the frost resistance of RAC and physical properties of the second generation recycled coarse aggregate(RCA_(2))of RAC after 300 freeze-thaw cycles were studied.The frost resistance of RAC was characterized by compressive strength,relative dynamic elastic modulus,and mass loss.As the physical properties of RCA_(2),the apparent density,water absorption,and crushing value were measured.And the SEM images of RAC after 300 freeze-thaw cycles were shown.The results indicated that the frost resistance of RAC cured at 80℃ for 7 days was comparable to that cured in the standard condition(cured for 28 days at 20℃±2℃ and 95%humidity),and the RAC cured at 100℃ was slightly worse.However,the frost resistance of RAC cured at 60℃ deteriorated seriously.The RAC cured at 80℃ for 7 days is the best.Whether after the freeze-thaw cycle or not,the RCA that curd at 60℃,80℃,and 100℃ for 7 days can also meet the requirements of Grade III RCA and be used as the aggregate of non-bearing part of prefabricated concrete components.RCA_(2) which is cured at 80℃ for 7 days had the best physical properties.
文摘A type of heat-curing phosphate binder was proposed,and orthogonal experiments based on the tensile strength of sand samples determined that the optimal composition of the binder was phosphoric acid:water:aluminum hydroxide:magnesium oxide:boric acid=300:70:60:9:8.Adding 10%polyvinyl alcohol(PVA)solution during the sand mixture process can significantly improve the 24 h tensile strength of sand samples.When adding 30 g phosphate binder and 8 g 10%PVA solution,the initial tensile strength of the sample is 0.76 MPa,the room temperature tensile strength is 2.29 MPa,and the 24 h tensile strength is 1.73 MPa.The heat-curing modified phosphate sand mold has high tensile strength and low gas generation,which can meet general casting production requirements.
文摘Energy demands are increasing continuously,and the development of sustainable technologies in energy systems is a critical and vital concern.Providing the required energy for social and economic needs in line with diminishing the environmental effects and pollution emissions is necessary to meet sustainable development.Designing new energy systems with improved efficiency,securing the energy need,using clean and renewable energy sources,reducing energy losses and pollution,and expanding the availability and access to energy are the key elements of sustainable energy development.
基金K.S.acknowledges the financial support from the Indian Space Research Organisation(ISRO),Government of India。
文摘Understanding the variation of lags with respect to the X-ray flux is important to explore the geometry of the inner region of the accretion disk in AGNs.We performed frequency-lag,energy–lag and spectral studies for two sets of observations,in order to investigate the variations in lags with respect to X-ray flux in the AGN source Mrk 704 using the XMM-Newton observatory.We divided one of the light curves into two sections which were noticed to exhibit a flux variation.The frequency-lag spectra in different energy domains revealed that reverberation(soft)lags varied along with the flux.For the first time,we show that the blurred reflection model can consistently explain the soft excess observed in the X-ray spectra for this source.The fluxes of soft(i.e.,reflection)and hard components were noted to vary by~18%and~9%respectively,across the sections.The soft lag amplitude was found to be larger at the high flux state than the amplitude at the low flux state.Most importantly,we found that both frequency-lag and energy–lag spectra do not display significant variation between two observational data sets despite a flux variation of 43%.This phenomenon cannot be explained by the reflection model because the soft lag amplitudes must be larger in the high flux state.The probable scenario is that,in the low flux state,the obscuring cloud delays the reflected soft photons which increases the soft lag amplitude.
基金Funded by the Natural Science Foundation of China(No.51408380)the Science and Technology Plan of He Bei Province(No.E2021210033)the Scientific and Technological Development Funds of the Central Government Shall Guide Local(No.216Z3801G)。
文摘In order to explore the internal curing mechanism of sepiolite in cement-based materials,the effects of sepiolite on the water consumption of standard consistency,setting time,viscosity,strength,pore structure characteristics,micro-hardness characteristics and two-dimensional surface characteristics of cement paste were studied,respectively.The experimental results show that the water consumption of standard consistency increases linearly with the increase of sepiolite content.The setting time and viscosity are also lengthened and increased with the addition of sepiolite,respectively.When the content of sepiolite exceeds 5%,the strength of the specimen increases significantly.The BET results show that the pore structure of the interfacial transition zone(ITZ)in hardened cement paste(HCP)with sepiolite is optimized after curing for28 d and its pore volume content with below 10 nm is decreased,especially for the specimen with a lower watercement ratio.The characteristics of microhardness and strength of specimens have the same law.Backscattered electron image(BSE-IA)shows that the ITZ of the specimen with sepiolite is denser and the unhydrated cement particles are less than the reference specimen.
基金Funded by the National Natural Science Foundation of China (Nos.U21A20149, 51878003, 51908378)Research Reserve of Anhui Jianzhu University (No.2022XMK01)Excellent Scientific Research and Innovation Team in Colleges and Universities of Anhui Province(No. 2022AH010017)。
文摘This study aims to clarify the effects of curing regimes and lightweight aggregate(LWA)on the morphology, width and mechanical properties of the interfacial transition zone(ITZ) of ultra-high performance concrete(UHPC), and provide reference for the selection of lightweight ultra-high performance concrete(L-UHPC) curing regimes and the pre-wetting degree LWA. The results show that, under the three curing regimes(standard curing, steam curing and autoclaved curing), LWA is tightly bound to the matrix without obvious boundaries. ITZ width increases with the water absorption of LWA and decreases with increasing curing temperature. The ITZ microhardness is the highest when water absorption is 3%, and the microhardness value is more stable with the distance from LWA. Steam and autoclaved curing increase ITZ microhardness compared to standard curing. As LWA pre-wetting and curing temperatures increase, the degree of hydration at the ITZ increases, generating high-density CSH(HD CSH) and ultra-high-density CSH(UHD CSH), and reducing unhydrated particles in ITZ. ITZ micro-mechanical properties are optimized due to hydration products being denser.
基金Funded by the Natural Sciences Foundation of China(No.51808025)the Pyramid Talent Training Project of BUCEA(No.JDYC20200329)。
文摘To explore the distribution of and the mechanical properties(compressive strength)of the hardened body of alkali slag-fly ash cementitious materials,this study was conducted by using the XRD,FTIR,SEM/EDS,and other test methods in three conditions:airtight drying(AD),airtight immersion(AI),and airtight soaking(AS).The 1D distribution law of free of hardened body under standard curing conditions was explored.The experimental results show that under standard curing conditions,the 1D distribution of within 0d-3 d shows a∨-shaped distribution,within 3-7 d show a∧-shaped distribution,and within 7-28 d tends to be balanced.The test results of leaching rate show that the free was the most stable under AD conditions and the hardened body bound the most by XRD,FTIR and SEM/EDS.And the compressive strength of the hardened body was the highest.The compressive strength of 28th reached 95.9 MPa.The definite distribution of provides an important reference for the strength development and durability evaluation of the hardened body of alkaliexcited cementitious materials.