Azoxy dyes and their copper complexes with maximum dichroism in the spectrum range from 550nm to 700nm were synthesized and used to prepare polyvinyl alcohol (PVA) polarizing films. These films showed excellent polari...Azoxy dyes and their copper complexes with maximum dichroism in the spectrum range from 550nm to 700nm were synthesized and used to prepare polyvinyl alcohol (PVA) polarizing films. These films showed excellent polarizing ability. In addition, a neutral gray polarizing film was prepared by mixing synthesized dichromatic dyes with other dyes. The obtained polarizable film for gray shade was little pervious to light over the visible radiation wavelength region, ranging from 400nm to 700nm at cross state, and excellent in the polarizing activities and stable to moisture and heat.展开更多
Gamma irradiation is employed for in situ preparation of PVA-PANI-ZnS nanocomposite. The irradiation dose is varied from 10 to 40 kGy at 10 kGy intervals. The XRD result confirms the formation of crystalline phases co...Gamma irradiation is employed for in situ preparation of PVA-PANI-ZnS nanocomposite. The irradiation dose is varied from 10 to 40 kGy at 10 kGy intervals. The XRD result confirms the formation of crystalline phases corresponding to ZnS nanoparticles, PVA and PANI. Field emission scanning electron microscopy shows the formation of agglomerated PANI along the PVA backbone, within which the ZnS nanoparticles are dispersed.UV-visible spectroscopy is conducted to measure the transmittance spectra of samples revealing the electronic absorption characteristics of ZnS and PANI nanoparticles. Photo-acoustic（PA） setup is installed to investigate the thermal properties of samples. The PA spectroscopy indicates a high value of thermal diffusivity for samples due to the presence of ZnS and PANI nanoparticles. Moreover, at higher doses, the more polymerization and formation of PANI and ZnS nanoparticles result in enhancement of thermal diffusivity.展开更多
Pure and doped Polyvinylidene difluoride (PVDF) films, for the detection of infrared radiation, have been well documented using the mechanism of pyroelectricity. Alternatively, the electrical properties of films made ...Pure and doped Polyvinylidene difluoride (PVDF) films, for the detection of infrared radiation, have been well documented using the mechanism of pyroelectricity. Alternatively, the electrical properties of films made from Polyvinyl Alcohol (PVA) have received considerable attention in recent years. The investigation of surface resistivities of both such films, to this point, has received far less consideration in comparison to pyroelectric effects. In this research, we report temperature dependent surface resistivity measurements of commercial, and of multiwall carbon nanotubes (MWCNT), or Ag-nanoparticle doped PVA films. Without any variation in the temperature range from 22°C to 40°C with controlled humidity, we found that the surface resistivity decreases initially, reaches a minimum, but rises steadily as the temperature continues to increase. This research was conducted with the combined instrumentation of the Keithley Model 6517 Electrometer and Keithley Model 8009 resistivity test fixture using both commercial and in-house produced organic thin films. With the objective to quantify the suitability of PVDF and PVA films as IR detector materials, when using the surface resistivity phenomenon, instead of or in addition to the pyroelectricity, surface resistivity measurements are reported when considering bolometry. We found that the surface resistivity measurements on PVA films were readily implemented.展开更多
The influence of PVA water soluble film on the quality of llaundry capsule was discussed from three aspects:appearance,manufacture and use.The basic properties of several mainstream PVA membranes on the market related...The influence of PVA water soluble film on the quality of llaundry capsule was discussed from three aspects:appearance,manufacture and use.The basic properties of several mainstream PVA membranes on the market related to laundry capsules were evaluated.The results show that the mist value of the film affects the appearance of the capsules.The higher the mist value is,the worse the transparency of the capsules is.The mechanical properties of the film affect the shape of the capsules,the tensile strength>35 Mpa,elongation>400%,modulus>50 Mpa,the shape of the capsules is more three-dimensional;The water solubility of the film can affect the production of the capsules,and the production of the capsules is smooth when the film breaking speed is greater than 20~30 s and the dissolution speed is 40~60 s.The film compatibility index reflects the effect of the capsules washing machine.The shorter the dissolution time of the compatibility,the less the residue of the capsules after washing.展开更多
基金Scientific Fundation of Anhui University of Technology and Science,China (No.2007YQ001)
文摘Azoxy dyes and their copper complexes with maximum dichroism in the spectrum range from 550nm to 700nm were synthesized and used to prepare polyvinyl alcohol (PVA) polarizing films. These films showed excellent polarizing ability. In addition, a neutral gray polarizing film was prepared by mixing synthesized dichromatic dyes with other dyes. The obtained polarizable film for gray shade was little pervious to light over the visible radiation wavelength region, ranging from 400nm to 700nm at cross state, and excellent in the polarizing activities and stable to moisture and heat.
文摘Gamma irradiation is employed for in situ preparation of PVA-PANI-ZnS nanocomposite. The irradiation dose is varied from 10 to 40 kGy at 10 kGy intervals. The XRD result confirms the formation of crystalline phases corresponding to ZnS nanoparticles, PVA and PANI. Field emission scanning electron microscopy shows the formation of agglomerated PANI along the PVA backbone, within which the ZnS nanoparticles are dispersed.UV-visible spectroscopy is conducted to measure the transmittance spectra of samples revealing the electronic absorption characteristics of ZnS and PANI nanoparticles. Photo-acoustic（PA） setup is installed to investigate the thermal properties of samples. The PA spectroscopy indicates a high value of thermal diffusivity for samples due to the presence of ZnS and PANI nanoparticles. Moreover, at higher doses, the more polymerization and formation of PANI and ZnS nanoparticles result in enhancement of thermal diffusivity.
文摘Pure and doped Polyvinylidene difluoride (PVDF) films, for the detection of infrared radiation, have been well documented using the mechanism of pyroelectricity. Alternatively, the electrical properties of films made from Polyvinyl Alcohol (PVA) have received considerable attention in recent years. The investigation of surface resistivities of both such films, to this point, has received far less consideration in comparison to pyroelectric effects. In this research, we report temperature dependent surface resistivity measurements of commercial, and of multiwall carbon nanotubes (MWCNT), or Ag-nanoparticle doped PVA films. Without any variation in the temperature range from 22°C to 40°C with controlled humidity, we found that the surface resistivity decreases initially, reaches a minimum, but rises steadily as the temperature continues to increase. This research was conducted with the combined instrumentation of the Keithley Model 6517 Electrometer and Keithley Model 8009 resistivity test fixture using both commercial and in-house produced organic thin films. With the objective to quantify the suitability of PVDF and PVA films as IR detector materials, when using the surface resistivity phenomenon, instead of or in addition to the pyroelectricity, surface resistivity measurements are reported when considering bolometry. We found that the surface resistivity measurements on PVA films were readily implemented.
文摘The influence of PVA water soluble film on the quality of llaundry capsule was discussed from three aspects:appearance,manufacture and use.The basic properties of several mainstream PVA membranes on the market related to laundry capsules were evaluated.The results show that the mist value of the film affects the appearance of the capsules.The higher the mist value is,the worse the transparency of the capsules is.The mechanical properties of the film affect the shape of the capsules,the tensile strength>35 Mpa,elongation>400%,modulus>50 Mpa,the shape of the capsules is more three-dimensional;The water solubility of the film can affect the production of the capsules,and the production of the capsules is smooth when the film breaking speed is greater than 20~30 s and the dissolution speed is 40~60 s.The film compatibility index reflects the effect of the capsules washing machine.The shorter the dissolution time of the compatibility,the less the residue of the capsules after washing.