The optical observation results of neocrystallization nucleation and growth of fine fully lamellar (FFL) α 2/ γ microstructure of a TiAl based alloy in rapid heating cyclic heat treatment process were reported. The ...The optical observation results of neocrystallization nucleation and growth of fine fully lamellar (FFL) α 2/ γ microstructure of a TiAl based alloy in rapid heating cyclic heat treatment process were reported. The characteristics of α+γ→α transformation under rapid heating conditions were analysed. A model for explaining the nucleation and growth mechanism of FFL α 2/ γ microstructure was proposed.展开更多
An annealed 50 Cr V4 steel was subjected to cyclic heat treatment process that consists of repeated short-duration(200 s)held at 840 °C(above Ac3 temperature of 790 °C) and short-duration(100 s) held at 700 ...An annealed 50 Cr V4 steel was subjected to cyclic heat treatment process that consists of repeated short-duration(200 s)held at 840 °C(above Ac3 temperature of 790 °C) and short-duration(100 s) held at 700 °C(below Ac1 temperature of 710 °C). The spheroidization ratio of cementite and the average size of particles increase with increasing the cyclic number of heat treatment. After5-cycle heat treatment, the spheroidization ratio of cementite is 100%, and the average size of the cementite particles is about0.53 μm. After cyclic heat treatment, the hardness, ultimate tensile strength and yield strength of the experimental steel gradually decrease with increasing cyclic number of heat treatment. The elongation of the as-received specimens is about 7.4%, the elongation of the 1-cycle specimen is 14.3%, and the elongation of 5-cycle specimen reaches a peak value of 22.5%, thereafter marginally decreases to 18.3% after 6-cycle heat treatment. Accordingly, the fractured surface initially exhibits the regions of wavy lamellar fracture. By increasing the cyclic number of heat treatment cycles, the regions of dimples consume the entire fractured surface gradually. Some large dimples can be found in the fracture surface of the specimen subjected to six heat treatment cycles.展开更多
To improve the strength-toughness of 13Cr4NiMo martensitic stainless steel(13-4MSS),a thermal cyclic heat treatment(TCHT)combined with the advantage of tempering was proposed.The microstructures were characterized by ...To improve the strength-toughness of 13Cr4NiMo martensitic stainless steel(13-4MSS),a thermal cyclic heat treatment(TCHT)combined with the advantage of tempering was proposed.The microstructures were characterized by scanning electron microscopy,X-ray diffraction and electron backscattered diffraction,and the mechanical behaviors in terms of tensile properties and impact toughness were analyzed in correlation with microstructural evolution.It was found that grains and the martensitic matrix were refined by TCHT through the cyclic quenching transformation and austenite recrystallization,which was conducive to more nucleation quantity of reversed austenite during tempering.Two-sphericalcap nucleation model was used to explain the effect of refined grains of TCHT on the nucleation of reversed austenite.Grain refinement by TCHT improved the brittle fracture stress to reduce the ductile-brittle transition temperature and thus improved the cryogenic impact toughness of 13-4MSS.Reversed austenite distributed at the martensitic lath boundary enhances the crack arrest performance and increases the britle fracture stress.It is concluded that reasonable TCHT plus tempering process significantly improves the strength-toughness of 13-4MSS,reflecting the comprehensive effect of grain refinement and reversed austenite.展开更多
Cyclic heat treatment that can continuously promote abnormal grain growth is widely used for the prepa-ration of single-crystal Fe-Mn-Al-based shape memory alloys.However,it takes a long time to prepare large-size Fe-...Cyclic heat treatment that can continuously promote abnormal grain growth is widely used for the prepa-ration of single-crystal Fe-Mn-Al-based shape memory alloys.However,it takes a long time to prepare large-size Fe-Mn-Al-based alloy single crystals via the reported cyclic heat treatments.Meanwhile,the long-time cyclic heat treatment at high temperatures leads to the development of defects including oxidation and a decrease in Mn,which would deteriorate superelasticity in the Fe-Mn-Al-based shape memory alloys.To shorten the fabrication time of single crystals,the effect of the cyclic heat treatment process on the abnormal grain growth in the Fe-Mn-Al-based alloys with different Ni contents was systematically investigated.It is found that the abnormal grain growth of Fe-Mn-Al-based alloys was not significantly affected by the Ni contents(within 2.1 at.%-6.2 at.%).In addition,the abnormal grain growth could be promoted by 1-2℃ min^(-1) cooling rate,high solution temperature,and multiple cycles,while it was insensitive to other processes including heating rate,dual-phase time as well as long-time solution treat-ment.These findings can guide optimizing the fabrication process of single crystals by cyclic heat treat-ment.Finally,the Fe_(41.9)Mn_(37.8)Al_(14.1) Ni_(6.2) single crystal prepared by the optimized cyclic heat treatment showed a recoverable strain of about 4%.展开更多
The cyclic semi-solid heat treatment represents a promising technique for improving microstructure and mechanical properties of a wide range of metallic alloys. In the current research the influence of cyclic semi-sol...The cyclic semi-solid heat treatment represents a promising technique for improving microstructure and mechanical properties of a wide range of metallic alloys. In the current research the influence of cyclic semi-solid heat treatment on microstructure of Al-18% Si alloy containing 0.8% Fe has been studied. All specimens were heated in an electrically heated resistance furnace with heating rate of 10°C·min-1 to 585°C. For a complete one cycle heat treatment (5 min heating time), samples after 5 min holding at 585°C were cooled to a temperature of 550°C in still air cooling and the samples were taken out immediately for water quenching. It was found that heat treatment cycles should be limited to 3 cycles or less in order to maintain fine grain size and globular structure without agglomeration and coalescence. Cyclic semi-solid heat treatment changes morphology of iron-rich intermetallics phases to be plate-like and fine plate iron-rich intermetallics phases, in stead of needle-like iron-rich intermetallics phases that are observed in as-cast samples. Cyclic heating shows a relatively higher hardness for all heating cycles compared with as-cast one due to its finer and globular structure. Cyclic semi-solid heat treatment technique results in lower coarsening rate constant compared with isothermal heat treatment one due to coarsening discontinuous effect.展开更多
The effect of cryogenic and heating treatment on the solution properties of rigid polymer nitrocellulose(NC)indilute tetrahydrofuran solution were studied with a sealed viscometer and a size exclusion chromatograph(SE...The effect of cryogenic and heating treatment on the solution properties of rigid polymer nitrocellulose(NC)indilute tetrahydrofuran solution were studied with a sealed viscometer and a size exclusion chromatograph(SEC),respectively.The experimental results show that the relative viscosity of NC solution decreases after repeated freezing-thawing treatment.The decreased viscosity value of NC could not be restored but decreased further after the solution beingre-heated.The experimental results of SEC are fully consistent with that of viscosity measurements.It is believed that theeffect of two treatments on NC solution both causes the apparent hydrodynamic volume to decrease.But they are assumed tobe ascribed to different mechanisms.展开更多
The effects of different treatments, such as dry heat,wet heat, solvent vapor and ultrasonic, on properties of the cyclic oligomers on the surface of polyester fiber are studied. The components of surface oligomers ar...The effects of different treatments, such as dry heat,wet heat, solvent vapor and ultrasonic, on properties of the cyclic oligomers on the surface of polyester fiber are studied. The components of surface oligomers are analyzed through Thin-Layer Chromatograph. The result shows that: all of the treatments, especially solvent vapor treatment, can significantly increase the content of surface cyclic oligomers. The content of cyclic trimer is increased more considerably than other oligomers. Moreover, the morphology and the distribution of surface cyclic oligomers are also different from different treatments: Dry heat and wet heat cause larger polygonal solids distributed evenly on the surface of fiber; solvent vapor makes fiber surface exhibit irregular rodlike crystal shapes randomly; ultrasonic treatment induces some obscure and smaller deposits on the surface of fiber.展开更多
文摘The optical observation results of neocrystallization nucleation and growth of fine fully lamellar (FFL) α 2/ γ microstructure of a TiAl based alloy in rapid heating cyclic heat treatment process were reported. The characteristics of α+γ→α transformation under rapid heating conditions were analysed. A model for explaining the nucleation and growth mechanism of FFL α 2/ γ microstructure was proposed.
文摘An annealed 50 Cr V4 steel was subjected to cyclic heat treatment process that consists of repeated short-duration(200 s)held at 840 °C(above Ac3 temperature of 790 °C) and short-duration(100 s) held at 700 °C(below Ac1 temperature of 710 °C). The spheroidization ratio of cementite and the average size of particles increase with increasing the cyclic number of heat treatment. After5-cycle heat treatment, the spheroidization ratio of cementite is 100%, and the average size of the cementite particles is about0.53 μm. After cyclic heat treatment, the hardness, ultimate tensile strength and yield strength of the experimental steel gradually decrease with increasing cyclic number of heat treatment. The elongation of the as-received specimens is about 7.4%, the elongation of the 1-cycle specimen is 14.3%, and the elongation of 5-cycle specimen reaches a peak value of 22.5%, thereafter marginally decreases to 18.3% after 6-cycle heat treatment. Accordingly, the fractured surface initially exhibits the regions of wavy lamellar fracture. By increasing the cyclic number of heat treatment cycles, the regions of dimples consume the entire fractured surface gradually. Some large dimples can be found in the fracture surface of the specimen subjected to six heat treatment cycles.
基金supported by Specific Research Project of Guangxi for Research Bases and Talents(Grant No.GuiKe AD19245145)Natural Science Foundation of Guangxi Province(Grant No.2018GXNSFBA281106).
文摘To improve the strength-toughness of 13Cr4NiMo martensitic stainless steel(13-4MSS),a thermal cyclic heat treatment(TCHT)combined with the advantage of tempering was proposed.The microstructures were characterized by scanning electron microscopy,X-ray diffraction and electron backscattered diffraction,and the mechanical behaviors in terms of tensile properties and impact toughness were analyzed in correlation with microstructural evolution.It was found that grains and the martensitic matrix were refined by TCHT through the cyclic quenching transformation and austenite recrystallization,which was conducive to more nucleation quantity of reversed austenite during tempering.Two-sphericalcap nucleation model was used to explain the effect of refined grains of TCHT on the nucleation of reversed austenite.Grain refinement by TCHT improved the brittle fracture stress to reduce the ductile-brittle transition temperature and thus improved the cryogenic impact toughness of 13-4MSS.Reversed austenite distributed at the martensitic lath boundary enhances the crack arrest performance and increases the britle fracture stress.It is concluded that reasonable TCHT plus tempering process significantly improves the strength-toughness of 13-4MSS,reflecting the comprehensive effect of grain refinement and reversed austenite.
基金supported by the National Natural Science Foundation of China (No.51971152)the Sichuan Science and Technology Program (No.2020YJ0258).
文摘Cyclic heat treatment that can continuously promote abnormal grain growth is widely used for the prepa-ration of single-crystal Fe-Mn-Al-based shape memory alloys.However,it takes a long time to prepare large-size Fe-Mn-Al-based alloy single crystals via the reported cyclic heat treatments.Meanwhile,the long-time cyclic heat treatment at high temperatures leads to the development of defects including oxidation and a decrease in Mn,which would deteriorate superelasticity in the Fe-Mn-Al-based shape memory alloys.To shorten the fabrication time of single crystals,the effect of the cyclic heat treatment process on the abnormal grain growth in the Fe-Mn-Al-based alloys with different Ni contents was systematically investigated.It is found that the abnormal grain growth of Fe-Mn-Al-based alloys was not significantly affected by the Ni contents(within 2.1 at.%-6.2 at.%).In addition,the abnormal grain growth could be promoted by 1-2℃ min^(-1) cooling rate,high solution temperature,and multiple cycles,while it was insensitive to other processes including heating rate,dual-phase time as well as long-time solution treat-ment.These findings can guide optimizing the fabrication process of single crystals by cyclic heat treat-ment.Finally,the Fe_(41.9)Mn_(37.8)Al_(14.1) Ni_(6.2) single crystal prepared by the optimized cyclic heat treatment showed a recoverable strain of about 4%.
文摘The cyclic semi-solid heat treatment represents a promising technique for improving microstructure and mechanical properties of a wide range of metallic alloys. In the current research the influence of cyclic semi-solid heat treatment on microstructure of Al-18% Si alloy containing 0.8% Fe has been studied. All specimens were heated in an electrically heated resistance furnace with heating rate of 10°C·min-1 to 585°C. For a complete one cycle heat treatment (5 min heating time), samples after 5 min holding at 585°C were cooled to a temperature of 550°C in still air cooling and the samples were taken out immediately for water quenching. It was found that heat treatment cycles should be limited to 3 cycles or less in order to maintain fine grain size and globular structure without agglomeration and coalescence. Cyclic semi-solid heat treatment changes morphology of iron-rich intermetallics phases to be plate-like and fine plate iron-rich intermetallics phases, in stead of needle-like iron-rich intermetallics phases that are observed in as-cast samples. Cyclic heating shows a relatively higher hardness for all heating cycles compared with as-cast one due to its finer and globular structure. Cyclic semi-solid heat treatment technique results in lower coarsening rate constant compared with isothermal heat treatment one due to coarsening discontinuous effect.
基金This work was financially supported by the funds of Jiangsu ScienceTechnology Department(JH03-013,JHjd03-008).
文摘The effect of cryogenic and heating treatment on the solution properties of rigid polymer nitrocellulose(NC)indilute tetrahydrofuran solution were studied with a sealed viscometer and a size exclusion chromatograph(SEC),respectively.The experimental results show that the relative viscosity of NC solution decreases after repeated freezing-thawing treatment.The decreased viscosity value of NC could not be restored but decreased further after the solution beingre-heated.The experimental results of SEC are fully consistent with that of viscosity measurements.It is believed that theeffect of two treatments on NC solution both causes the apparent hydrodynamic volume to decrease.But they are assumed tobe ascribed to different mechanisms.
文摘The effects of different treatments, such as dry heat,wet heat, solvent vapor and ultrasonic, on properties of the cyclic oligomers on the surface of polyester fiber are studied. The components of surface oligomers are analyzed through Thin-Layer Chromatograph. The result shows that: all of the treatments, especially solvent vapor treatment, can significantly increase the content of surface cyclic oligomers. The content of cyclic trimer is increased more considerably than other oligomers. Moreover, the morphology and the distribution of surface cyclic oligomers are also different from different treatments: Dry heat and wet heat cause larger polygonal solids distributed evenly on the surface of fiber; solvent vapor makes fiber surface exhibit irregular rodlike crystal shapes randomly; ultrasonic treatment induces some obscure and smaller deposits on the surface of fiber.