The friction and wear properties,as well as the scuffing resistance,of different piston-ring coatings mating with a chrome-plated cylinder liner were investigated.Interrupted wear tests under the lubricant starvation ...The friction and wear properties,as well as the scuffing resistance,of different piston-ring coatings mating with a chrome-plated cylinder liner were investigated.Interrupted wear tests under the lubricant starvation condition were conducted to examine the wear behavior of Cr-diamond coating(GDC)and diamond-like coating(DLC).The results indicated that the DLC coating had outstanding tribological properties(small coefficient of friction and wear loss)at 150°C,while the GDC coating exhibited better performance at an elevated temperature(240°C).The DLC coating had a better scuffing resistance;no material adhesion occurred for 70 min under the unlubricated condition.The interrupted wear behaviors revealed that the scuffing process of the GDC coating involved the consumption of lubricant oil with relatively stable wear,a reduction in the friction force,and the occurrence of scuffing,in sequence.In contrast,although the friction force also increased after a short period of weak friction,no scuffing was observed.This is attributed to the formation of a mixed oxide and graphitic C tribolayer.展开更多
The cylinder liner is one of the important parts of a diesel engine.Gray cast iron is the main material for manufacturing cylinder liners due to its good casting performance,convenient processing performance,good wear...The cylinder liner is one of the important parts of a diesel engine.Gray cast iron is the main material for manufacturing cylinder liners due to its good casting performance,convenient processing performance,good wear resistance and low cost.In the present work,the effects of vanadium(V)and tin(Sn)on the microstructure and properties of gray cast iron were studied.Results show that increasing the contents of V and Sn can not only refine the graphite,but also reduce the pearlite lamellar space.The graphite size and lamellar spacing of pearlite are firstly reduced and then increased.Pearlite quantity reaches over 98%after adding V and Sn.Adding V and Sn can promote the precipitation and solid solution strengthening of gray cast iron,so as to improve the mechanical properties.The Brinell hardness reaches the peak of 424 HB at the contents of 0.21wt.%V and 0.06wt.%Sn,and the sample containing 0.11wt.%V and 0.08wt.%Sn shows the highest compressive strength and tensile strength of 1,699 MPa and 515 MPa,respectively.The main strengthening mechanism comes from the solid solution strengthening and fine grain strengthening of V and Sn.展开更多
基金This research was supported by the Natural Science Foundation of Liaoning Province(2019-ZD-0165 and 2020-HYLH-47)the China Postdoctoral Science Foundation(2020M670729)the National Natural Science Foundation of China(51979018).
文摘The friction and wear properties,as well as the scuffing resistance,of different piston-ring coatings mating with a chrome-plated cylinder liner were investigated.Interrupted wear tests under the lubricant starvation condition were conducted to examine the wear behavior of Cr-diamond coating(GDC)and diamond-like coating(DLC).The results indicated that the DLC coating had outstanding tribological properties(small coefficient of friction and wear loss)at 150°C,while the GDC coating exhibited better performance at an elevated temperature(240°C).The DLC coating had a better scuffing resistance;no material adhesion occurred for 70 min under the unlubricated condition.The interrupted wear behaviors revealed that the scuffing process of the GDC coating involved the consumption of lubricant oil with relatively stable wear,a reduction in the friction force,and the occurrence of scuffing,in sequence.In contrast,although the friction force also increased after a short period of weak friction,no scuffing was observed.This is attributed to the formation of a mixed oxide and graphitic C tribolayer.
基金the financial support from the Jiangsu Innovation and Entrepreneurship Team Foundationthe National Natural Science Foundation of China (No. 51825401)the Natural Science Foundation of Heilongjiang Province of China (No. LH2020E032)
文摘The cylinder liner is one of the important parts of a diesel engine.Gray cast iron is the main material for manufacturing cylinder liners due to its good casting performance,convenient processing performance,good wear resistance and low cost.In the present work,the effects of vanadium(V)and tin(Sn)on the microstructure and properties of gray cast iron were studied.Results show that increasing the contents of V and Sn can not only refine the graphite,but also reduce the pearlite lamellar space.The graphite size and lamellar spacing of pearlite are firstly reduced and then increased.Pearlite quantity reaches over 98%after adding V and Sn.Adding V and Sn can promote the precipitation and solid solution strengthening of gray cast iron,so as to improve the mechanical properties.The Brinell hardness reaches the peak of 424 HB at the contents of 0.21wt.%V and 0.06wt.%Sn,and the sample containing 0.11wt.%V and 0.08wt.%Sn shows the highest compressive strength and tensile strength of 1,699 MPa and 515 MPa,respectively.The main strengthening mechanism comes from the solid solution strengthening and fine grain strengthening of V and Sn.