The Shima yield criterion used in finite element analysis for nickel-based superalloy powder compact during hot isostatic pressing(HIP) was modified through uniaxial compression experiments. The influence of cylindric...The Shima yield criterion used in finite element analysis for nickel-based superalloy powder compact during hot isostatic pressing(HIP) was modified through uniaxial compression experiments. The influence of cylindrical capsule characteristics on FGH4096M superalloy powder compact deformation and densification behavior during HIP was investigated through simulations and experiments. Results revealed the simulation shrinkage prediction fitted well with the experimental shrinkage including a maximum shrinkage error of 1.5%. It was shown that the axial shrinkage was 1.7% higher than radial shrinkage for a cylindrical capsule with the size of ∮50 mm × 100 mm due to the force arm difference along the axial and radial direction of the capsule. The stress deviated from the isostatic state in the capsule led to the uneven shrinkage and non-uniform densification of the powder compact. The ratio of the maximum radial displacement to axial displacement increased from0.47 to 0.75 with the capsule thickness increasing from 2 to 4 mm. The pressure transmission is related to the capsule thickness, the capsule material performance, and physical parameters in the HIP process.展开更多
The intergranular microcracking in polycrystalline Ni-rich cathode particle is led by anisotropic volume change and stress corrosion along grain boundary,accelerating battery performance decay.Herein,we have suggested...The intergranular microcracking in polycrystalline Ni-rich cathode particle is led by anisotropic volume change and stress corrosion along grain boundary,accelerating battery performance decay.Herein,we have suggested a simple but advanced solid-state method that ensures both uniform transition metal distribution and single-crystalline morphology for Ni-rich cathode synthesis without sophisticated coprecipitation.Pelletization-assisted mechanical densification(PAMD)process on solid-state precursor mixture enables the dynamic mass transfer through the increased solid-solid contact area which facilitates the grain growth during sintering process,readily forming micro-sized single-crystalline particle.Furthermore,the improved chemical reactivity by a combination of capillary effect and vacancyassisted diffusion provides homogeneous element distribution within each primary particle.As a result,single-crystalline Ni-rich cathode with PAMD process has eliminated a potential evolution of intergranular cracking,thus achieving superior energy retention capability of 85%over 150 cycles compared to polycrystalline Ni-rich particle even after high-pressure calendering process(corresponding to electrode density of~3.6 g cm^(-3))and high cut-off voltage cycling.This work provides a concrete perspective on developing facile synthetic route of micron-sized single-crystalline Ni-rich cathode materials for high energy density lithium-ion batteries(LIBs).展开更多
B_(2)O_(3)-Zn O-SiO_(2)(BZS)glass containing Cu O with excellent acid resistance,wetting properties,and high-temperature sintering density was prepared by high temperature melting method and then applied in copper ter...B_(2)O_(3)-Zn O-SiO_(2)(BZS)glass containing Cu O with excellent acid resistance,wetting properties,and high-temperature sintering density was prepared by high temperature melting method and then applied in copper terminal electrode for multilayer ceramic capacitors(MLCC)applications.The structure and property characterization of B_(2)O_(3)-Zn O-SiO_(2)glass,including X-ray diffraction,FTIR,scanning electron microscopy,high-temperature microscopy,and differential scanning calorimetry,indicated that the addition of CuO improved the glass’s acid resistance and glass-forming ability.The wettability and acid resistance of this glass were found to be excellent when CuO content was 1.50 wt%.Compared to BZS glass,the CuO-added glass exhibited excellent wettability to copper powder and corrosion resistance to the plating solution.The sintered copper electrode films prepared using the glass with CuO addition had better densification and lower sintering temperature of 750℃.Further analysis of the sintering mechanism reveals that the flowability and wettability of the glass significantly impact the sintering densification of the copper terminal electrodes.展开更多
Boron carbide(B_(4)C)has excellent high-temperature oxidation resistance,high hardness,low relative density,high melting point and excellent abrasive resistance,which is widely used in fields such as refractories,wear...Boron carbide(B_(4)C)has excellent high-temperature oxidation resistance,high hardness,low relative density,high melting point and excellent abrasive resistance,which is widely used in fields such as refractories,wear-resistant materials and lightweight protective materials.The research progress and application of B_(4)C materials in China and overseas in recent years were summarized.The influences of sintering processes(pressureless sintering,hot-pressing sintering,hot isostatic pressing sintering,spark plasma sintering and microwave sintering)and sintering additives(simple substances,oxides and carbides)on the B_(4)C densification were analyzed.The development of B_(4)C materials was prospected.展开更多
By phenomenological analysis of warm compaction, it is found that, compared with the contribution of particle plastical deformation to densification of powder compact,the particle rearrangement is a dominant densifica...By phenomenological analysis of warm compaction, it is found that, compared with the contribution of particle plastical deformation to densification of powder compact,the particle rearrangement is a dominant densification mechanism for powder warm compaction, and the plastical deformation of particles plays an important role in offering accommodating deformation for particle rearrangement and densifying powder compact at the final stage of pressing.In order to attain density gain as high as possible during warm compaction, six rules for designing warm compacting powder mixtures were proposed in detail.展开更多
The sintered W-15wt.%Cu alloys fabricated by mechanical alloying were re-sintered under pressure to increase the density and improve the properties of these alloys. The pressure was applied vertically along the axis o...The sintered W-15wt.%Cu alloys fabricated by mechanical alloying were re-sintered under pressure to increase the density and improve the properties of these alloys. The pressure was applied vertically along the axis of the sintered sample. Properties such as density, hardness, and bending strength were measured. The microstructures of the sintered bodies were observed. The results showed that the subsequent pressure sintering could increase the density of the sintered W-15wt.%Cu alloys. Their hardness, bending strength, and some other physical properties were also improved by this subsequent densification treatment.展开更多
Compression ratio is significant for cellular structures on energy absorption.In the present work,theoretical formulas to determine the initial densification strain of honeycomb structure were put forward by means of ...Compression ratio is significant for cellular structures on energy absorption.In the present work,theoretical formulas to determine the initial densification strain of honeycomb structure were put forward by means of minimum energy principle.Detailed densification strain points were identified,with full fold model for kinds of specimens.To validate,corresponding numerical simulations were carried out with explicit finite element method.Excellent agreement in terms of initial densification stain point has been observed between the theoretical calculation and numerical simulation.The results show that:(1) different honeycomb structure has different initial densification strain point,and its geometric configuration of cells plays an evident role on densification;(2)half-wave length of the wrinkle of honeycomb in folding process significantly influences on the densification strain point;(3) the initial densification point is an decreasing power function of the ratio of foil thickness to cell length,with the exponent 2/3.These achievements provide important references for design in cellular energy absorption devices.展开更多
FeAl/TiC composites were fabricated by hot pressing blended elemental powders. The effects of Ni-doping on thedensification and mechanical properties of the composites were studied. Results show that the density of th...FeAl/TiC composites were fabricated by hot pressing blended elemental powders. The effects of Ni-doping on thedensification and mechanical properties of the composites were studied. Results show that the density of the composites decreases with the content of TiC increasing, and the addition of Ni significantly improves the densificationprocess by enhancing mass transfer in the bonding phase. The mechanical properties of the composites are closelyrelated with their porosity. Besides increasing the density of the composites, the addition of Ni improves the mechanical properties by other three effects: solution-strengthening the bonding phase, strengthening the FeAI-TiC interfaceand increasing ductile fracture in FeAl phase.展开更多
Equivalent yield strength of sintered powder materials is determined by experiments,and the following yield condition is constructed based on it.Experiments on uniaxial compression,and plane strain,closed die upsettin...Equivalent yield strength of sintered powder materials is determined by experiments,and the following yield condition is constructed based on it.Experiments on uniaxial compression,and plane strain,closed die upsetting have been done using sintered copper,and the relation between the deformation resistance and compactness of the prefabricated preform is analysed.A design principle for the prefabricated preform density is proposed,and the effectiveness of shear plastic deformation to densifleation is pointed out.展开更多
The Ti6Al4V alloy castings were produced by the investment casting process, and the hot isostatic pressing(HIP) was used to remove shrinkage from castings. The processing pressure and holding time for HIP were 150 MPa...The Ti6Al4V alloy castings were produced by the investment casting process, and the hot isostatic pressing(HIP) was used to remove shrinkage from castings. The processing pressure and holding time for HIP were 150 MPa and 20 min, respectively. Four different HIP temperatures were tested, including 750 ℃, 850 ℃, 920 ℃ and 950 ℃. To evaluate the effects of temperature on densification and microstructure of Ti6Al4V alloy treated by HIP, non-destructive testing and metallographic observation was performed. The experimental results show that the shrinkage was completely closed at 920 ℃ and 950 ℃. The densification of Ti6Al4V alloy increased as the HIP temperature increased below 920 ℃. The lamel ae were more uniform, the thickness of lamel ae was obviously broadened and the structure was coarsen. Besides, the Norton creep equation was used to simulate the effect of different temperatures on the densification of Ti6Al4V alloy during HIP. The simulation results were in good agreement with the experimental results. It was also found that 920 ℃ is a suitable temperature for HIP for Ti6Al4V alloy.展开更多
We studied the characteristics of two-scale pore structure of preform in the deposition process and the mass transfer of reactant gas in dual-scale pores, and observed the physiochemical phenomenon associated with the...We studied the characteristics of two-scale pore structure of preform in the deposition process and the mass transfer of reactant gas in dual-scale pores, and observed the physiochemical phenomenon associated with the reaction. Thereby, we established mathematical models on two scales, respectively, preform and reactor. These models were used for the numerical simulation of the process of ceramic matrix composites densified by isothermal chemical vapor infiltration(ICVI). The models were used to carry out a systematic study on the influence of process conditions and the preform structure on the densification behaviors. The most important findings of our study are that the processing time could be reduced by about 50% without compromising the quality of the material, if the processing temperature is 950-1 000 ℃ for the first 70 hours and then raised to 1 100 ℃.展开更多
The densification rate of C/C composites fabricated by directional flow thermal gradient chemical vapor infiltration process from C 3H 6, C 3H 6 N 2 and C 3H 6 H 2 was investigated respectively. The mechanism on the r...The densification rate of C/C composites fabricated by directional flow thermal gradient chemical vapor infiltration process from C 3H 6, C 3H 6 N 2 and C 3H 6 H 2 was investigated respectively. The mechanism on the role of carrier gas in chemical vapor infiltration was also discussed. The results shows that whether or not adding N 2 as carrier gas has little influences on the densification behavior of C/C composites with the controlled temperature, the partial pressure of hydrocarbon and the effective residence time of the gas phase remain constant. When the controlled temperature is not less than 1 173 K,using N 2 or H 2 as carrier gas makes pronounced differences in densifying of C/C composites. The average bulk density of C/C composites from C 3H 6 H 2 is eight to ten percent higher than that from C 3H 6 N 2. However, when the controlled temperature is not higher than 1 123 K,the densification rate of C/C composites from C 3H 6 H 2 is much lower than that from C 3H 6 N 2, which implies that effects of carrier gas on densification of C/C composites are closely related to the type of carrier gas and infiltration temperature. At higher temperature, using H 2 as carrier gas is favorable to the densification of C/C composites, while at lower temperature, hydrogen, acting as reactive gas, can inhibit the formation of pyrolytic carbon.展开更多
A high-pressure hot-pressing process was applied to densify a commercial boron carbide-titanium diboride (B4C-TiB2) powder mixture.Nearly fully dense (98.6%) materials were obtained at 1700℃ under a pressure of 100MP...A high-pressure hot-pressing process was applied to densify a commercial boron carbide-titanium diboride (B4C-TiB2) powder mixture.Nearly fully dense (98.6%) materials were obtained at 1700℃ under a pressure of 100MPa.Compared to the sintering temperature required to achieve similar results when a pressure of only 30MPa was applied,the sintering temperature was found to decrease by about 200℃ under pressure of 100 MPa.Analysis of the thermodynamics and microstructure showed that the plastic deformation of the B4C grains induced by high pressure dominated the densification mechanism when high pressure was applied.Furthermore,higher pressure resulted in remarkably improved mechanical properties of the composites,which could be traced back to the generation of stacking faults in the B4C grains and aggregation of TiB2.展开更多
A novel temperature fluctuation synthesis/simultaneous densification process was developed for the preparation of Ti3SiC2 bulk ceramics. In this process. Si is used as an in-situ liquid forming phase and it is favorab...A novel temperature fluctuation synthesis/simultaneous densification process was developed for the preparation of Ti3SiC2 bulk ceramics. In this process. Si is used as an in-situ liquid forming phase and it is favorable for both the solid-liquid synthesis and the densification of Ti3SiC2 rainies. The present work demonstrated that the temperature fluctuation synthesis/simultaneous densification process is one of the most effective and simple methods for the preparation of Ti3SiC2 bulk materials providing relatively low synthesis temperature. short reaction time; and simultaneous synthesis and densification. This work also showed the capability to control the microstructure, e.g., the preferred orientation, of the bulk Ti3SiC2 materials simply by applying the hot pressing pressure at different Stages of the temperature fluctuation process. And textured Ti3SiC2 bulk materials with {002} faces of laminated Ti3SiC2 grains normal to the hot pressing axis were prepared.展开更多
Dense CaAl2Si2O8 ceramics were prepared via a two-step sintering process at temperatures below 1000℃. First, pre-sintered CaAl2Si2O8 powders containing small amounts of other crystal phases were obtained by sintering...Dense CaAl2Si2O8 ceramics were prepared via a two-step sintering process at temperatures below 1000℃. First, pre-sintered CaAl2Si2O8 powders containing small amounts of other crystal phases were obtained by sintering a mixture of calcium hydroxide and kaolin powders at 950℃ for 6 h. Subsequently, the combination of the pre-sintered ceramic powders with MeO'2B203 (Me = Ca, Sr, Ba) flux agents enabled the low-temperature densification sintering of the CaAl2Si2O8 ceramics at 950℃. The sintering behavior and phase formation of the CaAl2Si2O8 ceramics were investigated in terms of the addition of the three MeO·2B2O3 flux agents. Furthermore, alumina and quartz were introduced into the three flux agents to investigate the sintering behaviors, phase evolvements, microstructures, and physical properties of the resulting CaA12Si208 ceramics. The results showed that, because of their low-melting characteristics, the MeO·2B2O3 (Me = Ca, Sr, Ba) flux agents facilitated the formation of the CaAl2Si2O8 ceramics with a dense microstructure via liquid-phase sintering. The addition of alumina and quartz to the flux agents also strongly affected the microstructures, phase formation, and physical properties of the CaA12Si208 ceramics.展开更多
By synthesizing reactive powders via a self-sustaining combustion synthesis, the glycine-nitrate process, the gadolinium-doped celia (GDC) with the chemical formula Ce0.8Gd0.2O1.9 was prepared. The resultant powders...By synthesizing reactive powders via a self-sustaining combustion synthesis, the glycine-nitrate process, the gadolinium-doped celia (GDC) with the chemical formula Ce0.8Gd0.2O1.9 was prepared. The resultant powders were dispersed with the terpineol as the dispersant through different methods such as ball milling and high-shear dispersing. Coagulation factor (CF) was used to mark the degree of agglomeration on the nano-scale GDC in this work. The effect of agglomeration on the densification behavior at different sintering temperatures was investigated. The studies indicated that agglomeration retarded the densification at the sintering stage. The powders with better dispersion exhibited a higher sintered density at the same temperature. After effective dispersion treatment, GDC could be fully densified at the sintering temperature of 1300 ℃. The densification temperature was significantly lower than those reported previously. The high sintering kinetics of the ceramics was obtained based on the agglomeration control.展开更多
The effect of LiF on the densification and mechanical properties of hot-pressed Dy-α-sialon ceramics was studied. Comparatively, without LiF as sintering additive, the pure Dy-α-sialon ceramic should be sintered at ...The effect of LiF on the densification and mechanical properties of hot-pressed Dy-α-sialon ceramics was studied. Comparatively, without LiF as sintering additive, the pure Dy-α-sialon ceramic should be sintered at 1750 ℃. When LiF is used, the sintering temperature of the Dy-α-sialon is greatly lowered to 1500~1650 ℃. Obviously, the addition of LiF has a strong effect on the improvement in densification. Meanwhile, the resultant Dy-α-sialon has no significant changes in the mechanical properties.展开更多
This study introduces a novel method of electric field sintering for preparing NdFeB magnets. NdFeB alloy compacts were all sintered by electric fields for 8 min at 1000~C with different preset heating rates. The char...This study introduces a novel method of electric field sintering for preparing NdFeB magnets. NdFeB alloy compacts were all sintered by electric fields for 8 min at 1000~C with different preset heating rates. The characteristics of electric field sintering and the effects of heating rate on the sintering densification of NdFeB alloys were also studied. It is found that electric field sintering is a new non-pressure rapid sintering method for preparing NdFeB magnets with fine grains at a relatively lower sintering temperature and in a shorter sintering time. Using this method, the sintering temperature and process of the compacts can be controlled accurately. When the preset heating rate in- creasing from 5 to 2000~C/s the densification of NdFeB sintered compacts gradHally improves. As the preset heating rate is 2000C/s, Nd-rich phases are small, dispersed and uniformly distributed in the sintered compact, and the magnet has a better microstructure than that made by conventional vacuum sintering. Also, the maximum energy product of the sintered magnet reaches 95% of conventionally vacuum sintered magnets.展开更多
The densification behavior of a TiAl base alloy prepared by elemental powder metallurgy has been studied. It is found that a densification abnormality occurs at 1 400 ℃, i.e. the compact density decreases with the in...The densification behavior of a TiAl base alloy prepared by elemental powder metallurgy has been studied. It is found that a densification abnormality occurs at 1 400 ℃, i.e. the compact density decreases with the increase of hot pressing temperature. By microstructural observation, including optical microscopy and TEM, it has been concluded that the densification abnormality can be attributed to the different high temperature creep mechanisms induced by microstructure coarsening in the late period of densification.展开更多
Mo is difficult to sinter densely at a relatively low temperature due to its high melting point. In the present paper,by adding different weight contents of Ni and Cu additives, Mo alloys have been densified at 1473 K...Mo is difficult to sinter densely at a relatively low temperature due to its high melting point. In the present paper,by adding different weight contents of Ni and Cu additives, Mo alloys have been densified at 1473 K for an hour byhot-pressing method, and the optimum contents of Cu and Ni additives have been acquired: when the contents of Niand Cu are 3 and 2 wt pct respectively, the relative density of the sample reaches the maximum value. It was foundthat when the Ni-Cu solid solution was added into Mo alloys. the achieved density is higher than the case of Ni andCu additives. The experimental results indicate that, Ni and Cu play different roles in the process of sintering, theNi-Cu solid solution has the same function as Ni and Cu additives in the course of sintering Mo alloys, It shows moreactivating sintering feature for Mo than the Ni and Cu additives.展开更多
基金financially supported by Guangdong Province Key Field R&D Program, China (No. 2019B01 0935001)the National Nature Science Foundation of China (No. 51905192)the Fundamental Research Funds for the Central Universities (No. FRT-TP-20-006A2)
文摘The Shima yield criterion used in finite element analysis for nickel-based superalloy powder compact during hot isostatic pressing(HIP) was modified through uniaxial compression experiments. The influence of cylindrical capsule characteristics on FGH4096M superalloy powder compact deformation and densification behavior during HIP was investigated through simulations and experiments. Results revealed the simulation shrinkage prediction fitted well with the experimental shrinkage including a maximum shrinkage error of 1.5%. It was shown that the axial shrinkage was 1.7% higher than radial shrinkage for a cylindrical capsule with the size of ∮50 mm × 100 mm due to the force arm difference along the axial and radial direction of the capsule. The stress deviated from the isostatic state in the capsule led to the uneven shrinkage and non-uniform densification of the powder compact. The ratio of the maximum radial displacement to axial displacement increased from0.47 to 0.75 with the capsule thickness increasing from 2 to 4 mm. The pressure transmission is related to the capsule thickness, the capsule material performance, and physical parameters in the HIP process.
基金supported by the National Research Foundation of Korea(NRF)grant funded by the Korea government(MEST)(2021R1A2C1095408)supported by Basic Science Research Program through the National Research Foundation of Korea(NRF)funded by the Ministry of Education(2022R1A6A1A03051158)。
文摘The intergranular microcracking in polycrystalline Ni-rich cathode particle is led by anisotropic volume change and stress corrosion along grain boundary,accelerating battery performance decay.Herein,we have suggested a simple but advanced solid-state method that ensures both uniform transition metal distribution and single-crystalline morphology for Ni-rich cathode synthesis without sophisticated coprecipitation.Pelletization-assisted mechanical densification(PAMD)process on solid-state precursor mixture enables the dynamic mass transfer through the increased solid-solid contact area which facilitates the grain growth during sintering process,readily forming micro-sized single-crystalline particle.Furthermore,the improved chemical reactivity by a combination of capillary effect and vacancyassisted diffusion provides homogeneous element distribution within each primary particle.As a result,single-crystalline Ni-rich cathode with PAMD process has eliminated a potential evolution of intergranular cracking,thus achieving superior energy retention capability of 85%over 150 cycles compared to polycrystalline Ni-rich particle even after high-pressure calendering process(corresponding to electrode density of~3.6 g cm^(-3))and high cut-off voltage cycling.This work provides a concrete perspective on developing facile synthetic route of micron-sized single-crystalline Ni-rich cathode materials for high energy density lithium-ion batteries(LIBs).
基金the National Natural Science Foundation of China(Nos.51372179,51772224)the Open Project Foundation of Guangdong Fenghua Advanced Technology(No.FHR-JS-202011024)。
文摘B_(2)O_(3)-Zn O-SiO_(2)(BZS)glass containing Cu O with excellent acid resistance,wetting properties,and high-temperature sintering density was prepared by high temperature melting method and then applied in copper terminal electrode for multilayer ceramic capacitors(MLCC)applications.The structure and property characterization of B_(2)O_(3)-Zn O-SiO_(2)glass,including X-ray diffraction,FTIR,scanning electron microscopy,high-temperature microscopy,and differential scanning calorimetry,indicated that the addition of CuO improved the glass’s acid resistance and glass-forming ability.The wettability and acid resistance of this glass were found to be excellent when CuO content was 1.50 wt%.Compared to BZS glass,the CuO-added glass exhibited excellent wettability to copper powder and corrosion resistance to the plating solution.The sintered copper electrode films prepared using the glass with CuO addition had better densification and lower sintering temperature of 750℃.Further analysis of the sintering mechanism reveals that the flowability and wettability of the glass significantly impact the sintering densification of the copper terminal electrodes.
文摘Boron carbide(B_(4)C)has excellent high-temperature oxidation resistance,high hardness,low relative density,high melting point and excellent abrasive resistance,which is widely used in fields such as refractories,wear-resistant materials and lightweight protective materials.The research progress and application of B_(4)C materials in China and overseas in recent years were summarized.The influences of sintering processes(pressureless sintering,hot-pressing sintering,hot isostatic pressing sintering,spark plasma sintering and microwave sintering)and sintering additives(simple substances,oxides and carbides)on the B_(4)C densification were analyzed.The development of B_(4)C materials was prospected.
文摘By phenomenological analysis of warm compaction, it is found that, compared with the contribution of particle plastical deformation to densification of powder compact,the particle rearrangement is a dominant densification mechanism for powder warm compaction, and the plastical deformation of particles plays an important role in offering accommodating deformation for particle rearrangement and densifying powder compact at the final stage of pressing.In order to attain density gain as high as possible during warm compaction, six rules for designing warm compacting powder mixtures were proposed in detail.
基金This work was financially supported by the National Natural Science Foundation of China (No. 50174007)
文摘The sintered W-15wt.%Cu alloys fabricated by mechanical alloying were re-sintered under pressure to increase the density and improve the properties of these alloys. The pressure was applied vertically along the axis of the sintered sample. Properties such as density, hardness, and bending strength were measured. The microstructures of the sintered bodies were observed. The results showed that the subsequent pressure sintering could increase the density of the sintered W-15wt.%Cu alloys. Their hardness, bending strength, and some other physical properties were also improved by this subsequent densification treatment.
基金Project(51505502)supported by the National Natural Science Foundation of ChinaProject(2015BAG13B01)supported by the National Key Technology Support Program,China+1 种基金Project(ZZYJKT2017-09)supported by the State Key Laboratory of High Performance Complex Manufacturing,ChinaProject supported by the Open End Fund for the Valuable and Precision Instrument of Central Sonth University,China
文摘Compression ratio is significant for cellular structures on energy absorption.In the present work,theoretical formulas to determine the initial densification strain of honeycomb structure were put forward by means of minimum energy principle.Detailed densification strain points were identified,with full fold model for kinds of specimens.To validate,corresponding numerical simulations were carried out with explicit finite element method.Excellent agreement in terms of initial densification stain point has been observed between the theoretical calculation and numerical simulation.The results show that:(1) different honeycomb structure has different initial densification strain point,and its geometric configuration of cells plays an evident role on densification;(2)half-wave length of the wrinkle of honeycomb in folding process significantly influences on the densification strain point;(3) the initial densification point is an decreasing power function of the ratio of foil thickness to cell length,with the exponent 2/3.These achievements provide important references for design in cellular energy absorption devices.
基金This work was supported by Hunan Provincial Natural Science Foundation.
文摘FeAl/TiC composites were fabricated by hot pressing blended elemental powders. The effects of Ni-doping on thedensification and mechanical properties of the composites were studied. Results show that the density of the composites decreases with the content of TiC increasing, and the addition of Ni significantly improves the densificationprocess by enhancing mass transfer in the bonding phase. The mechanical properties of the composites are closelyrelated with their porosity. Besides increasing the density of the composites, the addition of Ni improves the mechanical properties by other three effects: solution-strengthening the bonding phase, strengthening the FeAI-TiC interfaceand increasing ductile fracture in FeAl phase.
文摘Equivalent yield strength of sintered powder materials is determined by experiments,and the following yield condition is constructed based on it.Experiments on uniaxial compression,and plane strain,closed die upsetting have been done using sintered copper,and the relation between the deformation resistance and compactness of the prefabricated preform is analysed.A design principle for the prefabricated preform density is proposed,and the effectiveness of shear plastic deformation to densifleation is pointed out.
基金supported by the National Natural Science Foundation of China(No.51475181)AECC Beijing Institute of Aeronautical Materials
文摘The Ti6Al4V alloy castings were produced by the investment casting process, and the hot isostatic pressing(HIP) was used to remove shrinkage from castings. The processing pressure and holding time for HIP were 150 MPa and 20 min, respectively. Four different HIP temperatures were tested, including 750 ℃, 850 ℃, 920 ℃ and 950 ℃. To evaluate the effects of temperature on densification and microstructure of Ti6Al4V alloy treated by HIP, non-destructive testing and metallographic observation was performed. The experimental results show that the shrinkage was completely closed at 920 ℃ and 950 ℃. The densification of Ti6Al4V alloy increased as the HIP temperature increased below 920 ℃. The lamel ae were more uniform, the thickness of lamel ae was obviously broadened and the structure was coarsen. Besides, the Norton creep equation was used to simulate the effect of different temperatures on the densification of Ti6Al4V alloy during HIP. The simulation results were in good agreement with the experimental results. It was also found that 920 ℃ is a suitable temperature for HIP for Ti6Al4V alloy.
基金Funded by the National Natural Science Foundation of China(No.51472092)
文摘We studied the characteristics of two-scale pore structure of preform in the deposition process and the mass transfer of reactant gas in dual-scale pores, and observed the physiochemical phenomenon associated with the reaction. Thereby, we established mathematical models on two scales, respectively, preform and reactor. These models were used for the numerical simulation of the process of ceramic matrix composites densified by isothermal chemical vapor infiltration(ICVI). The models were used to carry out a systematic study on the influence of process conditions and the preform structure on the densification behaviors. The most important findings of our study are that the processing time could be reduced by about 50% without compromising the quality of the material, if the processing temperature is 950-1 000 ℃ for the first 70 hours and then raised to 1 100 ℃.
文摘The densification rate of C/C composites fabricated by directional flow thermal gradient chemical vapor infiltration process from C 3H 6, C 3H 6 N 2 and C 3H 6 H 2 was investigated respectively. The mechanism on the role of carrier gas in chemical vapor infiltration was also discussed. The results shows that whether or not adding N 2 as carrier gas has little influences on the densification behavior of C/C composites with the controlled temperature, the partial pressure of hydrocarbon and the effective residence time of the gas phase remain constant. When the controlled temperature is not less than 1 173 K,using N 2 or H 2 as carrier gas makes pronounced differences in densifying of C/C composites. The average bulk density of C/C composites from C 3H 6 H 2 is eight to ten percent higher than that from C 3H 6 N 2. However, when the controlled temperature is not higher than 1 123 K,the densification rate of C/C composites from C 3H 6 H 2 is much lower than that from C 3H 6 N 2, which implies that effects of carrier gas on densification of C/C composites are closely related to the type of carrier gas and infiltration temperature. At higher temperature, using H 2 as carrier gas is favorable to the densification of C/C composites, while at lower temperature, hydrogen, acting as reactive gas, can inhibit the formation of pyrolytic carbon.
基金the National Natural Science Foundation of China(51672197)。
文摘A high-pressure hot-pressing process was applied to densify a commercial boron carbide-titanium diboride (B4C-TiB2) powder mixture.Nearly fully dense (98.6%) materials were obtained at 1700℃ under a pressure of 100MPa.Compared to the sintering temperature required to achieve similar results when a pressure of only 30MPa was applied,the sintering temperature was found to decrease by about 200℃ under pressure of 100 MPa.Analysis of the thermodynamics and microstructure showed that the plastic deformation of the B4C grains induced by high pressure dominated the densification mechanism when high pressure was applied.Furthermore,higher pressure resulted in remarkably improved mechanical properties of the composites,which could be traced back to the generation of stacking faults in the B4C grains and aggregation of TiB2.
基金the National Outstanding YOung Scientist Foundation Under Grant !No.59925208 the National Natural Science Foundation of China
文摘A novel temperature fluctuation synthesis/simultaneous densification process was developed for the preparation of Ti3SiC2 bulk ceramics. In this process. Si is used as an in-situ liquid forming phase and it is favorable for both the solid-liquid synthesis and the densification of Ti3SiC2 rainies. The present work demonstrated that the temperature fluctuation synthesis/simultaneous densification process is one of the most effective and simple methods for the preparation of Ti3SiC2 bulk materials providing relatively low synthesis temperature. short reaction time; and simultaneous synthesis and densification. This work also showed the capability to control the microstructure, e.g., the preferred orientation, of the bulk Ti3SiC2 materials simply by applying the hot pressing pressure at different Stages of the temperature fluctuation process. And textured Ti3SiC2 bulk materials with {002} faces of laminated Ti3SiC2 grains normal to the hot pressing axis were prepared.
基金supported by the Fundamental Research Funds for the Central Universities from China Government (Grant No. A0920502051513-5)
文摘Dense CaAl2Si2O8 ceramics were prepared via a two-step sintering process at temperatures below 1000℃. First, pre-sintered CaAl2Si2O8 powders containing small amounts of other crystal phases were obtained by sintering a mixture of calcium hydroxide and kaolin powders at 950℃ for 6 h. Subsequently, the combination of the pre-sintered ceramic powders with MeO'2B203 (Me = Ca, Sr, Ba) flux agents enabled the low-temperature densification sintering of the CaAl2Si2O8 ceramics at 950℃. The sintering behavior and phase formation of the CaAl2Si2O8 ceramics were investigated in terms of the addition of the three MeO·2B2O3 flux agents. Furthermore, alumina and quartz were introduced into the three flux agents to investigate the sintering behaviors, phase evolvements, microstructures, and physical properties of the resulting CaA12Si208 ceramics. The results showed that, because of their low-melting characteristics, the MeO·2B2O3 (Me = Ca, Sr, Ba) flux agents facilitated the formation of the CaAl2Si2O8 ceramics with a dense microstructure via liquid-phase sintering. The addition of alumina and quartz to the flux agents also strongly affected the microstructures, phase formation, and physical properties of the CaA12Si208 ceramics.
基金Project supported by the Key Research Programof the National Natural Science Foundation (90610035)
文摘By synthesizing reactive powders via a self-sustaining combustion synthesis, the glycine-nitrate process, the gadolinium-doped celia (GDC) with the chemical formula Ce0.8Gd0.2O1.9 was prepared. The resultant powders were dispersed with the terpineol as the dispersant through different methods such as ball milling and high-shear dispersing. Coagulation factor (CF) was used to mark the degree of agglomeration on the nano-scale GDC in this work. The effect of agglomeration on the densification behavior at different sintering temperatures was investigated. The studies indicated that agglomeration retarded the densification at the sintering stage. The powders with better dispersion exhibited a higher sintered density at the same temperature. After effective dispersion treatment, GDC could be fully densified at the sintering temperature of 1300 ℃. The densification temperature was significantly lower than those reported previously. The high sintering kinetics of the ceramics was obtained based on the agglomeration control.
文摘The effect of LiF on the densification and mechanical properties of hot-pressed Dy-α-sialon ceramics was studied. Comparatively, without LiF as sintering additive, the pure Dy-α-sialon ceramic should be sintered at 1750 ℃. When LiF is used, the sintering temperature of the Dy-α-sialon is greatly lowered to 1500~1650 ℃. Obviously, the addition of LiF has a strong effect on the improvement in densification. Meanwhile, the resultant Dy-α-sialon has no significant changes in the mechanical properties.
基金the National Natural Science Foundation of China(No.50945018)
文摘This study introduces a novel method of electric field sintering for preparing NdFeB magnets. NdFeB alloy compacts were all sintered by electric fields for 8 min at 1000~C with different preset heating rates. The characteristics of electric field sintering and the effects of heating rate on the sintering densification of NdFeB alloys were also studied. It is found that electric field sintering is a new non-pressure rapid sintering method for preparing NdFeB magnets with fine grains at a relatively lower sintering temperature and in a shorter sintering time. Using this method, the sintering temperature and process of the compacts can be controlled accurately. When the preset heating rate in- creasing from 5 to 2000~C/s the densification of NdFeB sintered compacts gradHally improves. As the preset heating rate is 2000C/s, Nd-rich phases are small, dispersed and uniformly distributed in the sintered compact, and the magnet has a better microstructure than that made by conventional vacuum sintering. Also, the maximum energy product of the sintered magnet reaches 95% of conventionally vacuum sintered magnets.
文摘The densification behavior of a TiAl base alloy prepared by elemental powder metallurgy has been studied. It is found that a densification abnormality occurs at 1 400 ℃, i.e. the compact density decreases with the increase of hot pressing temperature. By microstructural observation, including optical microscopy and TEM, it has been concluded that the densification abnormality can be attributed to the different high temperature creep mechanisms induced by microstructure coarsening in the late period of densification.
基金This research is sponsored by the National Natural Science Foundation of China under grant No.50171049.
文摘Mo is difficult to sinter densely at a relatively low temperature due to its high melting point. In the present paper,by adding different weight contents of Ni and Cu additives, Mo alloys have been densified at 1473 K for an hour byhot-pressing method, and the optimum contents of Cu and Ni additives have been acquired: when the contents of Niand Cu are 3 and 2 wt pct respectively, the relative density of the sample reaches the maximum value. It was foundthat when the Ni-Cu solid solution was added into Mo alloys. the achieved density is higher than the case of Ni andCu additives. The experimental results indicate that, Ni and Cu play different roles in the process of sintering, theNi-Cu solid solution has the same function as Ni and Cu additives in the course of sintering Mo alloys, It shows moreactivating sintering feature for Mo than the Ni and Cu additives.