The Evaluation of the Dietary Habits Influence on the Microhardness of Gingiva-Coloured Composite and Acrylic Denture Base Materials

Purpose: The study investigated the impact of dietary habits, specifically soda, milk kefir, water kefir, almond milk, and distilled water (control) consumption, on the microhardness of gingiva-coloured composite and acrylic denture bases. Methods: Materials included gingiva-coloured composite (Fusion Universal G1), acrylic (Imicryl), and subdivided Procryla group. Subgroups comprised 15 and 30-minute heat polymerized (Pro15, Pro30), and 1 wt% (Pro1Z) and 3 wt% (Pro3Z) zirconium added groups. Immersed in beverages for 1, 7, and 14 days, pH and microhardness were assessed. SEM examined random samples. Statistical analysis used repeated measures ANOVA, and post hoc tests (p Results: The gingiva-coloured composites displayed noteworthy time-associated microhardness changes (p 0.05). Despite variable pH levels in beverages, no substantial group interaction effects were observed (p > 0.05). Initial microhardness rankings shifted after a 14-day immersion. Conclusions: Gingiva-coloured composite exhibited the highest microhardness pre- and post-immersion, followed by Procryla30 and Imicryl groups. .

Evaluation the Vickers Hardness of Denture Base Materials

The aim of this study was to evaluate the Vickers Hardness of four different denture base materials. Four different denture base materials were used in this study: Heat-cured pink acrylic resin, self-cured acrylic resin, heat-cured clear acrylic resin and polyamide denture base materials. To-tally 80 disc shaped samples which 2 mm thickness and 40 mm diameter were prepared. The samples were stored in distilled water after polished. Then, Vickers Hardness test was performed with TMTeck HV-1000B (200 gram at 15 second). The statistically analysis of obtained data was performed with use one-way analysis of variance test. The results showed that the highest Vickers Hardness value (18.57 HV) was identified in heat-cured (pink) acrylic resin, the lowest Vickers Hardness value (9.62 HV) was identified in polyamide denture base materials. The result of one-way analysis of variance test showed that there were statistically very highly significant differences between four denture base materials of Vickers Hardness (p < 0.001). The obtained data presented that the self-cured denture base acrylic resin was the hardnest denture base materials.

Color Changes of Polyamid and Polymetyhl Methacrylate Denture Base Materials

Aim: Both conventional and flexible resins may show color alteration due to intrinsic and extrinsic factors. The aim of this study was to evaluate the color changes of the polyamid and heat polymerized acrylic denture base materials in storage of different staining solutions. Methods: Two denture base materials were used in this study. The speciemens were stored in two staining solutions (tea, coffee), distilled water and denture cleaner. For each group, 14 speciemens (25 × 15 × 2.5 mm) were prepared. The color of speciemens was measured using a colorimeter according to the CIE L*a*b* color scale. The color changes of speciemens were evaluated before and after 7 and 30 days. All data recorded were taken by the same investigator to minimize inconstancy of technique. The data were analyzed statistically by repeated measures analysis of variance and Tukey honestly significant difference multiple comparison tests. It was found no statistically significant difference between solutions (P > 0.05). Results: Polyamid denture base resin displayed the greatest colour change when compared to polymetyhl methacrylate denture base resin (P < 0.001). Polyamid material indicated the highest value (ΔE: 7.28) in coffee solution for 7 days. Significance: The colour stability of polymetyhl methacrylate denture base resin is greater than polyamid denture base resin.

Residual Monomer Content and Its Release into Water from the Denture Base Nanocomposite Using Organic Montmorillonite as Reinforcement

A novel kind of denture base nanocomposite was prepared by polymethyl methyacrylate（PMMA） and cethyltrimethylammonium bromide modified organic montmorillonite （OMMT）. The dispersion of montmorillonite in the polymer matrix was characterized by x-ray diffraction （XRD） and transimission electron microscope （TEM）.The content of residual MMA in nanocomposites and the amount of MMA released to water from nanocomposites were determined by gas chromatography （GC）. The analysis of TEM and XRD showed that exfoliated-intercalated and intercalated nanocomposites were formed when the content of OMMT was 3% and 5% in the PMMA powder respectively. The results of GC showed that the residual MMA increased with the increase of OMMT content in the polymer matrix. After 7 days in water, the amount of MMA released into water from the nanocomposites tended to be stable. The results of one-way ANOVA and t-test showed that OMMT gave a significant increase of residual MMA concentration （p〈0.05） in nanocomposites.

Effects of Chairside Polishing and Brushing on SurfaceRoughness of Acrylic Denture Base Resins

The effects of 3 chairside polishing kits and mechanical brushing on the surface roughness of 3 different acrylic denture base resins were compared. Acrylic denture base resins （auto-polymerizing, heat-polymerizing, injected heat-polymerizing resins） were examined after a tungsten carbide bur, and after chairside polishing using 3 polishing kits and pumice. The specimens were subjected to mechanical brushing using a wear tester to simulate 30 000 strokes of brushing. The surface roughness of the acrylic denture base resin specimens was measured using a contact pro-filometer. After the test, the random polished acrylic resins were evaluated by scanning electron mi-croscopy （SEM） and atomic force microscopy （AFM）. Acrylic denture base resins polished using the 3 types of polishing kits had a smoother surface than those finished with the tungsten carbide bur （p〈0.05）. The surface of the resin polished by a TC cutter exceeded the Ra of 0.2 μm （p〈0.05）. The auto-polymerizing resin showed a significantly higher surface roughness than the heat-polymerizing resin and injected heat-polymerizing resin （p〉0.05）. In the case of polishing step wise, there was almost no change in surface roughness after brushing （p〉0.05）.

Evaluation of Impact Strength and Micro-Hardness of Denture Base Acrylic Resin （PMMA） Part Ⅱ

Poly （methyl methacrylate） is widely used as denture base material. During fabrication of a denture, the physical and mechanical properties are influenced by cure condition. Each cure cycle or fabrication technique is attempts to optimize the properties for a given application. The aim of this study was to compare two types of commercially available denture base materials （heat-cure and self-cure） in their mechanical properties. The samples were prepared according to the daily routine work for sample preparation in dental laboratories. After reaching dough stage the mix packed into dumbbell shaped of stainless steel mould and pressed in a hydraulic bench press for 25 mins at room temperature. For heat cure the polymerization cycle was carried out using water bath, while self cure was done at room temperature. The impact strength was evaluated using Charpy impact test. The hardness test was conducted using a calibrated Vickers hardness tester machine. The lowest impact strength was observed in self-cure denture base material （self cure material 6.2 kJ/m^2 while heat cure 12.69 kJ/m^2. It appears that the tendency of heat cure to fracture was lower than self-cure denture base materials. Heat cure denture base material has significantly higher hardness test values than self-cure denture base material. The observed VHN value of the heat-cure was 20.09 g/mm^2 while the self-cure value was 12.7 g/mm^2. This is may be due to the plasticizer effect of residual monomer which was higher in self curing material as reported in previous work. Generally, the heat cure material showed better properties compared to self cure material.

Evaluation of Fracture Resistance for Autopolymerizing Acrylic Resin Materials Reinforced with Glass Fiber Mesh, Metal Mesh and Metal Wire Materials: An in Vitro Study

Statement of problem: Many processes have been applied to improve the fracture resistance of acrylic resin dentures by reinforcing them. The maximum goal of any denture repair is to restore the main strength of the denture and to avoid further fracture. Purpose: This study investigated the ability of self-curing acrylic resin to be strength and deflection of repaired acrylic resin joints reinforced with various reinforcement materials to resist fracture. Material and methods: Transverse strength of polymethyl methacrylate acrylic resin reinforced with glass fiber mesh, metal mesh, and metal wire was evaluated with a 3-point load test on 40 intact specimens (n = 10 for control group) (n = 10 per each reinforcement material group). Fractured joint margins were rounded, a 4-mm gap was placed between them, and then they were repaired with autopolymerizing acrylic resin and retested. Results: Transverse strength for the polymethyl methacrylate acrylic resin samples has showed fracture at the side of sample rather than in the middle area of reinforcement materials and some other samples showed bending statue rather than fracture. Conclusion: Reinforcement with glass fiber mesh, metal mesh, and metal wire produced transverse strength in the side area of resin denture base material rather than in the middle of reinforcement area with bending samples rather than fracture response.