The use of nanostructured composites as catalyst supports is a promising route to prepare catalysts with high selectivity and productivity. In this work, reduced graphene oxide-TiO_2(rGP-x) composites with a variation...The use of nanostructured composites as catalyst supports is a promising route to prepare catalysts with high selectivity and productivity. In this work, reduced graphene oxide-TiO_2(rGP-x) composites with a variation of reduced graphene oxide(rGO) content were synthesized by hydrothermal method. Pd/rGP-x catalysts were prepared in incipient-wetness impregnation method for the direct synthesis of H_2O_2 from H2 and O_2. The morphology and electronic properties of catalysts were investigated by XPS, TEM, and Raman spectroscopy.The ratio of Pd^(2+)/Pd^0 and the hydrophobicity of the catalysts were increased with the rising content of rGO. As the amount of rGO in the catalysts varied in the range of 0.025 wt%–2 wt%, the selectivity of H_2O_2 exhibited a tendency of increasing firstly and then decreasing from 0.1 wt% to 2 wt%. It indicates that good catalytic performance for H_2O_2 synthesis can be achieved only when appropriate amount of rGO is introduced. The H_2O_2 selectivity and productivity of Pd/r GP-0.025 both improved remarkably compared with Pd/P25. This enhancement originated from the combined effects of the proper ratio of Pd^(2+)/Pd^0 and hydrophobicity of the catalyst.展开更多
基金Supported by the National Key Basic Research Program of China(2013CB733505,2013CB733501)the National Natural Science Foundation of China(91334202)+2 种基金the Natural Science Foundation of Jiangsu Province of China(BK2012421,BK20130062)the Research Fund for the Doctoral Program of Higher Education of China(20123221120015)the Project for Priority Academic Program Development of Jiangsu Higher Education Institutions(PAPD)
文摘The use of nanostructured composites as catalyst supports is a promising route to prepare catalysts with high selectivity and productivity. In this work, reduced graphene oxide-TiO_2(rGP-x) composites with a variation of reduced graphene oxide(rGO) content were synthesized by hydrothermal method. Pd/rGP-x catalysts were prepared in incipient-wetness impregnation method for the direct synthesis of H_2O_2 from H2 and O_2. The morphology and electronic properties of catalysts were investigated by XPS, TEM, and Raman spectroscopy.The ratio of Pd^(2+)/Pd^0 and the hydrophobicity of the catalysts were increased with the rising content of rGO. As the amount of rGO in the catalysts varied in the range of 0.025 wt%–2 wt%, the selectivity of H_2O_2 exhibited a tendency of increasing firstly and then decreasing from 0.1 wt% to 2 wt%. It indicates that good catalytic performance for H_2O_2 synthesis can be achieved only when appropriate amount of rGO is introduced. The H_2O_2 selectivity and productivity of Pd/r GP-0.025 both improved remarkably compared with Pd/P25. This enhancement originated from the combined effects of the proper ratio of Pd^(2+)/Pd^0 and hydrophobicity of the catalyst.