Ce-doped nanosized ZnO desulfurizer was prepared by homogeneous precipitation,and its desulfurization efficiency at ambient temperature was investigated through dynamic experiments.The results showed that the desulfur...Ce-doped nanosized ZnO desulfurizer was prepared by homogeneous precipitation,and its desulfurization efficiency at ambient temperature was investigated through dynamic experiments.The results showed that the desulfurization activity of nanosized Ce-ZnO had improved greatly,compared to nanosized ZnO desulfurizer.Nanosized Ce-ZnO desulfurizer was characterized by XRD,TPD-MS,XPS,and TEM.The research results indicated that doping Ce decreased the particle size of the nanosized ZnO desulfurizer and ZnS was the principal desulfurization product.There were adsorption complexes of HS and S on the surface of desulfurizer as well.Only a small amount of vapor appeared in the tail gas on the condition of meeting the precision of desulfurization.展开更多
The compound nano-ZnO modified with Ce was prepared by homogeneous precipitation.IR,XRD and dynamic experiments show that the crystal size of nano-ZnO desulfurizer is decreased after being modified with Ce and its des...The compound nano-ZnO modified with Ce was prepared by homogeneous precipitation.IR,XRD and dynamic experiments show that the crystal size of nano-ZnO desulfurizer is decreased after being modified with Ce and its desulfurization activities are improved greatly.When calcined at 270 ℃,Ce distributes evenly on the ZnO particle surface as amorphous state oxides,and the amorphous ZnO·H2O also exists;when the calcining temperature is 570 ℃,the crystal CeO2 separates out and the amorphous structure of zinc oxide disappears,at the same time,the crystal is perfect and its size increases,but the desulfurization activities decrease.The desulfurization product of nano-ZnO modified with Ce was analyzed with XPS.The results show that the adsorption compound of HS,S and ZnS exists on the surface of the desulfurizer.展开更多
基金Project supported by the National Natural Science Foundation of China(50478026)
文摘Ce-doped nanosized ZnO desulfurizer was prepared by homogeneous precipitation,and its desulfurization efficiency at ambient temperature was investigated through dynamic experiments.The results showed that the desulfurization activity of nanosized Ce-ZnO had improved greatly,compared to nanosized ZnO desulfurizer.Nanosized Ce-ZnO desulfurizer was characterized by XRD,TPD-MS,XPS,and TEM.The research results indicated that doping Ce decreased the particle size of the nanosized ZnO desulfurizer and ZnS was the principal desulfurization product.There were adsorption complexes of HS and S on the surface of desulfurizer as well.Only a small amount of vapor appeared in the tail gas on the condition of meeting the precision of desulfurization.
基金the National Natural Science Foundation of China(Grant No.50478026)the Science Foundation for Young Scientists of Harbin University of Science and Technology(Grant No.2008XQJZ039)
文摘The compound nano-ZnO modified with Ce was prepared by homogeneous precipitation.IR,XRD and dynamic experiments show that the crystal size of nano-ZnO desulfurizer is decreased after being modified with Ce and its desulfurization activities are improved greatly.When calcined at 270 ℃,Ce distributes evenly on the ZnO particle surface as amorphous state oxides,and the amorphous ZnO·H2O also exists;when the calcining temperature is 570 ℃,the crystal CeO2 separates out and the amorphous structure of zinc oxide disappears,at the same time,the crystal is perfect and its size increases,but the desulfurization activities decrease.The desulfurization product of nano-ZnO modified with Ce was analyzed with XPS.The results show that the adsorption compound of HS,S and ZnS exists on the surface of the desulfurizer.