The temperature change of the die surface in practical aluminum alloy die casting process was analyzed,and a 2D model was formulated on the basis of a deep concave round cavity without sliding core to analyze thestres...The temperature change of the die surface in practical aluminum alloy die casting process was analyzed,and a 2D model was formulated on the basis of a deep concave round cavity without sliding core to analyze thestress distributions along the die surface in detail. Equipment was designed to test the thermal state of the die steelin different thermal loading conditions. The results of stress analysis showed that, the value of thermal stress (maximum1.5 GPa) caused in the die filling and die spraying stages was larger than the mechanical stress (maximum 85 MPa)caused in the die locking stage. The results of the thermal check experiment showed that there were three stages ofdie dissolving, and that the stress distribution shown by the samples' cracking routine was close to the die surfacestress analysis.展开更多
In this study, the Solidworks was used as pre-processor, which performed the three- dimensional solid construction and automatic enmeshment. The COSMOS was adopted as post- processor to display the temperature distrib...In this study, the Solidworks was used as pre-processor, which performed the three- dimensional solid construction and automatic enmeshment. The COSMOS was adopted as post- processor to display the temperature distribution and further to simulate the thermal stress distribution of dies. A software package for three-dimensional temperature fields of complicated die casting and its dies was developed and the temperature distributions of a fan cover casting were simulated by the software.展开更多
基金Shandong Postdoctoral Innovation Special Fund (No. 200703073)
文摘The temperature change of the die surface in practical aluminum alloy die casting process was analyzed,and a 2D model was formulated on the basis of a deep concave round cavity without sliding core to analyze thestress distributions along the die surface in detail. Equipment was designed to test the thermal state of the die steelin different thermal loading conditions. The results of stress analysis showed that, the value of thermal stress (maximum1.5 GPa) caused in the die filling and die spraying stages was larger than the mechanical stress (maximum 85 MPa)caused in the die locking stage. The results of the thermal check experiment showed that there were three stages ofdie dissolving, and that the stress distribution shown by the samples' cracking routine was close to the die surfacestress analysis.
文摘In this study, the Solidworks was used as pre-processor, which performed the three- dimensional solid construction and automatic enmeshment. The COSMOS was adopted as post- processor to display the temperature distribution and further to simulate the thermal stress distribution of dies. A software package for three-dimensional temperature fields of complicated die casting and its dies was developed and the temperature distributions of a fan cover casting were simulated by the software.