（Ba（0.6） Sr（0.4））（0.85） Bi（0.1） TiO3 ceramics doped with x wt%CaZrO3（x= 0-10） were synthesized by solid-state reaction method. The effects of CaZrO3 amount on the dielectric properties and structure of（Ba...（Ba（0.6） Sr（0.4））（0.85） Bi（0.1） TiO3 ceramics doped with x wt%CaZrO3（x= 0-10） were synthesized by solid-state reaction method. The effects of CaZrO3 amount on the dielectric properties and structure of（Ba（0.6）Sr（0.4））（0.85） Bi（0.1） TiO3 ceramics were investigated. X-ray diffraction results indicated a pure cubic perovskite structure for all samples and that the lattice parameter increased till x=5 and then slightly decreased. A homogenous microstructure was observed with the addition of CaZrO3. Dielectric measurements revealed a relaxor-like characteristic for all samples and that the diffusivity γ reached the maximum value of 1.78 at x=5. With the addition of CaZrO3, the dielectric constant dependence on electric field was weakened, insulation resistivity enhanced and dielectric breakdown strength improved obviously and reached 19.9 k V/mm at x=7.5. In virtue of low dielectric loss（tan d〈0.001 5）, moderate dielectric constant（er 〉1 500） and high breakdown strength（Eb 〉17.5 k V/mm）, the CaZrO3 doped（Ba（0.6）Sr（0.4））0.85 Bi（0.1） TiO3 ceramic is a potential candidate material for high power electric applications.展开更多
基金Funded by the National Natural Science Foundation of China(No.51302093)the Fundamental Research Funds for the Central Universities of China(Nos.2014TS046,2015MS017)
文摘（Ba（0.6） Sr（0.4））（0.85） Bi（0.1） TiO3 ceramics doped with x wt%CaZrO3（x= 0-10） were synthesized by solid-state reaction method. The effects of CaZrO3 amount on the dielectric properties and structure of（Ba（0.6）Sr（0.4））（0.85） Bi（0.1） TiO3 ceramics were investigated. X-ray diffraction results indicated a pure cubic perovskite structure for all samples and that the lattice parameter increased till x=5 and then slightly decreased. A homogenous microstructure was observed with the addition of CaZrO3. Dielectric measurements revealed a relaxor-like characteristic for all samples and that the diffusivity γ reached the maximum value of 1.78 at x=5. With the addition of CaZrO3, the dielectric constant dependence on electric field was weakened, insulation resistivity enhanced and dielectric breakdown strength improved obviously and reached 19.9 k V/mm at x=7.5. In virtue of low dielectric loss（tan d〈0.001 5）, moderate dielectric constant（er 〉1 500） and high breakdown strength（Eb 〉17.5 k V/mm）, the CaZrO3 doped（Ba（0.6）Sr（0.4））0.85 Bi（0.1） TiO3 ceramic is a potential candidate material for high power electric applications.