The dissolution kinetics of Al_(2)O_(3) in CaO-Al_(2)O_(3) SiOslags was studied using a high-temperature confocal scanning laser microscope at 1773 to 1873 K.The results show that the controlling step during the Al_(2...The dissolution kinetics of Al_(2)O_(3) in CaO-Al_(2)O_(3) SiOslags was studied using a high-temperature confocal scanning laser microscope at 1773 to 1873 K.The results show that the controlling step during the Al_(2)O_(3) dissolution was the diffusionin molten slag.It was found that the dissolution curves of Al_(2)O_(3) particles were hardly agreed with the traditional boundary layer diffusion model with the increase of the CaO/Al_(2)O_(3) ratio of slag.A modified diffusion equation considering slag viscosity was developed to study the dissolution mechanism of Al_(2)O_(3) in slag.Diffusion coefficients of Al_(2)O_(3) in slag were calculated as 2.8×10to 4.1×10m~2/s at the temperature of 1773-1873 K.The dissolution rate of Al_(2)O_(3) increased with higher temperature,CaO/Al_(2)O_(3),and particle size.A new model was shown to be v_(Al_(2)O_(3))=0.16×r_(0)^(1.58)×x^(3.52)×(T-T_(mp))^(1.11)to predict the dissolution rate and the total dissolution time of Al_(2)O_(3) inclusions with various sizes,where vAl_(2)O_(3) is the dissolution rate of Al_(2)O_(3) in volume,μm^(3)/s;x is the value of CaO/Al_(2)O_(3) mass ratio;R_(0) is the initial radius of Al_(2)O_(3),μm;T is the temperature,K;T_(mp) is the melting point of slag,K.展开更多
The dissolution kinetics of calcined ulexite in ammonium chloride solutions at high solid-to-liquid ratios were investigated. In the experiments, calcination temperature, solution concentration, reaction temperature, ...The dissolution kinetics of calcined ulexite in ammonium chloride solutions at high solid-to-liquid ratios were investigated. In the experiments, calcination temperature, solution concentration, reaction temperature, and pre-hydration were chosen as parameters. It was observed that the dissolution rate increased with increasing calcination temperature, solution concentration, and reaction temperature, whereas it was not affected by pre-hydration. Employing graphical and statistic methods, the dissolution rate, based on homogeneous reaction model, can be given as: (1-X(B2O3))-1-1= k(c(NH4Cl))1.982t. The activation energy for the dissolution of the ulexite sample calcined at 160 ℃ was found to be 84.04 kJ·mol-1.展开更多
The dissolution kinetics of gold and silver cyanidation of Cu-Au sulfide concentrate has been investigated at ambient temperature in consideration of effects of various parameters,such as particle size of ores,hydrody...The dissolution kinetics of gold and silver cyanidation of Cu-Au sulfide concentrate has been investigated at ambient temperature in consideration of effects of various parameters,such as particle size of ores,hydrodyna.mics of the process and initial cyanide concentration as well as oxygen partial pressure.The experimental data are mathematically treated with an approach based on the shrinking core model.A phenomenological expression describing the rate and rate constants for cyanidation of the concentrate is developed from the treatment.The dissolution of gold and silver is explained by an electrochemical mechanism in which the rate determining step is,the diffusion of cyanide and dissolved molecular oxygen through a porous layer formed during the minerals dis-solutions.展开更多
In vitro dissolution kinetics of a-tricalcium phosphate (α-TCP) cement and α-TCP cement containing tetracycline Hydrochloride(TTCH) were studied in the present paper. It shows that dissolution process of α-TCP ...In vitro dissolution kinetics of a-tricalcium phosphate (α-TCP) cement and α-TCP cement containing tetracycline Hydrochloride(TTCH) were studied in the present paper. It shows that dissolution process of α-TCP cement and TTCH-loaded α-TCP cement accords with Avrami dissolution kinetics model: x=1-exp(-kt^n), and Avrami constant n is 0.5 and 0.4 respectively, which means dissolution process is diffusion control. Apparent dissolution activation energy of α-TCP cement and TTCH-loaded α-TCP cement is about 9.87 kJ/moland 7.17 kJ/mol respectively. Comparing with α-TCP cement, activation energy and Avrami constant of TTCH-loaded α-TCP cement decrease slightly, but its [Ca^2+] solubility decreases from 40 ppm to 11.5 ppm, which could result from the change of interracial property and morphology of hydrated apatite crystal caused by absorption of TTCH on the apatite.展开更多
Dissolution kinetics of magnesitic-dolomite and magnesite-chrome refractories in secondary steelmaking slags was studied by means of the rotating cylinder method under forced convection. Materials investigated include...Dissolution kinetics of magnesitic-dolomite and magnesite-chrome refractories in secondary steelmaking slags was studied by means of the rotating cylinder method under forced convection. Materials investigated include four magnesitic-dolomite samples(MgO content 40% to 93%)and two magnesite-chrome samples (co-clinkered and semi-rebonded).Synthetic slags simulative of VOD and AOD slags with varying basicity (0.6-2.68) are used.The experiments are carried out in Ar atmosphere at different temperatures (1 600 ℃-1 750 ℃) and revolution speeds (200 r·min^-1 to 500 r·min^-1).The microstructure of specimens (before and after slag tests) are studied by optical microscopy, SEM and EPMA. Based on our experimental results the mechanism and kinetics of the dissolution process are discussed.展开更多
The selective dissolution of V and Fe from spent denitrification catalyst(SDC)with oxalic acid was investigated to minimise their environmental effects.The dissolution kinetics of different elements from SDC by using ...The selective dissolution of V and Fe from spent denitrification catalyst(SDC)with oxalic acid was investigated to minimise their environmental effects.The dissolution kinetics of different elements from SDC by using 0.1–1.5 mol L^(-1) oxalic acid concentration was studied at 60℃–90℃.V and Fe were preferentially released(65%and 81%)compared with Al,Ti and W within 5 min due to the redox reactions of oxalic acid.The dissolved fractions of Fe,V,Al,Wand Ti increased with the increase of oxalic acid concentration and reaction temperature.The dissolution kinetic experiments were analysed and controlled diffusion with n<0.5 according to the Avrami dissolve reaction model(R^(2)>0.92).The Arrhenius parameters of the Ea values of Ti,W,V,Fe and Al from SDC with oxalic acid were 30,26,20,19 and 11 kJ mol^(-1),respectively.The obtained Avrami equation of V and Fe was successfully used to predict their leaching behaviour in oxalic acid.Toxicity characteristic leaching procedure revealed that the toxicity risk of Vand Fe metals from SDC after leaching with oxalic acid decreased to below 5 mg kg^(-1) residua.Overall,the leaching residua by oxalic acid indicated its safety for the environment.展开更多
Widespread usage of engineered metallic quantum dots(QDs)within consumer products has evoked a need to assess their fate within environmental systems.QDs are mixed-metal nanocrystals that often include Cd2+which poses...Widespread usage of engineered metallic quantum dots(QDs)within consumer products has evoked a need to assess their fate within environmental systems.QDs are mixed-metal nanocrystals that often include Cd2+which poses a health risk as a nanocrystal or when leached into water.The goal of this work is to study the long-term metal cation leaching behavior and the factors affecting the dissolution processes of mercaptopropionic acid(MPA)capped CdSe/ZnS QDs in aphotic conditions.QD suspensions were prepared in different water conditions,and release of Zn2+and Cd2+cations were monitored over time by size exclusion chromatography-inductively coupled plasm a-mass spectrometry.In most conditions with dissolved 02 present,the ZnS shell degraded fairly rapidly over^1 week,while some of the CdSe core remained up to 80 days.Additional MPA,Zn2+,and Cd2+temporarily delayed dissolution,indicating a moderate role for capping agent detachment and mineral solubility.The presence of H2 O2 and the ligand ethylenediaminetetraacetate accelerated dissolution,while NOM had no kinetic effect.No dissolution of CdSe core was observed when 02 was absent or when QDs formed aggregates at higher concentrations with 02 present.The shrinking particle model with product layer diffusion control best describes Zn2+and Cd2+dissolution kinetics.The longevity of QDs in their nanocrystal form appears to be partly controlled by environmental conditions,with anoxic,aphotic environments preserving the core mineral phase,and oxidants or complexing ligands promoting shell and core mineral dissolution.展开更多
Kinetics of dissolution of silver present in precious metal 26~85℃. Dissolution rate of silver was much faster than scraps in HNO3 was studied in temperature range of that of copper at all temperatures. Effects of p...Kinetics of dissolution of silver present in precious metal 26~85℃. Dissolution rate of silver was much faster than scraps in HNO3 was studied in temperature range of that of copper at all temperatures. Effects of particle size, stirring speed, acid concentration and temperature on the rate of dissolving of silver were evaluated. Dissolution rate decreases with particle size and increases with temperature. Dissolving was accelerated with acid concentrations less than 10 mol/L. Concentrations greater than 10 mol/L resulted in slowing down of the dissolution rate. Shrinking core model with internal diffusion equation t/τ=1-3(1-x)^2/3+2(1-x) could be used to explain the mechanism of the reaction. Silver extraction resulted in activation energies of 33.95 kJ/mol for Ag-Au0.04-Cu0.10 and 68.87 kJ/mol for Ag-Cu0.23 particles. Inter-diffusion of silver and nitrate ions through the porous region of the insoluble alloying layer was the main resistance to the dissolving process. Results were tangible for applications in recycling of the material from electronic silver-bearing scraps, dental alloys, jewelry, silverware and anodic slime precious metal recovery.展开更多
Spinal cord injury(SCI)is a devastating trauma that leaves approximately 10,000 to 20,000 people paralyzed every year in the United States.The majority of these cases are young people that will live to almost a full...Spinal cord injury(SCI)is a devastating trauma that leaves approximately 10,000 to 20,000 people paralyzed every year in the United States.The majority of these cases are young people that will live to almost a full life expectancy,however,their quality of life is significantly reduced.After SCI there is loss of both sensory and motor function below the level of injury.展开更多
Direct observation of the dissolution behavior of nanomaterials could provide fundamental insight to understanding their anisotropic properties and stability. The dissolution mechanism in solution and vacuum has been ...Direct observation of the dissolution behavior of nanomaterials could provide fundamental insight to understanding their anisotropic properties and stability. The dissolution mechanism in solution and vacuum has been well documented. However, the gas-involved dissolution and regrowth have seldom been explored and the mechanisms remain elusive. We report herein, an in situ TEM study of the dissolution and regrowth dynamics of MoO2 nanowires under oxygen using environmental transmission electron microscopy (ETEM). For the first time, oscillatory dissolution on the nanowire tip is revealed, and, intriguingly, simultaneous layer-by-layer regrowth on the sidewall facets is observed, leading to a shorter and wider nanowire. Combined with first-principles calculations, we found that electron beam irradiation caused oxygen loss in the tip facets, which resulted in changing the preferential growth facets and drove the morphology reshaping.展开更多
In the present research, the dissolution mechanism of a Zr rich structure during annealing of a Ni3Al base alloy containing Cr, Mo, Zr and B, was investigated. The annealing treatments were performed up to 50 h at 900...In the present research, the dissolution mechanism of a Zr rich structure during annealing of a Ni3Al base alloy containing Cr, Mo, Zr and B, was investigated. The annealing treatments were performed up to 50 h at 900, 1000 and 1100℃. The alloy used in this investigation was produced by vacuum-arc remelting technique. The results show that at the beginning of the process, a mixed interface reaction and local equilibrium (long range diffusion) mechanism controls the dissolution process. After a short time, this mechanism changes and the dissolution mechanism of the Zr rich structure changes to only long range diffusion of Zr element. According to this mechanism, the activation energy of this process is estimated to be about 143.3 kJ.mol-1. Also the phases that contribute to this structure and the transformations that occur at the final steps of solidification of this alloy were introduced. According to the results, at the final step of solidification, a peritectic type reaction occurs in the form of L+ y→Ni7Zr2 and →-Ni7Zr2 segregates from the melt. Following this transformation, →-Ni7Zr2 eutectic separates from the remaining Zr rich liquid. The solidification process will be terminated by a ternary eutectic reaction in the form of L→y+Ni5Zr+Ni7Zr2.展开更多
In this paper,the research framework for specific structure crystallization modeling has been proposed in which four steps are required in order to investigate the rigorous crystallization modeling by thermodynamics.T...In this paper,the research framework for specific structure crystallization modeling has been proposed in which four steps are required in order to investigate the rigorous crystallization modeling by thermodynamics.The first is the activity coefficient model of the solution,the second is Solid-Liquid equilibrium,the third and fourth are the dissolution and crystallization kinetics modeling,respectively.Our investigations show that the mechanisms of complex structure formation and microphase transition can be analyzed by combining the dissolution and crystallization kinetics modeling.Moreover,the formation mechanism of the porous KCl has been analyzed,which may provide a reference for the porous structure formation in the advanced material synthesis.展开更多
Surface nanobubbles are spontaneously formed at the interface between hydrophobic surfaces and aqueous solutions,which show extraordinarily longer lifetime than that was predicted by the classical thermodynamics model...Surface nanobubbles are spontaneously formed at the interface between hydrophobic surfaces and aqueous solutions,which show extraordinarily longer lifetime than that was predicted by the classical thermodynamics model.In the present work,by using a surface plasmon resonance microscopy(SPRM)to quantitatively measure the dissolution kinetics of individual surface nanobubbles in real time,we explored the effects of ionic strength and pH value on the dissolution rates(lifetime)of nanobubbles.The results revealed that nanobubbles could exist stably for a long time in low-concentration electrolyte solutions or high-concentration non-electrolyte solutions,while they dissolved quickly in highconcentration electrolyte solutions.With the increase of ionic strength,the dissolution rates were accelerated by 2-3 orders of magnitude,and thus the lifespan of these surface nanobubbles was significantly shortened.In addition to ionic strength,it was further found that,with the increase of acidity or alkalinity of the solution,the dissolution rates of the surface nanobubbles were faster than that in neutral solution.These results demonstrated that the interfacial charge enrichment significantly contributed to the extraordinary stability of the surface nanobubbles.展开更多
Nanocrystal formulations have been explored to deliver poorly water-soluble drug molecules.Despite various studies of nanocrystal formulation and delivery,much more understanding needs to be gained into absorption mec...Nanocrystal formulations have been explored to deliver poorly water-soluble drug molecules.Despite various studies of nanocrystal formulation and delivery,much more understanding needs to be gained into absorption mechanisms and kinetics of drug nanocrystals at various levels,ranging from cells to tissues and to the whole body.In this study,nanocrystals of tetrakis(4-hydroxyphenyl)ethylene(THPE)with an aggregation-induced emission(AIE)property was used as a model to explore intracellular absorption mechanism and dissolution kinetics of nanocrystals.Cellular uptake studies were conducted with KB cells and characterized by confocal microscopy,fow cytometry,and quantitative analyses.The results suggested that THPE nanocrystals could be taken up by KB cells directly,as well as in the form of dissolved molecules.The cellular uptake was found to be concentration-and timedependent.In addition,the intracellular THPE also could be exocytosed from cells in forms of dissolved molecules and nanocrystals.Kinetic modeling was conducted to further understand the cellular mechanism of THPE nanocrystals based on frst-order ordinary differential equations(ODEs).By ftting the kinetic model against experimental measurements,it was found that the initial nanocrystal concentration had a great infuence on the dynamic process of dissolution,cellular uptake,and exocytosis of THPE nanocrystals.As the nanocrystal concentration increased in the culture media,dissolution of endocytosed nanocrystals became enhanced,subsequently driving the effux of THPE molecules from cells.展开更多
基金financially supported by the National Nature Science Foundation of China(Nos.U1860206,51725402)the Science and Technology Program of Hebei,China(Nos.20311006D,20591001D)。
文摘The dissolution kinetics of Al_(2)O_(3) in CaO-Al_(2)O_(3) SiOslags was studied using a high-temperature confocal scanning laser microscope at 1773 to 1873 K.The results show that the controlling step during the Al_(2)O_(3) dissolution was the diffusionin molten slag.It was found that the dissolution curves of Al_(2)O_(3) particles were hardly agreed with the traditional boundary layer diffusion model with the increase of the CaO/Al_(2)O_(3) ratio of slag.A modified diffusion equation considering slag viscosity was developed to study the dissolution mechanism of Al_(2)O_(3) in slag.Diffusion coefficients of Al_(2)O_(3) in slag were calculated as 2.8×10to 4.1×10m~2/s at the temperature of 1773-1873 K.The dissolution rate of Al_(2)O_(3) increased with higher temperature,CaO/Al_(2)O_(3),and particle size.A new model was shown to be v_(Al_(2)O_(3))=0.16×r_(0)^(1.58)×x^(3.52)×(T-T_(mp))^(1.11)to predict the dissolution rate and the total dissolution time of Al_(2)O_(3) inclusions with various sizes,where vAl_(2)O_(3) is the dissolution rate of Al_(2)O_(3) in volume,μm^(3)/s;x is the value of CaO/Al_(2)O_(3) mass ratio;R_(0) is the initial radius of Al_(2)O_(3),μm;T is the temperature,K;T_(mp) is the melting point of slag,K.
文摘The dissolution kinetics of calcined ulexite in ammonium chloride solutions at high solid-to-liquid ratios were investigated. In the experiments, calcination temperature, solution concentration, reaction temperature, and pre-hydration were chosen as parameters. It was observed that the dissolution rate increased with increasing calcination temperature, solution concentration, and reaction temperature, whereas it was not affected by pre-hydration. Employing graphical and statistic methods, the dissolution rate, based on homogeneous reaction model, can be given as: (1-X(B2O3))-1-1= k(c(NH4Cl))1.982t. The activation energy for the dissolution of the ulexite sample calcined at 160 ℃ was found to be 84.04 kJ·mol-1.
文摘The dissolution kinetics of gold and silver cyanidation of Cu-Au sulfide concentrate has been investigated at ambient temperature in consideration of effects of various parameters,such as particle size of ores,hydrodyna.mics of the process and initial cyanide concentration as well as oxygen partial pressure.The experimental data are mathematically treated with an approach based on the shrinking core model.A phenomenological expression describing the rate and rate constants for cyanidation of the concentrate is developed from the treatment.The dissolution of gold and silver is explained by an electrochemical mechanism in which the rate determining step is,the diffusion of cyanide and dissolved molecular oxygen through a porous layer formed during the minerals dis-solutions.
基金Supported by the National Natural Science Foundation of China (No.50772045)
文摘In vitro dissolution kinetics of a-tricalcium phosphate (α-TCP) cement and α-TCP cement containing tetracycline Hydrochloride(TTCH) were studied in the present paper. It shows that dissolution process of α-TCP cement and TTCH-loaded α-TCP cement accords with Avrami dissolution kinetics model: x=1-exp(-kt^n), and Avrami constant n is 0.5 and 0.4 respectively, which means dissolution process is diffusion control. Apparent dissolution activation energy of α-TCP cement and TTCH-loaded α-TCP cement is about 9.87 kJ/moland 7.17 kJ/mol respectively. Comparing with α-TCP cement, activation energy and Avrami constant of TTCH-loaded α-TCP cement decrease slightly, but its [Ca^2+] solubility decreases from 40 ppm to 11.5 ppm, which could result from the change of interracial property and morphology of hydrated apatite crystal caused by absorption of TTCH on the apatite.
文摘Dissolution kinetics of magnesitic-dolomite and magnesite-chrome refractories in secondary steelmaking slags was studied by means of the rotating cylinder method under forced convection. Materials investigated include four magnesitic-dolomite samples(MgO content 40% to 93%)and two magnesite-chrome samples (co-clinkered and semi-rebonded).Synthetic slags simulative of VOD and AOD slags with varying basicity (0.6-2.68) are used.The experiments are carried out in Ar atmosphere at different temperatures (1 600 ℃-1 750 ℃) and revolution speeds (200 r·min^-1 to 500 r·min^-1).The microstructure of specimens (before and after slag tests) are studied by optical microscopy, SEM and EPMA. Based on our experimental results the mechanism and kinetics of the dissolution process are discussed.
基金The authors are grateful for the financial support of the National Natural Science Foundation of China(No.51574214).
文摘The selective dissolution of V and Fe from spent denitrification catalyst(SDC)with oxalic acid was investigated to minimise their environmental effects.The dissolution kinetics of different elements from SDC by using 0.1–1.5 mol L^(-1) oxalic acid concentration was studied at 60℃–90℃.V and Fe were preferentially released(65%and 81%)compared with Al,Ti and W within 5 min due to the redox reactions of oxalic acid.The dissolved fractions of Fe,V,Al,Wand Ti increased with the increase of oxalic acid concentration and reaction temperature.The dissolution kinetic experiments were analysed and controlled diffusion with n<0.5 according to the Avrami dissolve reaction model(R^(2)>0.92).The Arrhenius parameters of the Ea values of Ti,W,V,Fe and Al from SDC with oxalic acid were 30,26,20,19 and 11 kJ mol^(-1),respectively.The obtained Avrami equation of V and Fe was successfully used to predict their leaching behaviour in oxalic acid.Toxicity characteristic leaching procedure revealed that the toxicity risk of Vand Fe metals from SDC after leaching with oxalic acid decreased to below 5 mg kg^(-1) residua.Overall,the leaching residua by oxalic acid indicated its safety for the environment.
基金financially supported by the United States National Science Foundation(grant number CBET-1254245)
文摘Widespread usage of engineered metallic quantum dots(QDs)within consumer products has evoked a need to assess their fate within environmental systems.QDs are mixed-metal nanocrystals that often include Cd2+which poses a health risk as a nanocrystal or when leached into water.The goal of this work is to study the long-term metal cation leaching behavior and the factors affecting the dissolution processes of mercaptopropionic acid(MPA)capped CdSe/ZnS QDs in aphotic conditions.QD suspensions were prepared in different water conditions,and release of Zn2+and Cd2+cations were monitored over time by size exclusion chromatography-inductively coupled plasm a-mass spectrometry.In most conditions with dissolved 02 present,the ZnS shell degraded fairly rapidly over^1 week,while some of the CdSe core remained up to 80 days.Additional MPA,Zn2+,and Cd2+temporarily delayed dissolution,indicating a moderate role for capping agent detachment and mineral solubility.The presence of H2 O2 and the ligand ethylenediaminetetraacetate accelerated dissolution,while NOM had no kinetic effect.No dissolution of CdSe core was observed when 02 was absent or when QDs formed aggregates at higher concentrations with 02 present.The shrinking particle model with product layer diffusion control best describes Zn2+and Cd2+dissolution kinetics.The longevity of QDs in their nanocrystal form appears to be partly controlled by environmental conditions,with anoxic,aphotic environments preserving the core mineral phase,and oxidants or complexing ligands promoting shell and core mineral dissolution.
文摘Kinetics of dissolution of silver present in precious metal 26~85℃. Dissolution rate of silver was much faster than scraps in HNO3 was studied in temperature range of that of copper at all temperatures. Effects of particle size, stirring speed, acid concentration and temperature on the rate of dissolving of silver were evaluated. Dissolution rate decreases with particle size and increases with temperature. Dissolving was accelerated with acid concentrations less than 10 mol/L. Concentrations greater than 10 mol/L resulted in slowing down of the dissolution rate. Shrinking core model with internal diffusion equation t/τ=1-3(1-x)^2/3+2(1-x) could be used to explain the mechanism of the reaction. Silver extraction resulted in activation energies of 33.95 kJ/mol for Ag-Au0.04-Cu0.10 and 68.87 kJ/mol for Ag-Cu0.23 particles. Inter-diffusion of silver and nitrate ions through the porous region of the insoluble alloying layer was the main resistance to the dissolving process. Results were tangible for applications in recycling of the material from electronic silver-bearing scraps, dental alloys, jewelry, silverware and anodic slime precious metal recovery.
基金the Bryon Riesch Paralysis Foundation for their generous financial support of this study (#133-PRJ57YV)
文摘Spinal cord injury(SCI)is a devastating trauma that leaves approximately 10,000 to 20,000 people paralyzed every year in the United States.The majority of these cases are young people that will live to almost a full life expectancy,however,their quality of life is significantly reduced.After SCI there is loss of both sensory and motor function below the level of injury.
文摘Direct observation of the dissolution behavior of nanomaterials could provide fundamental insight to understanding their anisotropic properties and stability. The dissolution mechanism in solution and vacuum has been well documented. However, the gas-involved dissolution and regrowth have seldom been explored and the mechanisms remain elusive. We report herein, an in situ TEM study of the dissolution and regrowth dynamics of MoO2 nanowires under oxygen using environmental transmission electron microscopy (ETEM). For the first time, oscillatory dissolution on the nanowire tip is revealed, and, intriguingly, simultaneous layer-by-layer regrowth on the sidewall facets is observed, leading to a shorter and wider nanowire. Combined with first-principles calculations, we found that electron beam irradiation caused oxygen loss in the tip facets, which resulted in changing the preferential growth facets and drove the morphology reshaping.
基金Advanced Material Research Center (AMRC) for providing the alloys,laboratory equipments and financial supports and Iran Aluminum Research Center (IARC) for laboratory equipments
文摘In the present research, the dissolution mechanism of a Zr rich structure during annealing of a Ni3Al base alloy containing Cr, Mo, Zr and B, was investigated. The annealing treatments were performed up to 50 h at 900, 1000 and 1100℃. The alloy used in this investigation was produced by vacuum-arc remelting technique. The results show that at the beginning of the process, a mixed interface reaction and local equilibrium (long range diffusion) mechanism controls the dissolution process. After a short time, this mechanism changes and the dissolution mechanism of the Zr rich structure changes to only long range diffusion of Zr element. According to this mechanism, the activation energy of this process is estimated to be about 143.3 kJ.mol-1. Also the phases that contribute to this structure and the transformations that occur at the final steps of solidification of this alloy were introduced. According to the results, at the final step of solidification, a peritectic type reaction occurs in the form of L+ y→Ni7Zr2 and →-Ni7Zr2 segregates from the melt. Following this transformation, →-Ni7Zr2 eutectic separates from the remaining Zr rich liquid. The solidification process will be terminated by a ternary eutectic reaction in the form of L→y+Ni5Zr+Ni7Zr2.
基金supported by the Chinese National Key Technology Research and Development Program(Grant Nos.2006BAB09B02,2006AA03Z455,and 2006BAE03B7-2)the Chinese National Science Foundation for Outstanding Young Scholars(No.20428606)+4 种基金the Natural Science Foundation of the Jiangsu Higher Education Institutions of China(08KJB530003)the National Natural Science Foundation of China(Grant Nos.20676062,20731160614,20736002,B061101,B060105,20706029,and 20706028)NSFC-RGC(No.20731160614)the Key Science Foundation of Jiangsu Province,China(BK 2004215)Program for Changjiang Scholars and Innovative Research Team in University(No.IRT0732).
文摘In this paper,the research framework for specific structure crystallization modeling has been proposed in which four steps are required in order to investigate the rigorous crystallization modeling by thermodynamics.The first is the activity coefficient model of the solution,the second is Solid-Liquid equilibrium,the third and fourth are the dissolution and crystallization kinetics modeling,respectively.Our investigations show that the mechanisms of complex structure formation and microphase transition can be analyzed by combining the dissolution and crystallization kinetics modeling.Moreover,the formation mechanism of the porous KCl has been analyzed,which may provide a reference for the porous structure formation in the advanced material synthesis.
基金We acknowledge financial support from the National Natural Science Foundation of China(grant Nos.21925403 and 21874070)the Excellent Research Program of Nanjing University(grant No.ZYJH004).
文摘Surface nanobubbles are spontaneously formed at the interface between hydrophobic surfaces and aqueous solutions,which show extraordinarily longer lifetime than that was predicted by the classical thermodynamics model.In the present work,by using a surface plasmon resonance microscopy(SPRM)to quantitatively measure the dissolution kinetics of individual surface nanobubbles in real time,we explored the effects of ionic strength and pH value on the dissolution rates(lifetime)of nanobubbles.The results revealed that nanobubbles could exist stably for a long time in low-concentration electrolyte solutions or high-concentration non-electrolyte solutions,while they dissolved quickly in highconcentration electrolyte solutions.With the increase of ionic strength,the dissolution rates were accelerated by 2-3 orders of magnitude,and thus the lifespan of these surface nanobubbles was significantly shortened.In addition to ionic strength,it was further found that,with the increase of acidity or alkalinity of the solution,the dissolution rates of the surface nanobubbles were faster than that in neutral solution.These results demonstrated that the interfacial charge enrichment significantly contributed to the extraordinary stability of the surface nanobubbles.
基金the financial support by the China Scholarship Council(No.201806995008,China)Key Projects of Chinese Medicine Research of Chongqing Municipal Health Bureau(ZY201701004,China)the Chao Endowment and Purdue Research Foundation for support(USA)。
文摘Nanocrystal formulations have been explored to deliver poorly water-soluble drug molecules.Despite various studies of nanocrystal formulation and delivery,much more understanding needs to be gained into absorption mechanisms and kinetics of drug nanocrystals at various levels,ranging from cells to tissues and to the whole body.In this study,nanocrystals of tetrakis(4-hydroxyphenyl)ethylene(THPE)with an aggregation-induced emission(AIE)property was used as a model to explore intracellular absorption mechanism and dissolution kinetics of nanocrystals.Cellular uptake studies were conducted with KB cells and characterized by confocal microscopy,fow cytometry,and quantitative analyses.The results suggested that THPE nanocrystals could be taken up by KB cells directly,as well as in the form of dissolved molecules.The cellular uptake was found to be concentration-and timedependent.In addition,the intracellular THPE also could be exocytosed from cells in forms of dissolved molecules and nanocrystals.Kinetic modeling was conducted to further understand the cellular mechanism of THPE nanocrystals based on frst-order ordinary differential equations(ODEs).By ftting the kinetic model against experimental measurements,it was found that the initial nanocrystal concentration had a great infuence on the dynamic process of dissolution,cellular uptake,and exocytosis of THPE nanocrystals.As the nanocrystal concentration increased in the culture media,dissolution of endocytosed nanocrystals became enhanced,subsequently driving the effux of THPE molecules from cells.