The nano-sized BaTiO3:La3+ powders were prepared by sol-gel process using butyl phthalate, barium acetate and lanthanum oxide as raw material, and these samples were tested by means of TG-DTA, XRD and SEM. The results...The nano-sized BaTiO3:La3+ powders were prepared by sol-gel process using butyl phthalate, barium acetate and lanthanum oxide as raw material, and these samples were tested by means of TG-DTA, XRD and SEM. The results indicate that with the annealing temperature and the doped concentration rising, the powders' particle sizes will increase and decrease respectively. When annealing temperature is 900℃and doped concentration is 7%, the phase is cubic without other phases, and the particle size of power is 43 .34 nm.展开更多
采用两步固相反应法,制备锆钛酸铅(PZT)纳米粉掺杂的钽酸锶铋(SrBi2Ta2O9,简写为SBT)陶瓷。研究了显微结构和电性能,并与未掺杂的SBT陶瓷进行比较。经测试分析表明:PZT纳米粉掺杂后的SBT陶瓷具有高度的c轴取向,其铁电与介电性能表现出...采用两步固相反应法,制备锆钛酸铅(PZT)纳米粉掺杂的钽酸锶铋(SrBi2Ta2O9,简写为SBT)陶瓷。研究了显微结构和电性能,并与未掺杂的SBT陶瓷进行比较。经测试分析表明:PZT纳米粉掺杂后的SBT陶瓷具有高度的c轴取向,其铁电与介电性能表现出明显的各向异性,其极化强度2Pr可达 21.6?06 C / cm2,矫顽场强Ec为 60.3?03 V / cm。展开更多
文摘The nano-sized BaTiO3:La3+ powders were prepared by sol-gel process using butyl phthalate, barium acetate and lanthanum oxide as raw material, and these samples were tested by means of TG-DTA, XRD and SEM. The results indicate that with the annealing temperature and the doped concentration rising, the powders' particle sizes will increase and decrease respectively. When annealing temperature is 900℃and doped concentration is 7%, the phase is cubic without other phases, and the particle size of power is 43 .34 nm.
文摘采用两步固相反应法,制备锆钛酸铅(PZT)纳米粉掺杂的钽酸锶铋(SrBi2Ta2O9,简写为SBT)陶瓷。研究了显微结构和电性能,并与未掺杂的SBT陶瓷进行比较。经测试分析表明:PZT纳米粉掺杂后的SBT陶瓷具有高度的c轴取向,其铁电与介电性能表现出明显的各向异性,其极化强度2Pr可达 21.6?06 C / cm2,矫顽场强Ec为 60.3?03 V / cm。