AA1060 aluminum foil was rolled from 4 mm to 20 μm by asymmetric rolling without intermediate annealing. The microstructures and textures were investigated. The original coarse grains with an average grain size of 60...AA1060 aluminum foil was rolled from 4 mm to 20 μm by asymmetric rolling without intermediate annealing. The microstructures and textures were investigated. The original coarse grains with an average grain size of 60 μm were refined to fine equiaxed grains with an average grain size of about 500 nm with mainly large grain boundaries. During the rolling, the intensities of copper texture C-{112}<111> and brass texture B-{011}<211> gradually increased, and most crystallites aggregated along the β and τ orientation lines. The orientation intensity reached the maximum value 26 when the foil was rolled to 500 μm, but significantly decreased to 16 when the thickness became 20 μm, and the texture mainly consisted of a rotation cubic texture RC-{100}<011>. With the combined forces including drawing, compressing and shearing, severe plastic deformation was obtained during the asymmetric rolling, promoting dynamic recrystallization at room temperature. Because of a combined force in the deformation zone and shear force along the normal direction, dynamic recrystallization occurs during the asymmetric rolling; therefore, the average grain size is significantly refined. The texture intensity of ultrathin strip first increases, i.e., work hardening, and then decreases mainly because of dynamic recrystallization.展开更多
The effects of rolling driving methods and technical factors on the microstructures and mechanical properties of aluminum foils based on the industrial trials were studied by TEM, tensile test and texture analysis. Th...The effects of rolling driving methods and technical factors on the microstructures and mechanical properties of aluminum foils based on the industrial trials were studied by TEM, tensile test and texture analysis. The results show that there exist obvious dynamic recovery and primary location re crystallization phenomena in the aluminum foils during high speed rolling. Meanwhile the phenomena become more obvious as the rolling speed or the reduction increases, especially in the asymmetrical rolling process with single roller driving, the dynamic primary location recrystallization is more likely to come into being. The effects of the dynamic recovery phenomena and the dynamic primary location recrystallization on the comprehensive final product ratio and the quality of aluminum foils were discussed.展开更多
基金Projects(51374069,U1460107) supported by the National Natural Science Foundation of China
文摘AA1060 aluminum foil was rolled from 4 mm to 20 μm by asymmetric rolling without intermediate annealing. The microstructures and textures were investigated. The original coarse grains with an average grain size of 60 μm were refined to fine equiaxed grains with an average grain size of about 500 nm with mainly large grain boundaries. During the rolling, the intensities of copper texture C-{112}<111> and brass texture B-{011}<211> gradually increased, and most crystallites aggregated along the β and τ orientation lines. The orientation intensity reached the maximum value 26 when the foil was rolled to 500 μm, but significantly decreased to 16 when the thickness became 20 μm, and the texture mainly consisted of a rotation cubic texture RC-{100}<011>. With the combined forces including drawing, compressing and shearing, severe plastic deformation was obtained during the asymmetric rolling, promoting dynamic recrystallization at room temperature. Because of a combined force in the deformation zone and shear force along the normal direction, dynamic recrystallization occurs during the asymmetric rolling; therefore, the average grain size is significantly refined. The texture intensity of ultrathin strip first increases, i.e., work hardening, and then decreases mainly because of dynamic recrystallization.
文摘The effects of rolling driving methods and technical factors on the microstructures and mechanical properties of aluminum foils based on the industrial trials were studied by TEM, tensile test and texture analysis. The results show that there exist obvious dynamic recovery and primary location re crystallization phenomena in the aluminum foils during high speed rolling. Meanwhile the phenomena become more obvious as the rolling speed or the reduction increases, especially in the asymmetrical rolling process with single roller driving, the dynamic primary location recrystallization is more likely to come into being. The effects of the dynamic recovery phenomena and the dynamic primary location recrystallization on the comprehensive final product ratio and the quality of aluminum foils were discussed.