Subsurface macro-inclusions and hooks are detrimental to the surface quality of deep-drawing steel sheets. However, little is known about the relationship between macro-inclusions and hooks. Thus, in this work, two ul...Subsurface macro-inclusions and hooks are detrimental to the surface quality of deep-drawing steel sheets. However, little is known about the relationship between macro-inclusions and hooks. Thus, in this work, two ultralow carbon (ULC) steel slabs and two low carbon (LC) aluminum-killed steel slabs were sampled to study the relationship between hooks and subsurface macro-inclusions, which were detected on the cross-sections of steel samples with an area of 56058 mm2 using an automated scanning electron microscopy/energy-disper-sive X-ray spectroscopy system. Results show that subsurface inclusions larger than 200 μm were almost entrapped by hook structures, whereas the location of other inclusions smaller than 200μm had no obvious dependence on the location of solidified hooks. Furthermore, the number density (ND) of subsurface inclusions larger than 200μm decreased from 0.02 to 0 cm-2 in ULC steel as the mean hook depth decreased from 1.57 to 1.01 mm. Similar trends were also observed in LC steel. In addition, the detected inclusions larger than 200μm were concentrated in the region near the slab center (3/8 width-5/8 width), where hook depths were also larger than those at any other locations. Therefore, minimizing the hook depth is an effective way to reduce inclusion-induced sliver defects in deep-drawing steels.展开更多
Viscoelastic behavior of the non-Hooke deformation of amorphous PET film before yield was investigated in the temperature region 74-80.5 degreesC around the glass transition temperature. The film specimen was drawn to...Viscoelastic behavior of the non-Hooke deformation of amorphous PET film before yield was investigated in the temperature region 74-80.5 degreesC around the glass transition temperature. The film specimen was drawn to yield point followed by unloading to zero stress, then the residual deformation was held constant; while the subsequent evolution of the stress was recorded. An induction period was found in the course of stress evolution followed by a stress step-increase. The induction period decreases with increasing drawing temperature with an activation energy of 1.10 MJ/mol.K, which is attributed to the time needed for the relaxation of rubbery deformation through cooperative internal rotations. At temperatures lower than 74 degreesC, there is no stress increase or the induction period becomes too long to be observed. Thus the nature of anelasticity in the non-Hooke region before yielding is attributed to stress induced rubbery deformation. The experimental results are interpreted in terms of Perez' theological model of a series connected Hooks spring and a Voigt element consisting of a parallel connected elastic spring and a dashpot.展开更多
文摘Subsurface macro-inclusions and hooks are detrimental to the surface quality of deep-drawing steel sheets. However, little is known about the relationship between macro-inclusions and hooks. Thus, in this work, two ultralow carbon (ULC) steel slabs and two low carbon (LC) aluminum-killed steel slabs were sampled to study the relationship between hooks and subsurface macro-inclusions, which were detected on the cross-sections of steel samples with an area of 56058 mm2 using an automated scanning electron microscopy/energy-disper-sive X-ray spectroscopy system. Results show that subsurface inclusions larger than 200 μm were almost entrapped by hook structures, whereas the location of other inclusions smaller than 200μm had no obvious dependence on the location of solidified hooks. Furthermore, the number density (ND) of subsurface inclusions larger than 200μm decreased from 0.02 to 0 cm-2 in ULC steel as the mean hook depth decreased from 1.57 to 1.01 mm. Similar trends were also observed in LC steel. In addition, the detected inclusions larger than 200μm were concentrated in the region near the slab center (3/8 width-5/8 width), where hook depths were also larger than those at any other locations. Therefore, minimizing the hook depth is an effective way to reduce inclusion-induced sliver defects in deep-drawing steels.
基金This work was supported by the National Key Projects for Fundamental Research-"Macromolecular Condensed State", Ministry of Science and Technology, China.
文摘Viscoelastic behavior of the non-Hooke deformation of amorphous PET film before yield was investigated in the temperature region 74-80.5 degreesC around the glass transition temperature. The film specimen was drawn to yield point followed by unloading to zero stress, then the residual deformation was held constant; while the subsequent evolution of the stress was recorded. An induction period was found in the course of stress evolution followed by a stress step-increase. The induction period decreases with increasing drawing temperature with an activation energy of 1.10 MJ/mol.K, which is attributed to the time needed for the relaxation of rubbery deformation through cooperative internal rotations. At temperatures lower than 74 degreesC, there is no stress increase or the induction period becomes too long to be observed. Thus the nature of anelasticity in the non-Hooke region before yielding is attributed to stress induced rubbery deformation. The experimental results are interpreted in terms of Perez' theological model of a series connected Hooks spring and a Voigt element consisting of a parallel connected elastic spring and a dashpot.