Soldering of LD31 aluminum alloys using Sn-Pb solder paste after electric brush plating Ni and Cu coatings was investigated. The technology of electric brush plating Ni and Cu was studied and plating solution was deve...Soldering of LD31 aluminum alloys using Sn-Pb solder paste after electric brush plating Ni and Cu coatings was investigated. The technology of electric brush plating Ni and Cu was studied and plating solution was developed. The microstructure of the coatings, soldered joint and fracture face were analyzed using optic microscopy, SEM and EDX. The shear strength of soldered joint could reach as high as 26.83MPa. The results showed that reliable soldered joint could be obtained at 230℃, the adhesion of coatings and LD31 aluminum alloy substrate was high enough to bear the thermal process in the soldering.展开更多
The Ni-Cr-Mo-Cu multi-element surface alloying with the electric brushplating Ni interlayer on the low carbon steel substrate has been investigated. By theelectrochemical method in 3.5 percent (mass fraction) NaCl sol...The Ni-Cr-Mo-Cu multi-element surface alloying with the electric brushplating Ni interlayer on the low carbon steel substrate has been investigated. By theelectrochemical method in 3.5 percent (mass fraction) NaCl solution, the corrosion resistance of thecomposite alloying layer and single alloying layer is determined. The experimental results showthat the corrosion resistance of the composite alloying layer is obviously better than that of thesingle alloying layer. The structure and composition of passive films formed on the two kinds ofalloyed layers after electrochemical tests in 3.5 percent NaCl solution have been studied usingX-ray photoelectron spectroscopy (XPS). It is concluded that the double glow plasma surface alloyingof low carbon steel with the electric brush plating Ni interlayer is an appropriate technique toenhance the corrosion resistance compared with the single double glow surface alloying.展开更多
In this paper, a new composite surface treatment technology of electric brush plating Ni W alloy and nitrocarburizing composite process of 38CrMoAl steel has been studied .The properties, microstructure and phase com...In this paper, a new composite surface treatment technology of electric brush plating Ni W alloy and nitrocarburizing composite process of 38CrMoAl steel has been studied .The properties, microstructure and phase composition of the surface layer of 38CrMoAl steel are examined by optical microscopy , scanning electron microscope (SEM) and X ray diffraction . The experiment on the wear resistance of surface layer is carried out . The effect of the thickness of electric brush plating of Ni W alloy and the holding time of nitrocarburizing on the properties and the microstructure of surface layer are studied .The results show that good metallurgical bonding is transformed from mechanical bonding in electric brush plating deposits with 38CrMoAl steel; the components of surface deposit microstructure are Ni base phase with less disperse WC,WN particles . The wear resistance of surface layer of 38CrMoAl steel treated by the composite process has increased 8 times compared with that by nitrocarburizing .The optimum electric brush plating thickness is 20 μm , and the optimum holding time of nitrocarburizing is 80 min at 540 ℃ .展开更多
文摘Soldering of LD31 aluminum alloys using Sn-Pb solder paste after electric brush plating Ni and Cu coatings was investigated. The technology of electric brush plating Ni and Cu was studied and plating solution was developed. The microstructure of the coatings, soldered joint and fracture face were analyzed using optic microscopy, SEM and EDX. The shear strength of soldered joint could reach as high as 26.83MPa. The results showed that reliable soldered joint could be obtained at 230℃, the adhesion of coatings and LD31 aluminum alloy substrate was high enough to bear the thermal process in the soldering.
文摘The Ni-Cr-Mo-Cu multi-element surface alloying with the electric brushplating Ni interlayer on the low carbon steel substrate has been investigated. By theelectrochemical method in 3.5 percent (mass fraction) NaCl solution, the corrosion resistance of thecomposite alloying layer and single alloying layer is determined. The experimental results showthat the corrosion resistance of the composite alloying layer is obviously better than that of thesingle alloying layer. The structure and composition of passive films formed on the two kinds ofalloyed layers after electrochemical tests in 3.5 percent NaCl solution have been studied usingX-ray photoelectron spectroscopy (XPS). It is concluded that the double glow plasma surface alloyingof low carbon steel with the electric brush plating Ni interlayer is an appropriate technique toenhance the corrosion resistance compared with the single double glow surface alloying.
文摘In this paper, a new composite surface treatment technology of electric brush plating Ni W alloy and nitrocarburizing composite process of 38CrMoAl steel has been studied .The properties, microstructure and phase composition of the surface layer of 38CrMoAl steel are examined by optical microscopy , scanning electron microscope (SEM) and X ray diffraction . The experiment on the wear resistance of surface layer is carried out . The effect of the thickness of electric brush plating of Ni W alloy and the holding time of nitrocarburizing on the properties and the microstructure of surface layer are studied .The results show that good metallurgical bonding is transformed from mechanical bonding in electric brush plating deposits with 38CrMoAl steel; the components of surface deposit microstructure are Ni base phase with less disperse WC,WN particles . The wear resistance of surface layer of 38CrMoAl steel treated by the composite process has increased 8 times compared with that by nitrocarburizing .The optimum electric brush plating thickness is 20 μm , and the optimum holding time of nitrocarburizing is 80 min at 540 ℃ .