Magnesia zirconia brick containing 11 wt% zirconia was prepared with magnesia and monoclinic zirconia as starting materials in order to replace the chrome-containing materials for Rtt furnace. The corrosion resistance...Magnesia zirconia brick containing 11 wt% zirconia was prepared with magnesia and monoclinic zirconia as starting materials in order to replace the chrome-containing materials for Rtt furnace. The corrosion resistance of magnesia zirconia brick and fused rebonded magnesia chrome brick （short for magnesia chrome brick） to high, and low basicity slag of RH fitrnace was comparatively researched by rotary slag method and their slag resistance mechanisms were analyzed. The results show that： （1） because the reaction layer containing CaZrO3 forms in magnesia zirconia brick, it has better corrosion resistance to high basicity slag than magnesia chrome brick, however, it has worse corrosion resistance to low basicity slag than magnesia chrome brick; （2） ZrO2 in the magnesia zirconia brick can absorb CaO in the slag, which decrea- ses the basicity of slag and inereases the viscosity of slag, so the degree of slag penetration in magnesia zircon.ia brick decreases ; （ 3 ） there is little zirconia in the slag layer of residual nutgnesia zirconia brick;from working face to original brick layer, the residual magnesia zirconia brick shows three layers： obviotasly deteriorative layer, slightly deteriorative layer, and original brick layer, but the residual magnesia chrome brick only shows two layers ： obviously deteriorative layer and original brick layer; the SiO2 content of residual magnesia zirconia brick is the highest in the slightly deteriorative layer, however, the SiO2 content of residual magnesia chrome brick gradually decreases front working face to original brick layer.展开更多
1 Scope This standard specifies the classification, technical requirements, test methods, inspection rules, marking, packing, transportation, and storage of magnesia bricks for glass furnace.
The rapid development of our country' s heavy non-ferrous metallurgical technology and the revolution in new type of heavynon-ferrous metallurgical furnace have imposed more critical demand on the refractory mater...The rapid development of our country' s heavy non-ferrous metallurgical technology and the revolution in new type of heavynon-ferrous metallurgical furnace have imposed more critical demand on the refractory materials ,i.e. high quality and long service life. This paper presents the domestic status of the refractories for flash furnace , briefly describes the wear of the refractory used, andit is considered that the domestic in refractories for flash-furnace can be surely realized.展开更多
Residual MgO-CaO brick after being used in AOD furnace was determined by OM, SEM and EDAX. Corrosion mechanism of MgO-CaO brick as furnace lining was studied. Results show that： The corrosion of MgO- CaO brick is mai...Residual MgO-CaO brick after being used in AOD furnace was determined by OM, SEM and EDAX. Corrosion mechanism of MgO-CaO brick as furnace lining was studied. Results show that： The corrosion of MgO- CaO brick is mainly attributed to the solution and infiltration of silicate liquid phase. Transverse cracks between reacted zone and original zone are parallel to the working face, which is an important factor for deteriorating the corrosion of MgO-CaO bricks.展开更多
Corrosion effect of ladle furnace （LF） refining slag on fired MgO-CaO bricks with about 34% CaO was studied by static crucible method,and corrosion mechanism was analyzed by techniques of scan electron micrograph,en...Corrosion effect of ladle furnace （LF） refining slag on fired MgO-CaO bricks with about 34% CaO was studied by static crucible method,and corrosion mechanism was analyzed by techniques of scan electron micrograph,energy dispersive spectrometer,and X-ray diffraction. The results show that：MgO-CaO bricks exhibit excellent corrosion resistance but poor penetration resistance to LF refining slag; oxidation of （Mg·Fe）O in reaction zone results in volume expansion forming cracks; penetration of 2CaO·Fe2O3 （C2F） from slag to MgO-CaO bricks increases liquid phases which accelerates corrosion of the bricks; a protective layer of 2CaO·SiO2 formed on reaction interface prevents penetration of C2F to the bricks.展开更多
Mobarakeh Steel Company produces 3 million tons of steel annually with eight 180 tons EBT furnaces. Different types of magnesia-carbon refractories have been employed at slagline during last 5 years. In the present st...Mobarakeh Steel Company produces 3 million tons of steel annually with eight 180 tons EBT furnaces. Different types of magnesia-carbon refractories have been employed at slagline during last 5 years. In the present study the wear and corrosion of MgO-C refractories of these furnaces have been studied via post-mortem analysis of used bricks and the observation of operational effects. Laboratory corrosion tests were also arranged to investigate the effect of slag chemistry and the mechanism of chemical corrosion . Characterization of different magnesia-carbon bricks clarified that the crystal size , type and chemistry of magnesia as well as graphite structure have the main influence on corrosion resistance. The CaO: SiO2 ratio in slag also plays a vital role in the wear of slagline refractories. The iron oxide content of slag also has a major role in graphite oxidation. Of metallurgical parameters , the electric power input and the contact time have great influence on refractories life. The results will be discussed with emphasis on particular operational factors in Mobarakeh steel plant.展开更多
文摘Magnesia zirconia brick containing 11 wt% zirconia was prepared with magnesia and monoclinic zirconia as starting materials in order to replace the chrome-containing materials for Rtt furnace. The corrosion resistance of magnesia zirconia brick and fused rebonded magnesia chrome brick （short for magnesia chrome brick） to high, and low basicity slag of RH fitrnace was comparatively researched by rotary slag method and their slag resistance mechanisms were analyzed. The results show that： （1） because the reaction layer containing CaZrO3 forms in magnesia zirconia brick, it has better corrosion resistance to high basicity slag than magnesia chrome brick, however, it has worse corrosion resistance to low basicity slag than magnesia chrome brick; （2） ZrO2 in the magnesia zirconia brick can absorb CaO in the slag, which decrea- ses the basicity of slag and inereases the viscosity of slag, so the degree of slag penetration in magnesia zircon.ia brick decreases ; （ 3 ） there is little zirconia in the slag layer of residual nutgnesia zirconia brick;from working face to original brick layer, the residual magnesia zirconia brick shows three layers： obviotasly deteriorative layer, slightly deteriorative layer, and original brick layer, but the residual magnesia chrome brick only shows two layers ： obviously deteriorative layer and original brick layer; the SiO2 content of residual magnesia zirconia brick is the highest in the slightly deteriorative layer, however, the SiO2 content of residual magnesia chrome brick gradually decreases front working face to original brick layer.
文摘1 Scope This standard specifies the classification, technical requirements, test methods, inspection rules, marking, packing, transportation, and storage of magnesia bricks for glass furnace.
文摘The rapid development of our country' s heavy non-ferrous metallurgical technology and the revolution in new type of heavynon-ferrous metallurgical furnace have imposed more critical demand on the refractory materials ,i.e. high quality and long service life. This paper presents the domestic status of the refractories for flash furnace , briefly describes the wear of the refractory used, andit is considered that the domestic in refractories for flash-furnace can be surely realized.
文摘Residual MgO-CaO brick after being used in AOD furnace was determined by OM, SEM and EDAX. Corrosion mechanism of MgO-CaO brick as furnace lining was studied. Results show that： The corrosion of MgO- CaO brick is mainly attributed to the solution and infiltration of silicate liquid phase. Transverse cracks between reacted zone and original zone are parallel to the working face, which is an important factor for deteriorating the corrosion of MgO-CaO bricks.
文摘Corrosion effect of ladle furnace （LF） refining slag on fired MgO-CaO bricks with about 34% CaO was studied by static crucible method,and corrosion mechanism was analyzed by techniques of scan electron micrograph,energy dispersive spectrometer,and X-ray diffraction. The results show that：MgO-CaO bricks exhibit excellent corrosion resistance but poor penetration resistance to LF refining slag; oxidation of （Mg·Fe）O in reaction zone results in volume expansion forming cracks; penetration of 2CaO·Fe2O3 （C2F） from slag to MgO-CaO bricks increases liquid phases which accelerates corrosion of the bricks; a protective layer of 2CaO·SiO2 formed on reaction interface prevents penetration of C2F to the bricks.
文摘Mobarakeh Steel Company produces 3 million tons of steel annually with eight 180 tons EBT furnaces. Different types of magnesia-carbon refractories have been employed at slagline during last 5 years. In the present study the wear and corrosion of MgO-C refractories of these furnaces have been studied via post-mortem analysis of used bricks and the observation of operational effects. Laboratory corrosion tests were also arranged to investigate the effect of slag chemistry and the mechanism of chemical corrosion . Characterization of different magnesia-carbon bricks clarified that the crystal size , type and chemistry of magnesia as well as graphite structure have the main influence on corrosion resistance. The CaO: SiO2 ratio in slag also plays a vital role in the wear of slagline refractories. The iron oxide content of slag also has a major role in graphite oxidation. Of metallurgical parameters , the electric power input and the contact time have great influence on refractories life. The results will be discussed with emphasis on particular operational factors in Mobarakeh steel plant.