The core-shell structure silicon-resin precursor powders were synthesized through coat-mix process and addition of Al2O3-SiO2-Y2O3 composite additives.A series of porous silicon carbide ceramics were produced after mo...The core-shell structure silicon-resin precursor powders were synthesized through coat-mix process and addition of Al2O3-SiO2-Y2O3 composite additives.A series of porous silicon carbide ceramics were produced after molding,carbonization and sintering.The phase,morphology,porosity,thermal conductivity,thermal expansion coefficient,and thermal shock resistance were analyzed.The results show that porous silicon carbide ceramics can be produced at low temperature.The grain size of porous silicon carbide ceramic is small,and the thermal conductivity is enhanced significantly.Composite additives also improve the thermal shock resistance of porous ceramics.The bending strength loss rate after 30 times of thermal shock test of the porous ceramics which were added Al2O3-SiO2-Y2O3 and sintered at 1 650 ℃ is only 6.5%.Moreover,the pore inside of the sample is smooth,and the pore size distribution is uniform.Composite additives make little effect on the thermal expansion coefficient of the porous silicon carbide ceramics.展开更多
SiC powder was rapidly synthesized in an induction furnace with crystalline silicon cutting waste and active carbon as raw materials,and then SiC porous ceramics were prepared at 1600 t for 4 h with carbon embedded us...SiC powder was rapidly synthesized in an induction furnace with crystalline silicon cutting waste and active carbon as raw materials,and then SiC porous ceramics were prepared at 1600 t for 4 h with carbon embedded using the powder as raw material,the starch and the graphite as pore-forming agents.Effects of additions of different pore-forming agents on the phase composition,microstructures,physical properties,and cold crushing strength of the porous ceramics were investigated.The results show that the main crystalline phases of the synthetic powder areα-S iC(6H-SiC)andβ-SiC(3C-SiC).The phase composition of the porous ceramics includesα-S iC(6H-SiC),β-SiC(3C-SiC),FeSi,quartz and Si2N20.The apparent porosity and closed porosity of the porous ceramics prepared by adding starch are higher,and the cold compressive strength of the porous ceramics added with graphite is higher.As increasing the additions of the starch,the apparent porosity,closed porosity and linear shrinkage ratio of the porous ceramics increase,and the bulk density decreases correspondingly.When 20 mass%starch is added,the apparent porosity,closed porosity,linear shrinkage ratio and cold compressive strength are 57.05%,2.03%,5.10%and 10.20 MPa,respectively.展开更多
SiC porous ceramics were prepared at 1 400 ℃ for4 h with crystalline silicon cutting waste and activated carbon as main starting materials and NH4HCO3 as the pore-forming agent. Effects of NH4HCO3 additions( 0,20%,30...SiC porous ceramics were prepared at 1 400 ℃ for4 h with crystalline silicon cutting waste and activated carbon as main starting materials and NH4HCO3 as the pore-forming agent. Effects of NH4HCO3 additions( 0,20%,30%,40%,by mass) on the phase composition,microstructure,sintering properties,cold compressive strength and thermal shock resistance of as-prepared Si C porous ceramics were investigated. The results show that:( 1) addition of NH4HCO3 remarkably influences the apparent porosity and cold compressive strength of specimens. The apparent porosity achieves its maximum value( 63. 40%) when 40% NH4HCO3 is added,while the minimum cold compressive strength is 4. 77 MPa;( 2) the specimen with 40% NH4HCO3 has the best thermal shock resistance. The thermal cycling times between1 000 ℃ to room temperature reach 62;( 3) the addition of NH4HCO3 does not remarkably affect the phase composition of the specimens;( 4) the specimens include a large number of SiC particles and a small amount of SiC whiskers.展开更多
An innovative approach has been developed to fabricate reticulated porous ceramics (RPCs) with uniform macrostruc-ture by using the polymeric sponge as the templates. In this approach, the coating process comprises of...An innovative approach has been developed to fabricate reticulated porous ceramics (RPCs) with uniform macrostruc-ture by using the polymeric sponge as the templates. In this approach, the coating process comprises of two stages. In the first stage, the thicker slurry was used to coat: uniformly the sponge substrate. The green body was preheated to produce a reticulated preform with enough handling strength after the sponge was burned out. In the second stage, the thinner slurry was used to coat uniformly the preform. The population of the microscopic and macroscopic flaws in the structure is reduced significantly by recoating process. A few filled cells and cell faces occur in the fabrication and the struts were thickened. A statistical evaluation by means of Weibull statistics was carried out on the bend strength data of RPCs, which were prepared by the traditional approach and innovative approach, respectively. The result shows that the mechanical reliability of RPCs is improved by the innovative approach. This innovative approach is very simple and controlled easily, and will open up new technological applications for RPCs.展开更多
In order to fabricate porous ceramics with good properties and proper production cost,SiC-Al2 O3 porous ceramics were prepared at 1 450 ℃ for 2 h from the powders of commercial silicon carbide and white fused corundu...In order to fabricate porous ceramics with good properties and proper production cost,SiC-Al2 O3 porous ceramics were prepared at 1 450 ℃ for 2 h from the powders of commercial silicon carbide and white fused corundum via a polymeric replication method. Effects of the mass ratio of SiC powder to white fused corundum powder（ 1 ∶ 3,1 ∶ 1 and 3 ∶ 1） on the appearance,phase composition,sintering properties and thermal shock resistance were investigated. The research results indicate that the as-prepared Si C-Al2 O3 porous ceramics have uniform pores,and their linear shrinkage ratio,apparent porosity and bulk density reach 4. 70%,67. 17%and 0. 83 g·cm-3,respectively. The thermal shock cycles from 1 400 ℃ to room temperature reach 23 including 15 cycles in air cooling condition and then 8 cycles in water cooling condition. Their main phases areα-Al2 O3 and Al6 Si2 O13 as well as a small amount of SiC and free SiO2. The as-prepared porous ceramic with the ratio of m（ SiC） ∶ m（ Al2 O3） = 1∶ 1 possesses prior comprehensive properties.展开更多
Three strategies were proposed to prolong the service life of continuous fiber-reinforced silicon carbide ceramic matrix composite(CMC-SiC),which served as thermal-structure components of aeroengine at thermo-mechanic...Three strategies were proposed to prolong the service life of continuous fiber-reinforced silicon carbide ceramic matrix composite(CMC-SiC),which served as thermal-structure components of aeroengine at thermo-mechanical-oxygenic coupling environment.As for some thermal-structure components with low working stress,improving the degree of densification was crucial to prolong the service life,and the related process approaches were recited.If the thermal-structure components worked under moderate stress,the matrix cracking stress(σ^(mc))should be improved as far as possible.The fiber preform architecture,interface shear strength,residual thermal stress,and matrix strengthening were associated withσ_(mc)in this review.Introducing self-healing components was quite significant with the appearance of matrix microcracks when CMC-SiC worked at more severe environment for hundreds of hours.The damage can be sealed by glass phase originating from the reaction between self-healing components and oxygen.The effective self-healing temperature range of different self-healing components was first summarized and distinguished.The structure,composition,and preparation process of CMC-SiC should be systematically designed and optimized to achieve long duration target.展开更多
基金Project(50802052)supported by the National Natural Science Foundation of China
文摘The core-shell structure silicon-resin precursor powders were synthesized through coat-mix process and addition of Al2O3-SiO2-Y2O3 composite additives.A series of porous silicon carbide ceramics were produced after molding,carbonization and sintering.The phase,morphology,porosity,thermal conductivity,thermal expansion coefficient,and thermal shock resistance were analyzed.The results show that porous silicon carbide ceramics can be produced at low temperature.The grain size of porous silicon carbide ceramic is small,and the thermal conductivity is enhanced significantly.Composite additives also improve the thermal shock resistance of porous ceramics.The bending strength loss rate after 30 times of thermal shock test of the porous ceramics which were added Al2O3-SiO2-Y2O3 and sintered at 1 650 ℃ is only 6.5%.Moreover,the pore inside of the sample is smooth,and the pore size distribution is uniform.Composite additives make little effect on the thermal expansion coefficient of the porous silicon carbide ceramics.
文摘SiC powder was rapidly synthesized in an induction furnace with crystalline silicon cutting waste and active carbon as raw materials,and then SiC porous ceramics were prepared at 1600 t for 4 h with carbon embedded using the powder as raw material,the starch and the graphite as pore-forming agents.Effects of additions of different pore-forming agents on the phase composition,microstructures,physical properties,and cold crushing strength of the porous ceramics were investigated.The results show that the main crystalline phases of the synthetic powder areα-S iC(6H-SiC)andβ-SiC(3C-SiC).The phase composition of the porous ceramics includesα-S iC(6H-SiC),β-SiC(3C-SiC),FeSi,quartz and Si2N20.The apparent porosity and closed porosity of the porous ceramics prepared by adding starch are higher,and the cold compressive strength of the porous ceramics added with graphite is higher.As increasing the additions of the starch,the apparent porosity,closed porosity and linear shrinkage ratio of the porous ceramics increase,and the bulk density decreases correspondingly.When 20 mass%starch is added,the apparent porosity,closed porosity,linear shrinkage ratio and cold compressive strength are 57.05%,2.03%,5.10%and 10.20 MPa,respectively.
文摘SiC porous ceramics were prepared at 1 400 ℃ for4 h with crystalline silicon cutting waste and activated carbon as main starting materials and NH4HCO3 as the pore-forming agent. Effects of NH4HCO3 additions( 0,20%,30%,40%,by mass) on the phase composition,microstructure,sintering properties,cold compressive strength and thermal shock resistance of as-prepared Si C porous ceramics were investigated. The results show that:( 1) addition of NH4HCO3 remarkably influences the apparent porosity and cold compressive strength of specimens. The apparent porosity achieves its maximum value( 63. 40%) when 40% NH4HCO3 is added,while the minimum cold compressive strength is 4. 77 MPa;( 2) the specimen with 40% NH4HCO3 has the best thermal shock resistance. The thermal cycling times between1 000 ℃ to room temperature reach 62;( 3) the addition of NH4HCO3 does not remarkably affect the phase composition of the specimens;( 4) the specimens include a large number of SiC particles and a small amount of SiC whiskers.
文摘An innovative approach has been developed to fabricate reticulated porous ceramics (RPCs) with uniform macrostruc-ture by using the polymeric sponge as the templates. In this approach, the coating process comprises of two stages. In the first stage, the thicker slurry was used to coat: uniformly the sponge substrate. The green body was preheated to produce a reticulated preform with enough handling strength after the sponge was burned out. In the second stage, the thinner slurry was used to coat uniformly the preform. The population of the microscopic and macroscopic flaws in the structure is reduced significantly by recoating process. A few filled cells and cell faces occur in the fabrication and the struts were thickened. A statistical evaluation by means of Weibull statistics was carried out on the bend strength data of RPCs, which were prepared by the traditional approach and innovative approach, respectively. The result shows that the mechanical reliability of RPCs is improved by the innovative approach. This innovative approach is very simple and controlled easily, and will open up new technological applications for RPCs.
文摘In order to fabricate porous ceramics with good properties and proper production cost,SiC-Al2 O3 porous ceramics were prepared at 1 450 ℃ for 2 h from the powders of commercial silicon carbide and white fused corundum via a polymeric replication method. Effects of the mass ratio of SiC powder to white fused corundum powder（ 1 ∶ 3,1 ∶ 1 and 3 ∶ 1） on the appearance,phase composition,sintering properties and thermal shock resistance were investigated. The research results indicate that the as-prepared Si C-Al2 O3 porous ceramics have uniform pores,and their linear shrinkage ratio,apparent porosity and bulk density reach 4. 70%,67. 17%and 0. 83 g·cm-3,respectively. The thermal shock cycles from 1 400 ℃ to room temperature reach 23 including 15 cycles in air cooling condition and then 8 cycles in water cooling condition. Their main phases areα-Al2 O3 and Al6 Si2 O13 as well as a small amount of SiC and free SiO2. The as-prepared porous ceramic with the ratio of m（ SiC） ∶ m（ Al2 O3） = 1∶ 1 possesses prior comprehensive properties.
基金This work was supported by the National Natural Science Foundation of China(Grant Nos.92060202,51632007,51872229,and 51521061)the 111 Project of China(Grant No.B08040)National Science and Technology Major Project(Grant No.2017-VI-0007-0077).
文摘Three strategies were proposed to prolong the service life of continuous fiber-reinforced silicon carbide ceramic matrix composite(CMC-SiC),which served as thermal-structure components of aeroengine at thermo-mechanical-oxygenic coupling environment.As for some thermal-structure components with low working stress,improving the degree of densification was crucial to prolong the service life,and the related process approaches were recited.If the thermal-structure components worked under moderate stress,the matrix cracking stress(σ^(mc))should be improved as far as possible.The fiber preform architecture,interface shear strength,residual thermal stress,and matrix strengthening were associated withσ_(mc)in this review.Introducing self-healing components was quite significant with the appearance of matrix microcracks when CMC-SiC worked at more severe environment for hundreds of hours.The damage can be sealed by glass phase originating from the reaction between self-healing components and oxygen.The effective self-healing temperature range of different self-healing components was first summarized and distinguished.The structure,composition,and preparation process of CMC-SiC should be systematically designed and optimized to achieve long duration target.