The effect of rare earth metals cerium, lanthanum and yttrium on chemical composition, structure and properties of electroless Co B alloy coating was studied. By plasma transmitting spectrograph, electron energy spec...The effect of rare earth metals cerium, lanthanum and yttrium on chemical composition, structure and properties of electroless Co B alloy coating was studied. By plasma transmitting spectrograph, electron energy spectrometer, X ray diffractometter, micro hardometer and vibratory sample magnetometer the chemical constitution, structure and properties of the alloy coatings were analyzed and inspected. The results show that with a tiny quantity of rare earth metal added into Co B alloy coating, the content of boron is decreased in the alloy coatings, and the kinds of rare earth metal have enormous effect on the structure and properties of electroless Co B alloy coating. At the same time electroless Co B alloy with amorphous structure is transformed to electroless Co B RE alloy with microcrystalline or crystalline structure. In this way microhardness of the coatings is increased remarkably. Cerium and lanthanum would also increase the saturated magnetic intensity and decrease coercitive force of the coating. So soft magnetization of the coatings would be improved.展开更多
By plasma transmitting spectrograph,electron energy spectrometry,X-ray diffractometry,transmission electron microscopy and micro-hardometry,the effects of ultrasonic irradiation and rare earth metal cerium on the depo...By plasma transmitting spectrograph,electron energy spectrometry,X-ray diffractometry,transmission electron microscopy and micro-hardometry,the effects of ultrasonic irradiation and rare earth metal cerium on the depositing speed,chemical composition,crystal structure and microhardness of electroless Co-Ni-B alloy coating were inspected and analyzed. The results show that cerium and ultrasonic irradiation can evidently raise the depositing speed of electroless Co-Ni-B alloy. The cerium content of electroless Co-Ni-B-Ce alloy coating also increases after ultrasonic irradiation applied to electroless Co-Ni-B plating process. Under the action of ultrasonic irradiation and rare metal cerium,the chemical composition of electroless Co-Ni-B alloy coating is changed. Electroless Co-Ni-B alloy with amorphous structure is transformed to electroless Co-Ni-B-Ce alloy with microcrystalline in general state and electroless Co-Ni-B-Ce alloy with crystalline structure in ultrasonic irradiation. In this way microhardness of the coatings increases remarkably.展开更多
利用恒电位仪、等离子发射光谱仪、电子能谱仪、X射线衍射仪、透射电子显微镜等考察和分析了引入稀土金属La时化学镀Co Fe B合金的阴极极化曲线、沉积速度、化学成分和晶体结构。结果表明 ,稀土La的介入明显改善了化学镀Co Fe B合金的...利用恒电位仪、等离子发射光谱仪、电子能谱仪、X射线衍射仪、透射电子显微镜等考察和分析了引入稀土金属La时化学镀Co Fe B合金的阴极极化曲线、沉积速度、化学成分和晶体结构。结果表明 ,稀土La的介入明显改善了化学镀Co Fe B合金的静止电位和极化度 ,随镀液里稀土金属La添加量的增加 ,合金的沉积速度和镀层中La的含量都是先增后降 ,且都在La加入 0 6g·L- 1 时达到最大值。稀土La的介入使化学镀Co Fe B La合金镀层中B的含量减少 ,Co和Fe的含量增加 ,并使具有非晶态结构的化学镀Co Fe B合金转化为晶态结构的化学镀Co Fe B La合金。展开更多
用化学镀方法制备了Ni Co W P合金电极,并研究了其在1mol/LNaOH溶液中的析氢电催化活性,实验表明在相同的电流密度下,Ni Co W P合金电极比Ni Co P、Ni W P合金电极具有更低析氢过电位,XRD实验显示其镀层为非晶态.并进一步研究了Ni Co W ...用化学镀方法制备了Ni Co W P合金电极,并研究了其在1mol/LNaOH溶液中的析氢电催化活性,实验表明在相同的电流密度下,Ni Co W P合金电极比Ni Co P、Ni W P合金电极具有更低析氢过电位,XRD实验显示其镀层为非晶态.并进一步研究了Ni Co W P合金电极的电化学稳定性和表观活化能,结果表明:Ni Co W P合金电极具有比Ni Co P、Ni W P合金电极更好的析氢电催化活性和电化学稳定性.展开更多
文摘The effect of rare earth metals cerium, lanthanum and yttrium on chemical composition, structure and properties of electroless Co B alloy coating was studied. By plasma transmitting spectrograph, electron energy spectrometer, X ray diffractometter, micro hardometer and vibratory sample magnetometer the chemical constitution, structure and properties of the alloy coatings were analyzed and inspected. The results show that with a tiny quantity of rare earth metal added into Co B alloy coating, the content of boron is decreased in the alloy coatings, and the kinds of rare earth metal have enormous effect on the structure and properties of electroless Co B alloy coating. At the same time electroless Co B alloy with amorphous structure is transformed to electroless Co B RE alloy with microcrystalline or crystalline structure. In this way microhardness of the coatings is increased remarkably. Cerium and lanthanum would also increase the saturated magnetic intensity and decrease coercitive force of the coating. So soft magnetization of the coatings would be improved.
文摘By plasma transmitting spectrograph,electron energy spectrometry,X-ray diffractometry,transmission electron microscopy and micro-hardometry,the effects of ultrasonic irradiation and rare earth metal cerium on the depositing speed,chemical composition,crystal structure and microhardness of electroless Co-Ni-B alloy coating were inspected and analyzed. The results show that cerium and ultrasonic irradiation can evidently raise the depositing speed of electroless Co-Ni-B alloy. The cerium content of electroless Co-Ni-B-Ce alloy coating also increases after ultrasonic irradiation applied to electroless Co-Ni-B plating process. Under the action of ultrasonic irradiation and rare metal cerium,the chemical composition of electroless Co-Ni-B alloy coating is changed. Electroless Co-Ni-B alloy with amorphous structure is transformed to electroless Co-Ni-B-Ce alloy with microcrystalline in general state and electroless Co-Ni-B-Ce alloy with crystalline structure in ultrasonic irradiation. In this way microhardness of the coatings increases remarkably.
文摘利用恒电位仪、等离子发射光谱仪、电子能谱仪、X射线衍射仪、透射电子显微镜等考察和分析了引入稀土金属La时化学镀Co Fe B合金的阴极极化曲线、沉积速度、化学成分和晶体结构。结果表明 ,稀土La的介入明显改善了化学镀Co Fe B合金的静止电位和极化度 ,随镀液里稀土金属La添加量的增加 ,合金的沉积速度和镀层中La的含量都是先增后降 ,且都在La加入 0 6g·L- 1 时达到最大值。稀土La的介入使化学镀Co Fe B La合金镀层中B的含量减少 ,Co和Fe的含量增加 ,并使具有非晶态结构的化学镀Co Fe B合金转化为晶态结构的化学镀Co Fe B La合金。
文摘用化学镀方法制备了Ni Co W P合金电极,并研究了其在1mol/LNaOH溶液中的析氢电催化活性,实验表明在相同的电流密度下,Ni Co W P合金电极比Ni Co P、Ni W P合金电极具有更低析氢过电位,XRD实验显示其镀层为非晶态.并进一步研究了Ni Co W P合金电极的电化学稳定性和表观活化能,结果表明:Ni Co W P合金电极具有比Ni Co P、Ni W P合金电极更好的析氢电催化活性和电化学稳定性.