The fracture modes of low alloy steels and cast irons under tensile and fatigue conditions were identified by electron back-scattered diffraction（EBSD） misorientation analysis in this research. The curves of grain r...The fracture modes of low alloy steels and cast irons under tensile and fatigue conditions were identified by electron back-scattered diffraction（EBSD） misorientation analysis in this research. The curves of grain reference orientation deviation（GROD） distribution perpendicular to the fracture surface were obtained by EBSD observation, and the characteristics of each fracture mode were identified. The GROD value of the specimen fractured in tension decreases to a constant related to the elongation of corresponding specimen in the far field（farther than 5 mm away from the fracture surface）. The peak exhibits in GROD curves of two smooth specimens and a notched specimen near the fracture surface（within 5 mm away from the fracture surface）, and the formation mechanisms were discussed in detail based on the influences of specimen geometries（smooth or notched） and material toughness. The GROD value of fatigue fractured specimen is close to that at undeformed condition in the whole field, except the small area near the crack path. The loading conditions（constant stress amplitude loading or constant stress intensity factor range K loading） and the EBSD striation formation during fatigue crack propagation were also studied by EBSD observation parallel to the crack path.展开更多
对七道次异步叠轧铜板采用220℃×30 m in和220℃×40 m in两种工艺进行退火,运用背散射电子衍射技术对两种铜板的再结晶程度、织构和晶界特征分布进行了研究。结果表明,经220℃×40 m in退火处理后,铜板的再结晶较完全,其...对七道次异步叠轧铜板采用220℃×30 m in和220℃×40 m in两种工艺进行退火,运用背散射电子衍射技术对两种铜板的再结晶程度、织构和晶界特征分布进行了研究。结果表明,经220℃×40 m in退火处理后,铜板的再结晶较完全,其织构为明显的{100}〈001〉立方织构;而经220℃×30 m in退火处理后,铜板内仍存在晶体缺陷,其织构为{123}〈412〉轧制织构及少量的{100}〈001〉立方织构。晶界特征分布图表明晶界都主要分布在Σ1、Σ3、Σ7、Σ9和Σ11位置上,采用220℃×40 m in退火处理后铜板中各主要晶界的含量明显高于采用220℃×30m in退火后的。展开更多
基金financially supported by Mitsubishi Heavy Industries,Ltd.,Japanthe National Natural Science Foundation of China(Nos.11572171,11632010 and U1533134)the opening project(No.KFJJ15-12M)of State Key Laboratory of Explosion Science and Technology(Beijing Institute of Technology)
文摘The fracture modes of low alloy steels and cast irons under tensile and fatigue conditions were identified by electron back-scattered diffraction（EBSD） misorientation analysis in this research. The curves of grain reference orientation deviation（GROD） distribution perpendicular to the fracture surface were obtained by EBSD observation, and the characteristics of each fracture mode were identified. The GROD value of the specimen fractured in tension decreases to a constant related to the elongation of corresponding specimen in the far field（farther than 5 mm away from the fracture surface）. The peak exhibits in GROD curves of two smooth specimens and a notched specimen near the fracture surface（within 5 mm away from the fracture surface）, and the formation mechanisms were discussed in detail based on the influences of specimen geometries（smooth or notched） and material toughness. The GROD value of fatigue fractured specimen is close to that at undeformed condition in the whole field, except the small area near the crack path. The loading conditions（constant stress amplitude loading or constant stress intensity factor range K loading） and the EBSD striation formation during fatigue crack propagation were also studied by EBSD observation parallel to the crack path.
文摘对七道次异步叠轧铜板采用220℃×30 m in和220℃×40 m in两种工艺进行退火,运用背散射电子衍射技术对两种铜板的再结晶程度、织构和晶界特征分布进行了研究。结果表明,经220℃×40 m in退火处理后,铜板的再结晶较完全,其织构为明显的{100}〈001〉立方织构;而经220℃×30 m in退火处理后,铜板内仍存在晶体缺陷,其织构为{123}〈412〉轧制织构及少量的{100}〈001〉立方织构。晶界特征分布图表明晶界都主要分布在Σ1、Σ3、Σ7、Σ9和Σ11位置上,采用220℃×40 m in退火处理后铜板中各主要晶界的含量明显高于采用220℃×30m in退火后的。