Radiator thermal performance test equipment plays a key role in the processing of developing a new type of heat radiator and its application products.The precise of temperature controlling,temperature measuring andflow measuring are the vital factors for a radiator thermal performance test equipment.Based on the above back-ground,this paper improves the measurement and control system of radiator thermal performance test equip-ment,which improves the accuracy of the radiator thermal performance test equipment.This paper also optimizes the software and hardware system simultaneously so as to improve the precision of the auto-test system of test equipment.Theflow rate ranges from 175 kg/h to 178 kg/h under different conditions.The average is 176.5 kg/h and the deviation rates are from 1.62%to 1.97%.The heat produced under various conditions is different.The maximum is 4.3 kW and the minimum is 4.2 kW for condition 1,the maximum is 3.3 kW and the minimum is 3.2 kW for condition 2 and the maximum is 1.95 kW and the minimum is 1.89 kW for condition 3.However,the deviation rate is about 2.9%,which shows that the device has high stability and high precision.This paper studies a new electronic heat cost allocate meter test method by radiator thermal performance test equipment at the same time.This paper tests temperature changes through four measures points and gets a result appeared as a heat backup which should be avoided when using in the test of electronic heat cost allocate meter.Some experiences and references could be gained for further research in the heating system from this test and research.

Effects of the precipitation of stabilizers on the mechanism of grain fracturing in a zirconia metering nozzle

The mechanism of grain fracturing in a zirconia metering nozzle used in the continuous casting process was studied. The phase composition, microstructure, and chemical composition of the residual samples were studied using an X-ray fluorescence analyzer, scanning electron microscope, and electron probe. Results revealed that the composition, structure, and mineral phase of the original layer, transition layer, and affected layer of the metering nozzle differed because of stabilizer precipitation and steel slag permeation. The stabilizer MgO formed low-melting phases with steel slag and impure SiO2 on the boundaries（pores） of zirconia grains; consequently, grain fracturing occurred and accelerated damage to the metering nozzle was observed.