Galvanic corrosion behavior of Ti-1023 titanium alloy coupled 30CrMnSiA steel was investigated in 3.5% NaCl solution. Particular attention was given to the effect of three different electroplated coatings on corrosion...Galvanic corrosion behavior of Ti-1023 titanium alloy coupled 30CrMnSiA steel was investigated in 3.5% NaCl solution. Particular attention was given to the effect of three different electroplated coatings on corrosion behavior of the galvanic couple. Galvanic corrosion test was conducted on Ti-1023 titanium alloy which coupled Ni-electroplated 30CrMnSiA, Zn-electroplated 30CrMnSiA, Cd-electroplated 30CrMnSiA and bare 30CrMnSiA, respectively. Corrosion properties including open circuit potential （Eoc）, galvanic corrosion potential （Eg）, and galvanic corrosion current （lg） were monitored. Corrosion morphology was observed by optical microscope （OM） and corrosion mechanism was analyzed and discussed. The results show that the three electroplated coatings improve the corrosion resistance of the anode in different magnitudes. Ni-electroplated 30CrMnSiA and Cd-electroplated 30CrMnSiA coatings are found to be least susceptible to galvanic corrosion when coupled Ti-1023 titanium alloy. Zn-electroplated 30CrMnSiA is moderately susceptible to galvanic corrosion. But the bare 30CrMnSiA is highly susceptible to galvanic corrosion in corrosive environment.展开更多
Pure Ni and its composites with different percentages of Ni-Cr nano-oxides were coated over carbon steel to assess the coating features and mechanical and corrosion behavior.A nano-oxide composite of Ni-Cr was first s...Pure Ni and its composites with different percentages of Ni-Cr nano-oxides were coated over carbon steel to assess the coating features and mechanical and corrosion behavior.A nano-oxide composite of Ni-Cr was first synthesized through chemical coprecipitation with uniform distribution constituents.Electrodeposition was employed to coat pure Ni and Ni-(Ni-Cr)oxides(10,20,30,40,and 50 g/L)on the steel sheets.Transmission electron microscope and field emission scanning electron microscope were adopted to examine the microstructure of powders and coatings,and X-ray diffraction analysis was employed to study the chemical composition.The microhardness,thickness,and wear resistance of the coatings were assessed,polarization and electrochemical impedance spectroscopy(EIS)tests were conducted to analyze the corrosion behavior,and the corresponding equivalent circuit was developed.Results showed flawless and crack-free coatings for all samples and uniform distribution of nano-oxides in the Ni matrix for the samples of 10-30 g/L.Agglomerated oxides were detected at high concentrations.Maximum microhardness(HV 661),thickness(116μm),and wear resistance of coatings were found at 30 g/L.A three-loop equivalent circuit corresponded satisfactorily to all EIS data.The corrosion resistance increased with the nano-oxide concentration of up to 30 g/L but decreased at 40 g/L.The sample of 50 g/L showed the best corrosion resistance.展开更多
基金the National Science Foundation of China (No.50571003)
文摘Galvanic corrosion behavior of Ti-1023 titanium alloy coupled 30CrMnSiA steel was investigated in 3.5% NaCl solution. Particular attention was given to the effect of three different electroplated coatings on corrosion behavior of the galvanic couple. Galvanic corrosion test was conducted on Ti-1023 titanium alloy which coupled Ni-electroplated 30CrMnSiA, Zn-electroplated 30CrMnSiA, Cd-electroplated 30CrMnSiA and bare 30CrMnSiA, respectively. Corrosion properties including open circuit potential （Eoc）, galvanic corrosion potential （Eg）, and galvanic corrosion current （lg） were monitored. Corrosion morphology was observed by optical microscope （OM） and corrosion mechanism was analyzed and discussed. The results show that the three electroplated coatings improve the corrosion resistance of the anode in different magnitudes. Ni-electroplated 30CrMnSiA and Cd-electroplated 30CrMnSiA coatings are found to be least susceptible to galvanic corrosion when coupled Ti-1023 titanium alloy. Zn-electroplated 30CrMnSiA is moderately susceptible to galvanic corrosion. But the bare 30CrMnSiA is highly susceptible to galvanic corrosion in corrosive environment.
文摘Pure Ni and its composites with different percentages of Ni-Cr nano-oxides were coated over carbon steel to assess the coating features and mechanical and corrosion behavior.A nano-oxide composite of Ni-Cr was first synthesized through chemical coprecipitation with uniform distribution constituents.Electrodeposition was employed to coat pure Ni and Ni-(Ni-Cr)oxides(10,20,30,40,and 50 g/L)on the steel sheets.Transmission electron microscope and field emission scanning electron microscope were adopted to examine the microstructure of powders and coatings,and X-ray diffraction analysis was employed to study the chemical composition.The microhardness,thickness,and wear resistance of the coatings were assessed,polarization and electrochemical impedance spectroscopy(EIS)tests were conducted to analyze the corrosion behavior,and the corresponding equivalent circuit was developed.Results showed flawless and crack-free coatings for all samples and uniform distribution of nano-oxides in the Ni matrix for the samples of 10-30 g/L.Agglomerated oxides were detected at high concentrations.Maximum microhardness(HV 661),thickness(116μm),and wear resistance of coatings were found at 30 g/L.A three-loop equivalent circuit corresponded satisfactorily to all EIS data.The corrosion resistance increased with the nano-oxide concentration of up to 30 g/L but decreased at 40 g/L.The sample of 50 g/L showed the best corrosion resistance.