Stable high-solids-content acrylate emulsion were obtained with a nonionic polymerizable emulsifier allyloxy nonylphenoxy poly （ethyleneoxy） （10） ether （ANPEO10）, and a conventional emulsifier OP-10 as a referen...Stable high-solids-content acrylate emulsion were obtained with a nonionic polymerizable emulsifier allyloxy nonylphenoxy poly （ethyleneoxy） （10） ether （ANPEO10）, and a conventional emulsifier OP-10 as a reference sample. 1H NMR proves that the polymerizable emulsifier ANPEO10 has been incorporated into the resulted acrylate polymers. TEM demonstrates that there are some differences in the particle morphologies. AFM proves that the polymerizable emulsifier ANPEO10 migrating to the surface of the emulsion film was much less than the conventional emulsifier OP-10. The polymerizable emulsifier ANPEO10 can enhance the adhesion with glass plate compared to the conventional emulsifier. Furthermore, with increasing amount of emulsifier, the surface free energy of the films first decreased and then increased, and the adhesion with glass plate is initially enhanced and then attenuated. The water-resistance and solvent-resistance of the films prepared by the polymerizable emulsifier ANPEO10 are superior to those prepared by the conventional emulsifier OP-10.展开更多
The emulsion polymerization of highly shear-stable copolymer dispersions of methyl methacrylate and butyl acrylate were carried out using poly （vinyl alcohol） with a thiol end group （PVA-SH） as protective colloid....The emulsion polymerization of highly shear-stable copolymer dispersions of methyl methacrylate and butyl acrylate were carried out using poly （vinyl alcohol） with a thiol end group （PVA-SH） as protective colloid. The dispersions can be transformed into corresponding redispersible powder via a spray dryingcooling process. On-line FT-IR monitoring shows that grafting polymer of PVA-g-PMMA was formed mainly at the stage-1 of the emulsion polymerization. TEM images show, the PVA-SH shell was fragmentary when adding SDS at initial stage and integrated when adding at particle growing or final stage. The particle size turns to be smaller when delayed adding SDS surfactant. Triethanolamine, a co-regulator of PVA-SH, controlled the M to 50 000-70 000 and reduced the PDI to 1.5-1.7. The acrylic dispersions with 0.8wt%-1.5wt% PVA-SH1 can be spray-dried into super dispersible polymer powder （SDPP）, which can easily disperse in water and form recon- stituted dispersions with an average particle size smaller than 1 micron.展开更多
基金Funded by Ministry of Education (No.2006-KL-008),and Qingxin Hanerchem Chemical Technology Co,Ltd.
文摘Stable high-solids-content acrylate emulsion were obtained with a nonionic polymerizable emulsifier allyloxy nonylphenoxy poly （ethyleneoxy） （10） ether （ANPEO10）, and a conventional emulsifier OP-10 as a reference sample. 1H NMR proves that the polymerizable emulsifier ANPEO10 has been incorporated into the resulted acrylate polymers. TEM demonstrates that there are some differences in the particle morphologies. AFM proves that the polymerizable emulsifier ANPEO10 migrating to the surface of the emulsion film was much less than the conventional emulsifier OP-10. The polymerizable emulsifier ANPEO10 can enhance the adhesion with glass plate compared to the conventional emulsifier. Furthermore, with increasing amount of emulsifier, the surface free energy of the films first decreased and then increased, and the adhesion with glass plate is initially enhanced and then attenuated. The water-resistance and solvent-resistance of the films prepared by the polymerizable emulsifier ANPEO10 are superior to those prepared by the conventional emulsifier OP-10.
文摘The emulsion polymerization of highly shear-stable copolymer dispersions of methyl methacrylate and butyl acrylate were carried out using poly （vinyl alcohol） with a thiol end group （PVA-SH） as protective colloid. The dispersions can be transformed into corresponding redispersible powder via a spray dryingcooling process. On-line FT-IR monitoring shows that grafting polymer of PVA-g-PMMA was formed mainly at the stage-1 of the emulsion polymerization. TEM images show, the PVA-SH shell was fragmentary when adding SDS at initial stage and integrated when adding at particle growing or final stage. The particle size turns to be smaller when delayed adding SDS surfactant. Triethanolamine, a co-regulator of PVA-SH, controlled the M to 50 000-70 000 and reduced the PDI to 1.5-1.7. The acrylic dispersions with 0.8wt%-1.5wt% PVA-SH1 can be spray-dried into super dispersible polymer powder （SDPP）, which can easily disperse in water and form recon- stituted dispersions with an average particle size smaller than 1 micron.