It has been found through analysis of defect components and micrographs that ＂oil-burn＂ defects on non- oriented silicon steel surf＇aces, which of ten occur after cold rolling, are composed of Fe, O, Si and C. This...It has been found through analysis of defect components and micrographs that ＂oil-burn＂ defects on non- oriented silicon steel surf＇aces, which of ten occur after cold rolling, are composed of Fe, O, Si and C. This study analyzed the fomation mechanism of ＇toil-burn＂ defects and the strategies to prevent them,and proposed, according to the equipment and process status in the production fields ,some relevant optimized control measures and process adjustment schemes from two perspectives of reducing the residual emulsion trod avoiding the specific temperature range. The results demonstrate that the application of the proposed optimization meastu＇es effectively inhibits the formation of ＂oil-bum＂ defects.展开更多
文摘It has been found through analysis of defect components and micrographs that ＂oil-burn＂ defects on non- oriented silicon steel surf＇aces, which of ten occur after cold rolling, are composed of Fe, O, Si and C. This study analyzed the fomation mechanism of ＇toil-burn＂ defects and the strategies to prevent them,and proposed, according to the equipment and process status in the production fields ,some relevant optimized control measures and process adjustment schemes from two perspectives of reducing the residual emulsion trod avoiding the specific temperature range. The results demonstrate that the application of the proposed optimization meastu＇es effectively inhibits the formation of ＂oil-bum＂ defects.