Recent advances of flexible perovskite solar cells

In few years only, the efficiency record of perovskite solar cells（PSCs） has raised quickly from 3.8% to over 22%. This emerging photovoltaic technology has primarily shown its great potential of industrialization. Flexible PSCs are thought to be one of the most priority options for mass production, related to the intrinsic advantage of perovskite thin films which could be deposited by facile solution processes at low temperature. Flexible PSCs have at least four advantages in comparison to the rigid counterpart：（1） it can generate higher power output at lighter weight,（2） it is easily portable,（3） it can be easily attached to architectures or textiles with diverse shapes, and（4） it is compatible with roll-to-roll fabrication in a large scale. In this review, we have summarized recent development of the key materials and technologies applied in flexible PSCs. The key materials including flexible substrates, transparent and conductive electrodes, and interfacial materials; some key technologies about roll-to-roll manufacture, encapsulation technology have been overviewed. Finally, a prospect on possible application directions of flexible PSCs has been discussed.

Preparation Process and Properties of Porous Ecological Concrete

By using waste bricks as aggregate,a kind of porous ecological concrete was prepared and the mixing technique and its properties were studied. Effects of the cement paste fluidity on workability of the porous ecological concrete were investigated,and influences of the water-cement ratio,the aggregate-cement ratio and the aggregate size on compressive strength and porosity of the porous ecological concrete were also discussed. Results show that for preparation of the porous ecological concrete,the aggregates should be enveloped with neat cement paste,and recommended fluidity of the cement paste is 200～235 mm. With the increasing of the aggregate-cement ratio,porosity of the porous ecological concrete increases while the 28 d compressive strength decreases. With increasing of the water-cement ratio,porosity of the porous ecological concrete decreases. And relationship between compressive strength and water-cement ratio of the porous ecological concrete does not follow Bolomey's formula. As a result of this study the porous ecological concrete is prepared,its porosity is 38.93%,the water absorption is 11.39% and the compressive strength is 1.14 MPa.