A Bilayer High-Temperature Dielectric Film with Superior Breakdown Strength and Energy Storage Density

The further electrification of various fields in production and daily life makes it a topic worthy of exploration to improve the performance of capacitors for a long time,including thin-film capacitors.The discharge energy density of thin-film capacitors that serves as one of the important types directly depends on electric field strength and the dielectric constant of the insulation material.However,it has long been a great challenge to improve the breakdown strength and dielectric constant simultaneously.Considering that boron nitride nanosheets(BNNS)possess superior insulation and thermal conductivity owing to wide band gap and 2-dimensional structure,a bilayer polymer film is prepared via coating BNNS by solution casting on surface of polyethylene terephthalate(PET)films.By revealing the bandgap and insulating behavior with UV absorption spectrum,leakage current,and finite element calculation,it is manifested that nanocoating contributes to enhance the bandgap of polymer films,thereby suppressing the charge injection by redirecting their transport from electrodes.Worthy to note that an ultrahigh breakdown field strength(~736 MV m^(−1)),an excellent discharge energy density(~8.77 J cm^(−3))and a prominent charge-discharge efficiency(~96.51%)are achieved concurrently,which is ascribed to the contribution of BNNS ultrathin layer.In addition,the modified PET films also have superior comprehensive performance at high temperatures(~120°C).The materials and methods here selected are easily accessible and facile,which are suitable for large-scale roll-to-roll process production,and are of certain significance to explore the methods about film modification suitable for commercial promotion.

Improved Breakdown Strength in(Ba_(0.6)Sr_(0.4))_(0.85)Bi_(0.1)TiO_3 Ceramics with Addition of CaZrO_3 for Energy Storage Application

（Ba（0.6） Sr（0.4））（0.85） Bi（0.1） TiO3 ceramics doped with x wt%CaZrO3（x= 0-10） were synthesized by solid-state reaction method. The effects of CaZrO3 amount on the dielectric properties and structure of（Ba（0.6）Sr（0.4））（0.85） Bi（0.1） TiO3 ceramics were investigated. X-ray diffraction results indicated a pure cubic perovskite structure for all samples and that the lattice parameter increased till x=5 and then slightly decreased. A homogenous microstructure was observed with the addition of CaZrO3. Dielectric measurements revealed a relaxor-like characteristic for all samples and that the diffusivity γ reached the maximum value of 1.78 at x=5. With the addition of CaZrO3, the dielectric constant dependence on electric field was weakened, insulation resistivity enhanced and dielectric breakdown strength improved obviously and reached 19.9 k V/mm at x=7.5. In virtue of low dielectric loss（tan d〈0.001 5）, moderate dielectric constant（er 〉1 500） and high breakdown strength（Eb 〉17.5 k V/mm）, the CaZrO3 doped（Ba（0.6）Sr（0.4））0.85 Bi（0.1） TiO3 ceramic is a potential candidate material for high power electric applications.

High-temperature energy storage dielectric with inhibition of carrier injection/migration based on band structure regulation

Dielectric capacitors have a high power density,and are widely used in military and civilian life.The main problem lies in the serious deterioration of dielectric insulation performance at high temperatures.In this study,a polycarbonate(PC)-based energy storage dielectric was designed with BN/SiO_(2)heterojunctions on its surface.Based on this structural design,a synergistic suppression of the carrier injection and transport was achieved,significantly improving the insulating properties of the polymer film.In particular,the composite film achieves optimal high-temperature energy-storage properties.The composite film can withstand an electric field intensity of 760 MV m^(-1)at 100℃and obtain an energy storage density of 8.32 J cm^(-3),while achieving a breakthrough energy storage performance even at 150℃(610 MV m^(-1),5.22 J cm^(-3)).Through adjustment of the heterojunction structure,free adjustment of the insulation performance of the material can be realized;this is of great significance for the optimization of the material properties.