Currently, a conventional two-step method has been used to generate black silicon （BS） surfaces on silicon substrates for solar cell manufacturing. However, the performances of the solar cell made with such surface ...Currently, a conventional two-step method has been used to generate black silicon （BS） surfaces on silicon substrates for solar cell manufacturing. However, the performances of the solar cell made with such surface generation method are poor, because of the high surface recombination caused by deep etching in the conventional surface generation method for BS. In this work, a modified wet chemical etching solution with additives was developed. A homogeneous BS layer with random porous structure was obtained from the modified solution in only one step at room temperature. The BS layer had low reflectivity and shallow etching depth. The additive in the etch solution performs the function of pH-modulation. After 16-min etching, the etching depth in the samples was approximately 200 nm, and the spectrum-weighted-reflectivity in the range from 300 nm to 1200 nm was below 5%. BS solar cells were fabricated in the production line. The decreased etching depth can improve the electrical performance of solar cells because of the decrease in surface recombination. An efficiency of 15.63% for the modified etching BS solar cells was achieved on a large area, p- type single crystalline silicon substrate with a 624.32-mV open circuit voltage and a 77.88% fill factor.展开更多
A novel wet etching method for AlGaN/GaN heterojunction structures is proposed using thermal oxidation f ollowed by wet etching in KOH solution.It is found that an AlGaN/GaN heterostructure after high temperature oxid...A novel wet etching method for AlGaN/GaN heterojunction structures is proposed using thermal oxidation f ollowed by wet etching in KOH solution.It is found that an AlGaN/GaN heterostructure after high temperature oxidation above 700℃could be etched off in a homothermal（70℃） KOH solution while the KOH solution had no etching effects on the region of the AlGaN/GaN heterostructure protected by a SiO_2 layer during the oxidation process.A groove structure with 150 nm step depth on an AlGaN/GaN heterostructure was formed after 8 h thermal oxidation at 900℃followed by 30 min treatment in 70℃KOH solution.As the oxidation time increases,the etching depth approaches saturation and the roughness of the etched surface becomes much better.The physical mechanism of this phenomenon is also discussed.展开更多
文摘Currently, a conventional two-step method has been used to generate black silicon （BS） surfaces on silicon substrates for solar cell manufacturing. However, the performances of the solar cell made with such surface generation method are poor, because of the high surface recombination caused by deep etching in the conventional surface generation method for BS. In this work, a modified wet chemical etching solution with additives was developed. A homogeneous BS layer with random porous structure was obtained from the modified solution in only one step at room temperature. The BS layer had low reflectivity and shallow etching depth. The additive in the etch solution performs the function of pH-modulation. After 16-min etching, the etching depth in the samples was approximately 200 nm, and the spectrum-weighted-reflectivity in the range from 300 nm to 1200 nm was below 5%. BS solar cells were fabricated in the production line. The decreased etching depth can improve the electrical performance of solar cells because of the decrease in surface recombination. An efficiency of 15.63% for the modified etching BS solar cells was achieved on a large area, p- type single crystalline silicon substrate with a 624.32-mV open circuit voltage and a 77.88% fill factor.
基金supported by the National Natural Science Foundation of China(Nos.60406004,60890193,60736033)the National Key Micrometer/Nanometer Processing Laboratory,China
文摘A novel wet etching method for AlGaN/GaN heterojunction structures is proposed using thermal oxidation f ollowed by wet etching in KOH solution.It is found that an AlGaN/GaN heterostructure after high temperature oxidation above 700℃could be etched off in a homothermal（70℃） KOH solution while the KOH solution had no etching effects on the region of the AlGaN/GaN heterostructure protected by a SiO_2 layer during the oxidation process.A groove structure with 150 nm step depth on an AlGaN/GaN heterostructure was formed after 8 h thermal oxidation at 900℃followed by 30 min treatment in 70℃KOH solution.As the oxidation time increases,the etching depth approaches saturation and the roughness of the etched surface becomes much better.The physical mechanism of this phenomenon is also discussed.