In this paper, preparation process of nano TiO2 with sol-gel method at low temperature was optimized by response surface method. The nano TiO2 was analysised by DRS and XRD. Result show that： 20mL tetrabutyl titanate...In this paper, preparation process of nano TiO2 with sol-gel method at low temperature was optimized by response surface method. The nano TiO2 was analysised by DRS and XRD. Result show that： 20mL tetrabutyl titanate, 10mL acetic acid, 6mL ethanol dosage, aging time was 29h, aging temperature was 36℃, Nano TiO2 was prepared under the condition. Particle size of nano particles was 37.3nm, Photodegradation rate was 90.2%. It had good photocatalytic ability.展开更多
文摘In this paper, preparation process of nano TiO2 with sol-gel method at low temperature was optimized by response surface method. The nano TiO2 was analysised by DRS and XRD. Result show that： 20mL tetrabutyl titanate, 10mL acetic acid, 6mL ethanol dosage, aging time was 29h, aging temperature was 36℃, Nano TiO2 was prepared under the condition. Particle size of nano particles was 37.3nm, Photodegradation rate was 90.2%. It had good photocatalytic ability.