Extraction of valuable metals from low-grade nickeliferous laterite ore by reduction roasting-ammonia leaching method

Nickel and cobalt were extracted from low-grade nickeliferous laterite ore using a reduction roasting-ammonia leaching method.The reduction roasting-ammonia leaching experimental tests were chiefly introduced,by which fine coal was used as a reductant.The results show that the optimum process conditions are confirmed as follows:in reduction roasting process,the mass fraction of reductant in the ore is 10%,roasting time is 120 min,roasting temperature is 1 023-1 073 K;in ammonia leaching process,the liquid-to-solid ratio is 4:1(mL/g),leaching temperature is 313 K,leaching time is 120 min,and concentration ratio of NH3 to CO2 is 90 g/L:60 g/L.Under the optimum conditions,leaching efficiencies of nickel and cobalt are 86.25% and 60.84%,respectively.Therefore,nickel and cobalt can be effectively reclaimed,and the leaching agent can be also recycled at room temperature and normal pressure.

Transformation and leaching kinetics of silicon from low-grade nickel laterite ore by pre-roasting and alkaline leaching process

The mineralogical phase transformation of a low-grade nickel laterite ore during pre-roasting process and the extraction of silicon during alkaline leaching process were investigated.The results indicate that the reaction activity of nickel ores is effectively improved by pre-roasting at650°C for2h,because of the transformation of lizardite into magnesium olivine and protoenstatite.When finely ground ore samples(44-61μm)pre-roasted firstly react with sodium hydroxide solution(60g/L)with a solid/liquid ratio of1:5at140°C for120min,the extraction of silicon can reach89.89%,and the other valuable elements of magnesium,iron and nickel are accumulated in the solid residues.The leaching kinetics of nickel laterite ore can be described successfully by the diffusion through the product layer control model.The activation energy is calculated to be11.63kJ/mol and the kinetics equation can be expressed as1-3(1-x)2/3+2(1-x)=13.53×10-2exp[-11.63/(RT)]t.

Process development for the direct solvent extraction of nickel and cobalt from nitrate solution:aluminum,cobalt,and nickel separation using Cyanex 272

A direct solvent extraction（DSX） process for purifying nickel and cobalt from the nitric acid leach solution of nickel laterite ores was conceived and experimentally probed. The proposed process consists of two solvent extraction（SX） steps but with only one extractant - bis（2,4,4-trimethylpentyl）phosphinic acid（Cyanex？ 272） - used in both steps. The first extraction step involved the removal of aluminum and zinc, whereas the second extraction step involved the separation of cobalt along with manganese from nickel. The experimental results showed essentially quantitative removal of aluminum（〉97%） and zinc（〉99%） in a single extraction stage using 20vol% Cyanex 272 at pH 2.1. Some cobalt（32%） and manganese（55%） were co-extracted but were easily scrubbed out completely from the loaded organic phase using dilute sulfuric acid at pH ≤ 1.38. Cobalt and manganese in the first extraction raffinate were extracted completely in four extraction stages at staggered pH values of 4.0, 4.4, 4.5, and 4.0 in the first, second, third, and fourth stages, respectively, using also 20vol% Cyanex 272. A small amount of nickel（up to 6.6%） was co-extracted but was easily scrubbed out completely with dilute sulfuric acid at pH 2.0. A flow diagram showing the input and output conditions and the metals separated under the deduced optimum conditions is presented.

Influence of laterite nickel ore on extracting iron from Bayer red mud by carbothermal smelting reduction

In view of the difficulty of extracting iron from Bayer red mud,a new idea of adding laterite nickel ore into red mud was proposed to prepare a high value-added product.Toward this,the influences of laterite nickel ore on thermodynamic reaction,slagging and smelting reduction of extracting iron from red mud were studied.The results indicated that the product of extracting iron from red mud(R100)was changed with the addition of laterite nickel ore(R70L30).The slag of R100 was strongly basic,while the R70L30 was weakly acidic with composition closer to the ideal blast furnace slag.The metal recovery of R100 was 75.16%and that of R70L30 was 94.05%.At the same temperature,the slag viscosity of R70L30 was significantly lower than that of R100,which proved that laterite nickel ore can adjust the basicity,reduce melting point of slag and improve metal recovery.Because Fe,Ni and Cr in red mud and laterite nickel ore can be reduced sufficiently,a low Ni–Cr alloy cast iron can be directly prepared.

红土镍矿提镍工艺进展

介绍了目前国内外红土镍矿处理的火法工艺技术、湿法工艺技术以及其它工艺技术研究现状以及相关的理论研究工作,为今后低品位红土镍矿的开发提供参考。