It has been found that there are marked errors in the value of valid opening size of heat-bonded nonwoven fabrics between theoretical calculations and engineering measurements. A new modified theoretical model is adva...It has been found that there are marked errors in the value of valid opening size of heat-bonded nonwoven fabrics between theoretical calculations and engineering measurements. A new modified theoretical model is advanced in this paper. The equivalent diameter of the pore of a fibre web is used to calculate the valid opening size instead of the maximum diameter of inscribed circle used, because the fibres in practical fibre webs are flexible elastomers with definite diameters and the pore of fibre web may produce deformation in screening teat and engineering usage. The results show that the theoretical calculations coincide well with the engineering measurements. This method offers a theoretical basis for computer simulation to the performance of filters of heatbonded nonwoven fabrics.展开更多
Nickel-based superalloy lattice sandwich structures present higher stiffness,higher strength and higher temperature resistance in comparison with other metals.In this study,the Kagome unit was adopted to design the la...Nickel-based superalloy lattice sandwich structures present higher stiffness,higher strength and higher temperature resistance in comparison with other metals.In this study,the Kagome unit was adopted to design the lattice sandwich structure and ProCAST software was used to simulate the filling and solidification processes of the nickel-based superalloy.Grain morphology and sizes of the nickel-based superalloy lattice sandwich structures were simulated by using of cellular automaton coupled with finite element model(CAFE),and indirect additive manufacture combining with investment casting were carried out to fabricate the nickel-based superalloy lattice sandwich structures.The calculated grain morphology and sizes are in good agreement with the experimental results.The grains are mainly equiaxed with an average size of about 500µm.The simulated results also show that the superheat of melting and the mold preheated temperature have significant influence on the grain size of the Kagome lattice sandwich structures,lower superheat of melting and mold preheated temperatures are encouraged to obtain the fine grains while assuring the integrity of the Kagome lattice sandwich structures for industrial application.展开更多
The effects of fibre/matrix bonding, fabric density, fibre volume fraction and bundle size on microstructure, mechanical properties and failure mechanisms in carbon fibre reinforced composites （plastic and carbon mat...The effects of fibre/matrix bonding, fabric density, fibre volume fraction and bundle size on microstructure, mechanical properties and failure mechanisms in carbon fibre reinforced composites （plastic and carbon matrix） have been investigated. The microstructure of unloaded and cracked samples was studied by optical microscopy and scanning electron microscopy （SEM）, respectively whereas the mechanical behaviour was examined by 3- point bending experiments. Exclusively one type of experimental resole type phenolic resin was applied. A strong fibre/matrix bonding, which is needed for high strength of carbon fibre reinforced plastic （CFRP） materials leads to severe composite damages during the pyrolysis resulting in low strength, brittle failure and a very low utilisation of the fibres strain to failure in C/C composites. Inherent fabric parameters such as an increasing fabric density or bundle size or a reduced fibre volume fraction introduce inhomogenities to the CFRP＇s microstructure. Results are lower strength and stiffness whereas the strain to failure increases or remains unchanged. Toughness is almost not affected. In C/C composites inhomogenities due to a reduced bundle size reduce strain to failure, strength, stiffness and toughness. Vice versa a declining fibre volume fraction leads to exactly the opposite behaviour. Increasing the fabric density （weight per unit area） causes similar effects as in CFRPs.展开更多
文摘It has been found that there are marked errors in the value of valid opening size of heat-bonded nonwoven fabrics between theoretical calculations and engineering measurements. A new modified theoretical model is advanced in this paper. The equivalent diameter of the pore of a fibre web is used to calculate the valid opening size instead of the maximum diameter of inscribed circle used, because the fibres in practical fibre webs are flexible elastomers with definite diameters and the pore of fibre web may produce deformation in screening teat and engineering usage. The results show that the theoretical calculations coincide well with the engineering measurements. This method offers a theoretical basis for computer simulation to the performance of filters of heatbonded nonwoven fabrics.
基金financially supported by the National Science and Technology Major Project of China(No.2017ZA04014001)the Natural Science Foundation of Liaoning Province of China(Nos.2019-ZD-0997,20170540890)the Technology Development Fund of China Academy of Machinery Science and Technology(No.170217ZS01)
文摘Nickel-based superalloy lattice sandwich structures present higher stiffness,higher strength and higher temperature resistance in comparison with other metals.In this study,the Kagome unit was adopted to design the lattice sandwich structure and ProCAST software was used to simulate the filling and solidification processes of the nickel-based superalloy.Grain morphology and sizes of the nickel-based superalloy lattice sandwich structures were simulated by using of cellular automaton coupled with finite element model(CAFE),and indirect additive manufacture combining with investment casting were carried out to fabricate the nickel-based superalloy lattice sandwich structures.The calculated grain morphology and sizes are in good agreement with the experimental results.The grains are mainly equiaxed with an average size of about 500µm.The simulated results also show that the superheat of melting and the mold preheated temperature have significant influence on the grain size of the Kagome lattice sandwich structures,lower superheat of melting and mold preheated temperatures are encouraged to obtain the fine grains while assuring the integrity of the Kagome lattice sandwich structures for industrial application.
文摘The effects of fibre/matrix bonding, fabric density, fibre volume fraction and bundle size on microstructure, mechanical properties and failure mechanisms in carbon fibre reinforced composites （plastic and carbon matrix） have been investigated. The microstructure of unloaded and cracked samples was studied by optical microscopy and scanning electron microscopy （SEM）, respectively whereas the mechanical behaviour was examined by 3- point bending experiments. Exclusively one type of experimental resole type phenolic resin was applied. A strong fibre/matrix bonding, which is needed for high strength of carbon fibre reinforced plastic （CFRP） materials leads to severe composite damages during the pyrolysis resulting in low strength, brittle failure and a very low utilisation of the fibres strain to failure in C/C composites. Inherent fabric parameters such as an increasing fabric density or bundle size or a reduced fibre volume fraction introduce inhomogenities to the CFRP＇s microstructure. Results are lower strength and stiffness whereas the strain to failure increases or remains unchanged. Toughness is almost not affected. In C/C composites inhomogenities due to a reduced bundle size reduce strain to failure, strength, stiffness and toughness. Vice versa a declining fibre volume fraction leads to exactly the opposite behaviour. Increasing the fabric density （weight per unit area） causes similar effects as in CFRPs.