To further increase the mechanical properties, 0.5wt.% Sm was introduced to a Mg-10Y alloy in this study. The effects of Sm addition on the microstructures and mechanical properties of the Mg-10Y alloy, especially the...To further increase the mechanical properties, 0.5wt.% Sm was introduced to a Mg-10Y alloy in this study. The effects of Sm addition on the microstructures and mechanical properties of the Mg-10Y alloy, especially the aged Mg-10Y alloy, were investigated. The microstructure observation and tensile tests were performed by using an optical microscopy, a scanning electron microscopy and a universal material testing machine, respectively. The phase analysis was performed using X-ray diffractometer. The results show that the 0.5wt.% Sm addition can not only promote the formation of fine and dispersed Mg24Y5 phases, but also improve their morphology and distribution; it also increases the thermal stability of Mg24Y5 phases. Sm addition is seen to increase the ultimate tensile strength of Mg-10Y alloy at elevated temperatures(200, 250, 300 and 350 ℃), while decrease the elongation. But the elongation is still up to 7.5% even at 350 ℃. In the range of 250 ℃ to 300℃, the ultimate tensile strength of the alloy reaches its maximum(with a range average of 235 MPa) and is not sensitive to the temperature change, which is very useful to the application of heat-resistant magnesium alloys. Even at 350 ℃, the ultimate tensile strength of Mg-10Y-0.5Sm is still up to 155 MPa. Considering both of the ultimate tensile strength and elongation, the maximum application temperature of the Mg-10Y-0.5Sm alloy can be up to 300 ℃. The strengthening mechanisms of Mg-10Y-0.5Sm alloy are mainly attributed to dispersion strengthening of Mg24Y5 phase particles with a certain solubility of Sm and grain refinement strengthening of α-Mg matrix.展开更多
A large amount of cutting heat is produced during the heavy cutting process,and insert life is restricted by the effect of thermal load. The thermal load experiment of cemented carbide SCS,WF and YT15 is carried out,a...A large amount of cutting heat is produced during the heavy cutting process,and insert life is restricted by the effect of thermal load. The thermal load experiment of cemented carbide SCS,WF and YT15 is carried out,and the results show that the bending strength and fracture toughness of cemented carbide material decrease obviously under cyclic thermal load,while in the cooling process,the material mechanical property changes worse suddenly. The high-temperature mechanical property of SCS is the most stable,and that of YT15is the worst. Further,a relation model among cutting temperature,cutting parameters and insert life is established. Finally,the measures to improve heavy cemented carbide inserts life are summarized from the aspects of cutting parameters selection,insert optimization design and TiCN,A12O3,TiN complex insert coating. The research results are expected to provide support and reference for heavy cutting technology and insert technology.展开更多
This paper presents an investigation into modelling the rheological properties of epoxy asphalt concrete( EAC) by using the Huet-Sayegh model. Complex modulus tests were conducted on EAC specimens at various temperatu...This paper presents an investigation into modelling the rheological properties of epoxy asphalt concrete( EAC) by using the Huet-Sayegh model. Complex modulus tests were conducted on EAC specimens at various temperature and loading frequency conditions. Dynamic modulus and phase angles obtained from the complex modulus tests were used in the construction of the Huet-Sayegh model. The dynamic modulus master curve was developed by the Huet-Sayegh model as well as the Burgers model for comparison purpose. The results showed that EAC exhibits typical rheological behavior whose dynamic modulus decreases with the increase of temperature while increases with the increase of frequency,and phase angles increase with the decrease of frequencies and the increase of temperatures. The Huet-Sayegh model predicts the dynamic modulus master curve of EAC very well and much better than the Burgers model over a wide range of frequencies.展开更多
基金financially supported by the National Natural Science Foundation of China(No.51171059)the Innovative Research Team(in Science and Technology)in University of Henan Province(No.2012IRTSTHN008)the Basic and Frontier Technologies Research Plan of Henan Province(No.102300410018)
文摘To further increase the mechanical properties, 0.5wt.% Sm was introduced to a Mg-10Y alloy in this study. The effects of Sm addition on the microstructures and mechanical properties of the Mg-10Y alloy, especially the aged Mg-10Y alloy, were investigated. The microstructure observation and tensile tests were performed by using an optical microscopy, a scanning electron microscopy and a universal material testing machine, respectively. The phase analysis was performed using X-ray diffractometer. The results show that the 0.5wt.% Sm addition can not only promote the formation of fine and dispersed Mg24Y5 phases, but also improve their morphology and distribution; it also increases the thermal stability of Mg24Y5 phases. Sm addition is seen to increase the ultimate tensile strength of Mg-10Y alloy at elevated temperatures(200, 250, 300 and 350 ℃), while decrease the elongation. But the elongation is still up to 7.5% even at 350 ℃. In the range of 250 ℃ to 300℃, the ultimate tensile strength of the alloy reaches its maximum(with a range average of 235 MPa) and is not sensitive to the temperature change, which is very useful to the application of heat-resistant magnesium alloys. Even at 350 ℃, the ultimate tensile strength of Mg-10Y-0.5Sm is still up to 155 MPa. Considering both of the ultimate tensile strength and elongation, the maximum application temperature of the Mg-10Y-0.5Sm alloy can be up to 300 ℃. The strengthening mechanisms of Mg-10Y-0.5Sm alloy are mainly attributed to dispersion strengthening of Mg24Y5 phase particles with a certain solubility of Sm and grain refinement strengthening of α-Mg matrix.
基金Sponsored by the National Natural Science Foundation of China(Grant No.51205095)Support Program for Key Youth(Grant No.1154G39)
文摘A large amount of cutting heat is produced during the heavy cutting process,and insert life is restricted by the effect of thermal load. The thermal load experiment of cemented carbide SCS,WF and YT15 is carried out,and the results show that the bending strength and fracture toughness of cemented carbide material decrease obviously under cyclic thermal load,while in the cooling process,the material mechanical property changes worse suddenly. The high-temperature mechanical property of SCS is the most stable,and that of YT15is the worst. Further,a relation model among cutting temperature,cutting parameters and insert life is established. Finally,the measures to improve heavy cemented carbide inserts life are summarized from the aspects of cutting parameters selection,insert optimization design and TiCN,A12O3,TiN complex insert coating. The research results are expected to provide support and reference for heavy cutting technology and insert technology.
基金Sponsored by the Natgional Natural Science Foundation of China(Grant No.51208103)the China Postdoctoral Science Foundation(Grant No.2012M520976)the Basic Research Foundation of Southeast University
文摘This paper presents an investigation into modelling the rheological properties of epoxy asphalt concrete( EAC) by using the Huet-Sayegh model. Complex modulus tests were conducted on EAC specimens at various temperature and loading frequency conditions. Dynamic modulus and phase angles obtained from the complex modulus tests were used in the construction of the Huet-Sayegh model. The dynamic modulus master curve was developed by the Huet-Sayegh model as well as the Burgers model for comparison purpose. The results showed that EAC exhibits typical rheological behavior whose dynamic modulus decreases with the increase of temperature while increases with the increase of frequency,and phase angles increase with the decrease of frequencies and the increase of temperatures. The Huet-Sayegh model predicts the dynamic modulus master curve of EAC very well and much better than the Burgers model over a wide range of frequencies.