The growth behaviors of short through cracks (0.2 < △a < 2.2mm) and long cracks are compared using CT type specimens in aluminum-lithium alloy 8090 T651. It is found that the short cracks grow much more than lo...The growth behaviors of short through cracks (0.2 < △a < 2.2mm) and long cracks are compared using CT type specimens in aluminum-lithium alloy 8090 T651. It is found that the short cracks grow much more than long ones and are observed to grow at the stress intensity ranges far below the long crack threshold. The distinction of growth bahavior between short and long cracks is attributed to the difference of their crack closure effect. The growth behavior of short cracks can be rationalized with that of long ones in terms of effective stress intensity ranges. The upper demarcation value of short through cracks for aluminum-lithium alloy 8090 is presented.展开更多
文摘The growth behaviors of short through cracks (0.2 < △a < 2.2mm) and long cracks are compared using CT type specimens in aluminum-lithium alloy 8090 T651. It is found that the short cracks grow much more than long ones and are observed to grow at the stress intensity ranges far below the long crack threshold. The distinction of growth bahavior between short and long cracks is attributed to the difference of their crack closure effect. The growth behavior of short cracks can be rationalized with that of long ones in terms of effective stress intensity ranges. The upper demarcation value of short through cracks for aluminum-lithium alloy 8090 is presented.