Effect of Fatigue Loading on the Mechanical Properties and Resistance of High-strength Straight-hole Recycled Pervious Concrete to Rainstorm-based Waterlogging

A novel high-strength straight-hole recycled pervious concrete(HSRPC)for the secondary highway pavement was prepared in this paper.This study aimed to investigate the effect of porosity(0.126%,0.502%,and 1.13%),vehicle loading stress level(0.5 and 0.8)and service life on the resistance to rainstormbased waterlogging of HSRPC under fatigue loading.The mechanical properties of HSRPC in terms of flexural strength and dynamic elastic modulus were studied.The waterlogging resistance of HSRPC was described by surface water depth and drainage time.The microstructure of HSRPC were observed with scanning electron microscopy(SEM).Results showed that although the dynamic elastic modulus and flexural strength of HSRPC decreased with the increasing number of fatigue loading,the flexural strength of HSRPC was still greater than5 MPa after design service life of 20 years.After 2.5×10^(5)times of fatigue loading,the permeability coefficient of HSRPC with a porosity of 0.502%and 1.13%increased by 18.4%and 22.9%,respectively;while the permeability coefficient of HSRPC with 0.126%porosity dropped to 0.35 mm/s.The maximum surface water depth of HSRPC with a porosity of 0.126%,0.502%,and 1.13%were 8,5 and 4 mm,respectively.SEM results showed that fatigue loading expanded the number and width of cracks around the tiny pores in HSRPC.

The Transport Properties of Concrete under the Simultaneous Coupling of Fatigue Load and Environment Factors

A set of coupling experimental instrument was designed to study the transport properties of chloride ion in concrete under simultaneous coupling action of fatigue load and environmental factors. Firstly the water-saturated performance of modem concrete was investigated, then diffusion performance of chloride ion under different stress levels and different temperature were studied respectively; meanwhile, the time- dependent behavior of the chloride ion diffusion in concrete was also researched. The results showed that the saturation degree of concrete can reach as high as 99%. Besides, diffusion coefficient of chloride ion increased with increasing of the stress level and temperature, and when the stress level and temperature are at 0.6 and 60 ℃ respectively, the diffusion coefficient is 6.3 ×10 -14 m2/s, moreover the diffusion coefficient of chloride ion in concrete decreased with time under the simultaneous coupling action of fatigue load and environment factors.

Effect of fatigue loading-confining stress unloading rate on marble mechanical behaviors: An insight into fracture evolution analyses

Rocks in underground works usually experience rather complex stress disturbance.For this,their fracture mechanism is significantly different from rocks subjected to conventional triaxial compression conditions.The effects of stress disturbances on rock geomechanical behaviors under fatigue loading conditions and triaxial unloading conditions have been reported in previous studies.However,little is known about the dependence of the unloading rate on fatigue loading and confining stress unloading(FL-CSU)conditions that influence rock failure.In this paper,we aimed at investigating the fracture behaviors of marble under FL-CSU conditions using the post-test X-ray computed tomography(CT)scanning technique and the GCTS RTR 2000 rock mechanics system.Results show that damage accumulation at the fatigue stage can influence the final fracture behaviors of marble.The stored elastic energy for rock samples under FL-CSU tests is relatively larger compared to those under conventional triaxial tests,and the dissipated energy used to drive damage evolution and crack propagation is larger for FL-CSU tests.In FL-CSU tests,as the unloading rate increases,the dissipated energy grows and elastic energy reduces.CT scanning after the test reveals the impacts of the unloading rate on the crack pattern and a fracture degree index is therein defined in this context to represent the crack dimension.It shows that the crack pattern after FL-CSU tests depends on the unloading rate,and the fracture degree is in agreement with the analysis of both the energy dissipation and the amount of energy released.The effect of unloading rate on fracture evolution characteristics of marble is revealed by a series of FL-CSU tests.

Residual Tensile Strength of Plain Concrete Under Tensile Fatigue Loading

The functional relation between the residual tensile strength of plain concrete and number of cycles was determined. 99 tappered prism specimens of plain concrete were tested under uniaxial tensile fatigue loading. Based on the probability distribution of the residual tensile strength, the empirical expressions of the residual tensile strength corresponding to the number of cycles were obtained. The residual tensile strength attenuating curves can be used to predict the residual fatigue life of the specimen under variable-amplitude fatigue loading. There is a good correlation between residual tensile strength and residual secant elastic modulus. The relationship between the residual secant elastic modulus and number of cycles was also established.

Chloride Ion Transport in Fly Ash Mortar under Action of Fatigue Loading

In order to study the chloride ion transport performance in fly ash addition mortar, a new method, in which the fatigue loading and chloride diffusion are undertaken simultaneously, was developed. This method realizes coupling the fatigue damage process and the process of chloride transporting of fly ash mortar. The transport performance of chloride in fly ash mortar specimens was studied under different stress levels. Moreover, the effect of fly ash content on transport performance of chloride ion in mortar was investigated. AE （Acoustic Emission） and SEM were used to acquire the damage distribution of mortar specimens under action of fatigue load. The results show that the diffusion coefficient of chloride in mortar specimens increases with stress level of fatigue loading. The addition of fly ash can mitigate the penetration of chloride ion. The results of microcmck 3D location acquired by AE, accompanied with crack characterizing from SEM, indicate that the damage degree of mortar specimen increases with stress level of fatigue loading. Furthermore, higher damage degree of mortar leads to more the chloride ion content in the sample.

TREATMENT OF COMPLEX LOAD HISTORY AND CONSTRUCTION OF FATIGUE LOAD SPECTRUM

A new, more actual approach for omitting small loads in a loading history was pres-ented according to crack closure, and load interactive effects which are large on damage of com-ponents were studied. Intrinsic periodic spectrum block representing a damage element of a loadhistory, a new concept, was put out. It has been proven by theoretic analysis and tests that themodes of constructing fatigue loading spectrum have little effect on damage of components,which will change the incomplete knowledges on constructing fatigue spectrum ago.

Fatigue Properties of Plain Concrete Under Triaxial Compressive Cyclic Loading

Experiments were made on plain concrete subjected to triaxial static loading and constant amplitude compressive fatigue loading with a constant lateral pressure in two directions. The initial confining pressure was 0, 0.1 f c , 0.25 f c and 0.4 f c , respectively, for the static test, and 0.1 f c and 0.25 f c for the fatigue test. Based on the triaxial compressive constitutive behavior of concrete, the inflexion of confining pressure evolution was chosen to be the fatigue damage criterion during the test. The rule of evolution of longitudinal maximum and minimum strains, longitudinal cyclic modulus and damage were recorded and analyzed. According to the Fardis Chen criterion model and the concept of equivalent fatigue life and equivalent stress level, a unified S N curve for multi axial compressive fatigue loading was proposed. Thus, the fatigue strength factors for different fatigue loading cases can be obtained. The present investigation provides information for the fatigue design of concrete structures.

Research on the Follow-Up Control Strategy of Biaxial Fatigue Test of Wind Turbine Blade Based on Electromagnetic Excitation

Aiming at the drift problem that the tracking control of the actual load relative to the target load during the electromagnetic excitation biaxial fatigue test of wind turbine blades is easy to drift,a biaxial fatigue testingmachine for electromagnetic excitation is designed,and the following strategy of the actual load and the target load is studied.A Fast Transversal Recursive Least Squares algorithm based on fuzzy logic(Fuzzy FTRLS)is proposed to develop a fatigue loading following dynamic strategy,which adjusts the forgetting factor in the algorithmthrough fuzzy logic to overcome the contradiction between convergence accuracy and convergence speed and solve the phenomenon of amplitude overshoot and phase lag of the actual load relative to the target load.Combined with the previous research results,a simulation model was constructed to verify the strategy’s effectiveness.Field tests were carried out to verify its follow-up effect.The results showthat the tracking error of flapwise and edgewise direction iswithin 4%,which has better robustness and dynamic and static performance than the traditional Recursive Least Squares(RLS)algorithm.

Fatigue Life Prediction under Service Load Considering Strengthening Effect of Loads below Fatigue Limit

Lightweight design requires an accurate life prediction for structures and components under service loading histories. However, predicted life with the existing methods seems too conservative in some cases, leading to a heavy structure. Because these methods are established on the basis that load cycles would only cause fatigue damage, ignore the strengthening effect of loads. Based on Palmgren-Miner Rule （PMR）, this paper introduces a new method for fatigue life prediction under service loadings by taking into account the strengthening effect of loads below the fatigue limit. In this method, the service loadings are classified into three categories： damaging load, strengthening load and none-effect load, and the process for fatigue life prediction is divided into two stages： stage I and stage II, according to the best strengthening number of cycles. During stage I, fatigue damage is calculated considering both the strengthening and damaging effect of load cycles. While during stage II, only the damaging effect is considered. To validate this method, fatigue lives of automobile half shaft and torsion beam rear axle are calculated based on the new method and traditional methods, such as PMR and Modified Miner Rule （MMR）, and fatigue tests of the two components are conducted under service loading histories. The tests results show that the percentage errors of the predicted life with the new method to mean life of tests for the two components are –3.78% and –1.76% separately, much lesser than that with PMR and MMR. By considering the strengthening effect of loads below the fatigue limit, the new method can significantly improve the accuracy for fatigue life prediction. Thus lightweight design can be fully realized in the design stage.

ESTIMATION OF FATIGUE LIFE UNDER RANDOM LOADING WITH PLASTIC HYSTERESIS ENERGY THEOREM

Fatigue damage of materials includes static damage and cyclic damage.Static damage is a ratio of the plastic energy in first static loading to the statictoughness, while cyclic damage is the ratio of the cyclic plastic hysteresis energy to thefatigue toughness. In the calculation, cyclic hardening (or softening) of a material istaken into account, which results in the increase (or decrease) of the yield stress. Forsimplification, it is assumed that stress and strain in cyclic loading vary in accordancewith the hysteresis loop. Fatigue toughness of a material can be detennined bysymmetric cyclic stress controlled fatigue test. A method, rational and convenient forengineering, is proposed to estimate the fatigue life under random loading based onplastic hysteresis energy theorem. Preliminary verification by test is satisfactory.

FATIGUE RELIABILITY DESIGN AND ESTIMATION METHOD FOR VARIABLE LOADING

A method is presented for estimating fatigue reliability under variable loading, which isbased on load cycles-fatigue life interference theory as well as cumulative fatigue damageanalysis. The basic opinion is that for variable loading the increment of failure probability pro-duced by each load cycle is determined by the stress level as well as the damage state at whichthis load cycle applies Contrast to 'conditional reliability-equivalent life methodology'. this meth-od calculates the equivalent cycle numbers between different stress levels according to cumulativefatigue damage rule but not equivalent failure probability.

Research on the Fatigue Flexural Performance of RC Beams Attacked by Salt Spray

The fatigue flexural performance of RC beams attacked by salt spray was studied. A testing method involving electro osmosis, electrical accelerated corrosion and salt spray was proposed. This corrosion process method effectively simulates real-world salt spray and fatigue loading exerted by RC components on sea bridges. Four RC beams that have different stress amplitudes were tested. It is found that deterioration by corrosion and fatigue loading reduces the fatigue life of the RC and decreases the ability of deformation. The fatigue life and deflection ability could be reduced by increasing the stress amplitude and the corrosion duration time. The test result demonstrates that this experimental method can couple corrosion deterioration and fatigue loading reasonably. This procedure may be applied to evaluate the fatigue life and concrete durability of RC components located in a natural salt spray environment.

Influence of cyclic loading on the fracture toughness and load bearing capacities of all-ceramic crowns

The purpose of this study was to investigate how cyclic loading influenced the fracture toughness of hot-press lithium disilicate and zirconia core materials and whether there was an increase in the propensity for crown failure. Two types of all-ceramic crowns including the IPS e.max Press system （n=24） and the Lava zirconia system （n=24）, were selected. Sectioned specimens were subjected to cyclic loading with the maximum magnitude of 200 N （R=0.1） until two million cycles. The material properties including Young＇s modulus （E） and hardness （H） and the fracture toughness （K,c） of the core materials were evaluated using indentation methods （n= 12 each）. The load-bearing capacities of the specimens were examined by means of monotonic load to fracture （n=12 each）. It was found that the material properties, including E, Hand Knc, of the two types of dental ceramics, were reduced. Statistical analysis indicated that there were no significant influences of fatigue loading on material properties E and H for both types of dental ceramics or Kgc for zirconia, while for the IPS e.max Press core, K,c, which was parallel to the direction of the lithium disilicate crystals, was significantly reduced （P-0.001）. A conclusion was drawn that zirconia possesses high mechanical reliability and sustainable capacity to resist fatigue loading, while fatigue loading remarkably degraded the anisotropic mechanical behaviour of hot-press lithium disilicate ceramics.

Experimental Study on the Degradation of Bonding Behavior between Reinforcing Bars and Concrete after Corrosion and Fatigue Damage

In marine environments,the durability of reinforced concrete structures such as bridges,which suffer from the coupled effects of corrosion and fatigue damage,is significantly reduced.Fatigue loading can result in severe dete-rioration of the bonds between reinforcing steel bars and the surrounding concrete,particularly when reinforcing bars are corroded.Uniaxial tension testing was conducted under static loading and fatigue loading conditions to investigate the bonding characteristics between corroded reinforcing bars and concrete.An electrolyte corrosion technique was used to accelerate steel corrosion.The results show that the bond strength was reduced under fati-gue loading,although the concrete did not crack.Therefore,fatigue loading has negative effects on the bond strength between corroded steel bars and concrete.The effects of corrosion cracking on bond strength become more pronounced after corrosion cracking appears along the main reinforcing bars.When the average width of cracking along main reinforcing bars exceeds 3 mm,the bonding properties deteriorate rapidly based on the effects of corrosion cracking,whereas fatigue loading exhibits no additional effects on bond strength.

Stochastic Analysis of Short-Term Structural Responses and Fatigue Damages of A Submerged Tension Leg Platform Wind Turbine in Wind and Waves

In connection with the design of floating wind turbines,stochastic dynamic analysis is a critical task considering nonlinear wind and wave forces.To study the random structural responses of a newly designed submerged tension leg platform(STLP)wind turbine,a set of dynamic simulations and comparison analysis with the MIT/NREL TLP wind turbine are carried out.The signal filter method is used to evaluate the mean and standard deviations of the structural response.Furthermore,the extreme responses are estimated by using the mean upcrossing rate method.The fatigue damages for blade root,tower,and mooring line are also studied according to the simulated time-series.The results and comparison analysis show that the STLP gives small surge and pitch motions and mooring line tensions in operational sea states due to the small water-plane area.Additionally,in severe sea states,the STLP gives lower extreme values of platform pitch,slightly larger surge and heave motions and better towerbase and mooring line fatigue performances than those of the MIT/NREL TLP.It is found that the STLP wind turbine has good performances in structural responses and could be a potential type for exploiting the wind resources located in deep waters.

船舶与海洋工程结构疲劳分析的最新进展

A review is provided of various approaches that have been adopted recently to assess the fatigue of ships and offshore structures.The relevant fatigue loading is reviewed first,focusing on the successive loading and unloading of the cargo and the transient loadings.The factors influencing fatigue strength are discussed,including the geometrical parameters,material,residual stress,and ones related to the environment.Different approaches for fatigue analyses of seam-welded joints are covered,i.e.,the structural stress or strain approach,the notch stress or strain approach,notch intensity approach,and the crack propagation approach.

Experimental Study of Post-heated Steel Reinforced Recycled Concrete Columns Repaired with CFRP

The mechanical and thermal properties of steel reinforced concrete columns with CFRP reinforcement were examined after exposure to a high temperature of 500℃. The concrete made with normal and recycled coarse aggregate（RCA） was fabricated and three different RCA replacement ratios（0, 50%, and 100%） were investigated. The fatigue properties of steel reinforced concrete with RCA and CFRP reinforcement were tested for two million cycles at a frequency of 2.5 Hz. The test results show that the failure of strengthened specimens is mainly caused by rupture of CFRP jacket and buckling of inner section steel reinforcement. However, for the unstrengthened specimen, both of inner steel buckling and core concrete cracking are the main contributors to the damage. The load-bearing capacity, deformation and energy dissipation of the specimens during the fatigue test could be strengthened greatly by CFRP reinforcement. However, the CFRP reinforcement has little influence on the improvement of the stiffness of the specimens, which may be caused by a plastic damage accumulation during the early cycles of fatigue tests. Finally, a static test was conducted on the postfatigue specimens, the results showed that a large decrease in stiffness was observed for the specimens subjected to high temperature and fatigue, and the fatigue loading had a higher influence on the specimens than the high temperature.

DAMAGE TOLERANCE ANALYSIS ON HOLLOW AXLES OF HIGH SPEED MOTOR TRAINS

According to the rules of UIC515-3, the service loads of the axles are defined, which include some different loads cases as follows： the static loads; the impact loads resulted from running through the rail joints and unevenness rails; the loads through curves and from braking. Through the calculating and analysis, the stress distribution of the hollow axles is obtained for 200 km/h high speed motor trains used in China. At the same time, the fatigue crack growth of hollow axles is studied, and the initial surface cracks of 2 mm depth caused by hard objects strike or the other causes are discussed. On the basis of the linear elastic fracture mechanics theory, the stress intensity factor of the crack of the geometry transition outside the wheel seat is also studied. Associated with fatigue crack propagation equation and the corresponding crack propagation threshold, the crack propagation characteristics under different shapes are calculated. Then the running distances are educed with different shapes propagating to the critical length, and the estimation of the residual lives about hollow axles which are the reference values of examine and repair limit of the hollow axle is given.

Fatigue Induced Alteration of the Superficial Strength Properties of 2024 Aluminum Alloy

aluminum alloy 2024 T3 specimens have been subjected to constant amplitude fatigue loading at R=0.1. During fatigue, an appreciable increase of the surface hardness of the material at the meso-scale can be observed and captured by means of nanoindentations. Surface hardness increases with increasing fatigue stress amplitude and advancing number of applied fatigue cycles. Observed increase of specimen surface hardening degree during fatigue causes an evolution of superficial mechanical strength properties of the alloy. Stress-strain curves associated with the evoluting superficial mechanical properties are derived, employing a developed finite element method （FEM）-supported evaluation procedure of nanoindentation experimental results.

Application of semi-analytical finite element method to analyze asphalt pavement response under heavy traffic loads

Accurate assessment of the impact of heavy traffic loads on asphalt pavements requires a computational model which is able to calculate the response of the pavement fast and precisely. Currently the most finite element analysis programs based on traditional methods have various limitations. A specific program SAFEM was developed based on a semi-analytical finite element method to overcome the problems. It is a three-dimensional FE program that requires only a two-dimensional mesh by incorporating the semi- analytical method using Fourier series in the third dimension. The computational accuracy and efficiency of the program was verified by analytical verification previously. The experimental verification is carried out in this paper and the results show that the SAFEM is able to predict the mechanical responses of the asphalt pavement. Using the program SAFEM, the impact of heavy traffic loads was analyzed in terms of stress and strain dis- tribution, surface deflection and fatigue life. The results indicate that if the asphalt pave- ment is subjected to the heavy traffic load more, the thicknesses and stiffness of the pavement structural layers should be increased adequately in order to support the surface deflection, The compressive stress in asphalt binder course is relatively large and increases more significantly compared with that in the other asphalt layers when the axle load becomes larger. With comparison of the predicted fatigue life, the increase of the axle load will lead to the destruction of the asphalt pavement extremely easily.