Excellent weldability substantially contributes to the intrinsic quality of steels,while appropriate chemical composition plays a primary role in the essential weldability of steels.The poor weldability of ferritic st...Excellent weldability substantially contributes to the intrinsic quality of steels,while appropriate chemical composition plays a primary role in the essential weldability of steels.The poor weldability of ferritic stainless steels could be improved through modification with minor alloy elements while minimally increasing the cost.Therefore,studying the effect of minor alloy elements on the weldability of steels is of considerable importance.In this study,several steels of middle-chromium hyperpure ferritic stainless 00Cr21Ti with different Ni content(0.3%,0.5%,0.8%,and 1.0%)were developed,and their weldabilities of butt joint samples welded using the metal inert gas welding process,including the influence of welded joints on the microstructure,tensile performance,corrosion resistance,and fatigue property,were investigated.Results show that the steels with w(Ni)≥0.8%exhibit excellent mechanical properties compared with those with low-Ni content steels,further,their impact toughness at normal atmospheric temperature meets the industrial application standard and the fatigue property is similar to that of 304 austenitic stainless steel.Moreover,results show that the corrosion resistance of all the samples is almost at the same level.The results acquired in this study are supposed to be useful for the optimization of the chemical composition of stainless steels aiming to improve weldability.展开更多
With the increase in the content of carbon, nitrogen and titanium in 430 ferritic stainless steel, the refinement of the solidification structure is obvious and the proportion of equiaxed grain increases remarkably as...With the increase in the content of carbon, nitrogen and titanium in 430 ferritic stainless steel, the refinement of the solidification structure is obvious and the proportion of equiaxed grain increases remarkably as well. This is attributed to the increasing role of the inhomogeneous nucleation by TiN particles during solidification. In addition, more fine precipitations of （Ti ,Nb）N are found in steel with increased carbon and nitrogen content.展开更多
The thermodynamics of TiN precipitation in liquid steel of 430 ferrite stainless steel has been calculated to find out the condition of TiN precipitation during the initial solidification stage. The difference in the ...The thermodynamics of TiN precipitation in liquid steel of 430 ferrite stainless steel has been calculated to find out the condition of TiN precipitation during the initial solidification stage. The difference in the solidification structure of 430 ferrite stainless steel has been discussed through comparative tests of vacuum induction furnace melting with different contents of Ti. It has been found that the equiaxed grain proportion can be increased from 20% to 69% as the content of Ti from 0.1% up to 0. 4%. The size of the TiN particles precipitated is 1-3 μm and the number of TiN particles is about （200- 300）/μm^2. It is found that the effect of using TiN to refine the solidification structure has been confirmed under the strict process condition used for 430 ferrite stainless steel.展开更多
With Nb-Ti-stabilized 430 ferritic stainless steel（NTS430FSS） and SUS 430 ferritic stainless steel（SUS430FSS） as experimental materials, the influence of precipitation on intergranular corrosion resistance was inv...With Nb-Ti-stabilized 430 ferritic stainless steel（NTS430FSS） and SUS 430 ferritic stainless steel（SUS430FSS） as experimental materials, the influence of precipitation on intergranular corrosion resistance was investigated. A series of aging treatment were carried out. The free-exposure corrosion test and double loop electrochemical potentiokinetic reactivation（DL-EPR） test with a scan rate of 1.67 m V/s at 26 °C were applied to evaluate the intergranular corrosion（IGC） resistance. Metallographic observation, scanning electron microscope（SEM）, transmission electron microscope（TEM） with energy dispersive spectroscopy（EDS） and X-ray diffraction（XRD） analysis were conducted. The results show that IGC occurred in SUS430 FSS aged above 700 °C, while it occurred in NTS430 FSS as the temperature was improved to 1 050 °C. The critical degree of sensitization Ir/Ia reaches 0.305 in SUS430 FSS, which is higher than that of NTS430 FSS, i.e. 0.010, aged at 950 °C for 2 h. The TEM, EDS and XRD results show that a large amount of Cr23C6 precipitates with size of 60 nm×22 nm are located at the SUS430 FSS grain boundaries as chains. With the addition of Nb and Ti and reduction of C, the amount of precipitates reduces significantly in NTS430 FSS. A majority of Cr23C6 were replaced by Ti C and Nb C. Only a small amount of spherical Ti C（R=186 nm） and square Ti N（312 nm×192 nm） with Nb and Cr adsorbed are left along grain boundaries. Due to the dual stabilization of Nb and Ti, the precipitation of Cr23C6 is restrained, the chromium depleted region is avoided and accordingly the resistance to the intergranular corrosion is improved.展开更多
文摘Excellent weldability substantially contributes to the intrinsic quality of steels,while appropriate chemical composition plays a primary role in the essential weldability of steels.The poor weldability of ferritic stainless steels could be improved through modification with minor alloy elements while minimally increasing the cost.Therefore,studying the effect of minor alloy elements on the weldability of steels is of considerable importance.In this study,several steels of middle-chromium hyperpure ferritic stainless 00Cr21Ti with different Ni content(0.3%,0.5%,0.8%,and 1.0%)were developed,and their weldabilities of butt joint samples welded using the metal inert gas welding process,including the influence of welded joints on the microstructure,tensile performance,corrosion resistance,and fatigue property,were investigated.Results show that the steels with w(Ni)≥0.8%exhibit excellent mechanical properties compared with those with low-Ni content steels,further,their impact toughness at normal atmospheric temperature meets the industrial application standard and the fatigue property is similar to that of 304 austenitic stainless steel.Moreover,results show that the corrosion resistance of all the samples is almost at the same level.The results acquired in this study are supposed to be useful for the optimization of the chemical composition of stainless steels aiming to improve weldability.
基金this project by both the National Natural Science Foundation of China(NSF 50734002)and Baosteel is fully acknowledged.
文摘With the increase in the content of carbon, nitrogen and titanium in 430 ferritic stainless steel, the refinement of the solidification structure is obvious and the proportion of equiaxed grain increases remarkably as well. This is attributed to the increasing role of the inhomogeneous nucleation by TiN particles during solidification. In addition, more fine precipitations of （Ti ,Nb）N are found in steel with increased carbon and nitrogen content.
基金The National Basic Research Program of China (2004CB619107)
文摘The thermodynamics of TiN precipitation in liquid steel of 430 ferrite stainless steel has been calculated to find out the condition of TiN precipitation during the initial solidification stage. The difference in the solidification structure of 430 ferrite stainless steel has been discussed through comparative tests of vacuum induction furnace melting with different contents of Ti. It has been found that the equiaxed grain proportion can be increased from 20% to 69% as the content of Ti from 0.1% up to 0. 4%. The size of the TiN particles precipitated is 1-3 μm and the number of TiN particles is about （200- 300）/μm^2. It is found that the effect of using TiN to refine the solidification structure has been confirmed under the strict process condition used for 430 ferrite stainless steel.
文摘With Nb-Ti-stabilized 430 ferritic stainless steel（NTS430FSS） and SUS 430 ferritic stainless steel（SUS430FSS） as experimental materials, the influence of precipitation on intergranular corrosion resistance was investigated. A series of aging treatment were carried out. The free-exposure corrosion test and double loop electrochemical potentiokinetic reactivation（DL-EPR） test with a scan rate of 1.67 m V/s at 26 °C were applied to evaluate the intergranular corrosion（IGC） resistance. Metallographic observation, scanning electron microscope（SEM）, transmission electron microscope（TEM） with energy dispersive spectroscopy（EDS） and X-ray diffraction（XRD） analysis were conducted. The results show that IGC occurred in SUS430 FSS aged above 700 °C, while it occurred in NTS430 FSS as the temperature was improved to 1 050 °C. The critical degree of sensitization Ir/Ia reaches 0.305 in SUS430 FSS, which is higher than that of NTS430 FSS, i.e. 0.010, aged at 950 °C for 2 h. The TEM, EDS and XRD results show that a large amount of Cr23C6 precipitates with size of 60 nm×22 nm are located at the SUS430 FSS grain boundaries as chains. With the addition of Nb and Ti and reduction of C, the amount of precipitates reduces significantly in NTS430 FSS. A majority of Cr23C6 were replaced by Ti C and Nb C. Only a small amount of spherical Ti C（R=186 nm） and square Ti N（312 nm×192 nm） with Nb and Cr adsorbed are left along grain boundaries. Due to the dual stabilization of Nb and Ti, the precipitation of Cr23C6 is restrained, the chromium depleted region is avoided and accordingly the resistance to the intergranular corrosion is improved.