The effect of friction pressure p and oxygen concentration xo on the fireproof performance of Ti40 titanium alloy was studied by frictional ignition test, the U--Xo relationship quantitatively describing the fireproof...The effect of friction pressure p and oxygen concentration xo on the fireproof performance of Ti40 titanium alloy was studied by frictional ignition test, the U--Xo relationship quantitatively describing the fireproof performance of Ti40 was established and the fireproof mechanism of Ti40 was analyzed by SEM, XRD and EDS. The results show that the p--xo relationship of Ti40 obeys parabolic rule. The varying range of xo is about 25% while p varies within 0.1-0.25 MPa. When Xo is 〉70%, Ti40 is ignited immediately at room temperature and develops into continual and steady burning, and the duration of burning is more than 10 s. The fireproof performance of Ti40 is better than TC4 while xo of Ti40 is at least 40% higher than TC4. When Xo is low, the fireproof performance of Ti40 is more sensitive to p; when Xo increases, it is more sensitive to Xo. The forming of fused oxides of V205, TiO2 and Cr203 with strong inner interaction during friction is the basic reason of high fireproof performance of Ti40.展开更多
The effects and heat transfer mode of water film and sprinkler system on the heat-resistant property associated with the insulation of a fireproof glass were investigated. In the experiments, fireproof glass with a si...The effects and heat transfer mode of water film and sprinkler system on the heat-resistant property associated with the insulation of a fireproof glass were investigated. In the experiments, fireproof glass with a size of 3 300 mm （height）×2 200 mm （width） ×12 mm （thickness） was exposed to an oil pool fire with a power of approximately 1.4 MW. The experimental results show that the application of the water film or sprinkler system on the glass can effectively resist the intensive heat from the fire in the test due to the absorption of latent heat. The permitted period of integrity and insulation with a water film and a sprinkler system could be extended to 60 min. It should be noted that the temperature of the glass surface Can be kept under 60℃in a 60 min test. The experimental results suggest that it is feasible to substitute fireproof glass with water film for a fireproof door as long as the water film or sprinkler system can work stably and water can cover the whole surface of the frreproof glass.展开更多
基金Project(20123021004) supported by the Key Program of the Aeronautical Science Foundation of ChinaProject(51312030501) supported by the Pre-Research Program of China
文摘The effect of friction pressure p and oxygen concentration xo on the fireproof performance of Ti40 titanium alloy was studied by frictional ignition test, the U--Xo relationship quantitatively describing the fireproof performance of Ti40 was established and the fireproof mechanism of Ti40 was analyzed by SEM, XRD and EDS. The results show that the p--xo relationship of Ti40 obeys parabolic rule. The varying range of xo is about 25% while p varies within 0.1-0.25 MPa. When Xo is 〉70%, Ti40 is ignited immediately at room temperature and develops into continual and steady burning, and the duration of burning is more than 10 s. The fireproof performance of Ti40 is better than TC4 while xo of Ti40 is at least 40% higher than TC4. When Xo is low, the fireproof performance of Ti40 is more sensitive to p; when Xo increases, it is more sensitive to Xo. The forming of fused oxides of V205, TiO2 and Cr203 with strong inner interaction during friction is the basic reason of high fireproof performance of Ti40.
基金Project(2006BAK06B02) supported by the National Science and Technology Pillar Program during the Eleven Five-Year Plans of ChinaProject(70701019) supported by the National Natural Science Foundation of China
文摘The effects and heat transfer mode of water film and sprinkler system on the heat-resistant property associated with the insulation of a fireproof glass were investigated. In the experiments, fireproof glass with a size of 3 300 mm （height）×2 200 mm （width） ×12 mm （thickness） was exposed to an oil pool fire with a power of approximately 1.4 MW. The experimental results show that the application of the water film or sprinkler system on the glass can effectively resist the intensive heat from the fire in the test due to the absorption of latent heat. The permitted period of integrity and insulation with a water film and a sprinkler system could be extended to 60 min. It should be noted that the temperature of the glass surface Can be kept under 60℃in a 60 min test. The experimental results suggest that it is feasible to substitute fireproof glass with water film for a fireproof door as long as the water film or sprinkler system can work stably and water can cover the whole surface of the frreproof glass.